Title:Glass alteration in the process of long-term corrosion caused by internal stress: A comparative study of degraded and intact domains in 19th century semi-opaque turquoise glass seed beads using micro-FTIR spectroscopy and SEM

Abstract:In the paper, the long-term corrosion of 19th century beads made of turquoise lead-potassium glass is investigated using polarising light microscopy, FTIR spectroscopy and scanning electron microscopy including EDX spectroscopy and elemental mapping. Corrosion of turquoise seed-bead glass of the 19th century has been shown to comprise several mutually connected processes developing in parallel and intensifying one another. These processes are the directed migration of alkali-metal impurities, the glass depolymerization, and the nucleation of micro discontinuities followed by the formation of micro cracks and their gradual growth. In course of time, their cumulative and apparently synergistic effect results in glass fracturing terminated with bead crumbling into tiny discoloured sand-like particles. All these phenomena are controlled by the common driving force, namely, by the internal stress originated from the bead production process. Thus, the phenomenon of corrosion of beads made of stressed glass is the process of the internal stress relaxation in glass through the nucleation and growth of cracks, which lasts for decades at room temperature. It is dramatically accelerated when beads are heat treated at moderate temperature, however. The process takes place even if beads are kept in well-controlled museum environment.