Condensed Matter > Materials Science

arXiv:2209.09460 (cond-mat)
[Submitted on 20 Sep 2022 (v1), last revised 30 Jan 2023 (this version, v2)]

Title:Effect of Substrate Surface on the Wide Bandgap SnO2 Thin Films Grown by Spin Coating

Authors:Md. Nur Amin Bitu, Nazmul Islam Tanvir, Suravi Islam, Syed Farid Uddin Farhad
View PDF
Abstract:Tin (IV) oxide (SnO2) sols have been synthesized from SnCl2.2H2O precursor solution by applying two different processing conditions. The prepared sols were then deposited on UV-Ozone treated quartz and soda lime glass (SLG) substrates by spin coating. The as-synthesized film was soft-baked at about 100 deg. C. for 10 min. This process was repeated five times to get a compact film, followed by air-annealing at 250 deg. C. for 2 hours. The pristine and annealed films were characterized by UV-Vis-NIR spectroscopy, Grazing Incident X-Ray Diffraction (GIXRD), and Field Emission Scanning Electron Microscope (FESEM). The effect of the substrate surface was investigated by measuring the contact angles with De-Ionized (DI) water. UV-Ozone treatment of substrate provides a cleaner surface to grow a homogeneous film. The electrical resistivity of annealed thin films was carried out by a four-point-collinear probe employing the current reversal technique and found in the range of approx. 2x10^3 to 3x10^3 Ohm-cm. Film thickness was found in the range of approx. 137-285 nm, measured by a stylus profilometer. UV-VIs-NIR Transmission data revealed that all the thin film samples showed maximum (82-89) % transmission in the visible range. The optical bandgap of the thin films was estimated to be approx. 3.75-4.00 eV and approx. 3.78-4.35 eV for the films grown on SLG and quartz substrates, respectively.
Comments: 7 pages, 4 figures
Subjects: Materials Science (cond-mat.mtrl-sci); Applied Physics (physics.app-ph); Chemical Physics (physics.chem-ph)
Cite as: arXiv:2209.09460 [cond-mat.mtrl-sci]
  (or arXiv:2209.09460v2 [cond-mat.mtrl-sci] for this version)
  https://doi.org/10.48550/arXiv.2209.09460

Submission history

From: Md. Nur Amin Bitu [view email]
[v1] Tue, 20 Sep 2022 04:32:06 UTC (1,091 KB)
[v2] Mon, 30 Jan 2023 04:56:12 UTC (2,147 KB)
Full-text links:

Access Paper:

  • View PDF
  • Other Formats
license icon view license
Current browse context:
cond-mat.mtrl-sci
< prev   |   next >
new | recent | 2022-09
Change to browse by:
cond-mat
physics
physics.app-ph
physics.chem-ph

References & Citations

export BibTeX citation

Bookmark

BibSonomy logo Reddit logo

Bibliographic and Citation Tools

Bibliographic Explorer (What is the Explorer?)
Connected Papers (What is Connected Papers?)
Litmaps (What is Litmaps?)
scite Smart Citations (What are Smart Citations?)

Code, Data and Media Associated with this Article

alphaXiv (What is alphaXiv?)
CatalyzeX Code Finder for Papers (What is CatalyzeX?)
DagsHub (What is DagsHub?)
Gotit.pub (What is GotitPub?)
Hugging Face (What is Huggingface?)
Papers with Code (What is Papers with Code?)
ScienceCast (What is ScienceCast?)

Demos

Replicate (What is Replicate?)
Hugging Face Spaces (What is Spaces?)
TXYZ.AI (What is TXYZ.AI?)

Recommenders and Search Tools

Influence Flower (What are Influence Flowers?)
CORE Recommender (What is CORE?)
IArxiv Recommender (What is IArxiv?)

arXivLabs: experimental projects with community collaborators

arXivLabs is a framework that allows collaborators to develop and share new arXiv features directly on our website.

Both individuals and organizations that work with arXivLabs have embraced and accepted our values of openness, community, excellence, and user data privacy. arXiv is committed to these values and only works with partners that adhere to them.

Have an idea for a project that will add value for arXiv's community? Learn more about arXivLabs.

Which authors of this paper are endorsers? | Disable MathJax (What is MathJax?)