Title:Soft x-ray absorption and scattering from $\rm Na_x Ca_{2-x} CuO_2 Cl_2$ at x=0.08

Abstract: X-ray absorption (XAS) and resonant soft x-ray scattering (RSXS) measurements were carried out on single crystals of doped $\rm Na_{0.08}Ca_{1.92}CuO_2Cl_2$ (NCCOC) at the $\rm Cu L_{3/2}$ and $\rm O~K$ edges. These experiments allow the direct measurement of both the $k=0$ and $k\neq0$ unoccupied density of states of the $\rm CuO_{2}$ planes. A mobile carrier peak (MCP) and reduced weight in the upper Hubbard band (UHB) compared to $\rm Sr_2CuO_2Cl_2$ (SCCO) are observed at this doping, indicating that spectral weight transfer occurs in this system in a manner similar to other doped cuprates. The absence of apical oxygens is seen as a reduced O $p_x$ density of states just above the UHB, which is likely related to the enhanced two-dimensionality of this system. No evidence was seen for a $4a \times 4a$ density of states (DOS) modulation as reported previously [T. Hanaguri \emph{et al.}, Nature \textbf{430}, 1001 (2004)] indicating that this effect is not directly related to DOS modulations in, for example, $\rm La_{2-x}Ba_xCuO_4$ [P. Abbamonte \emph{et al.}, Nature Physics \textbf{1}, 155 (2005)]. This might be explained in terms of glassy electronic behavior or the existence of a surface-nucleated phase transition in NCCOC [S. E. Brown \emph{et al.}, Phys. Rev. B \textbf{71}, 224512 (2005)].