Demonstration of a laser powder bed fusion combinatorial sample for high-throughput microstructure and indentation characterization
Authors:
Jordan S. Weaver,
Adam L. Pintar,
Carlos Beauchamp,
Howie Joress,
Kil-Won Moon,
Thien Q. Phan
Abstract:
High-throughput experiments that use combinatorial samples with rapid measurements can be used to provide process-structure-property information at reduced time, cost, and effort. Developing these tools and methods is essential in additive manufacturing where new process-structure-property information is required on a frequent basis as advances are made in feedstock materials, additive machines, a…
▽ More
High-throughput experiments that use combinatorial samples with rapid measurements can be used to provide process-structure-property information at reduced time, cost, and effort. Developing these tools and methods is essential in additive manufacturing where new process-structure-property information is required on a frequent basis as advances are made in feedstock materials, additive machines, and post-processing. Here we demonstrate the design and use of combinatorial samples produced on a commercial laser powder bed fusion system to study 60 distinct process conditions of nickel superalloy 625: five laser powers and four laser scan speeds in three different conditions. Combinatorial samples were characterized using optical and electron microscopy, x-ray diffraction, and indentation to estimate the porosity, grain size, crystallographic texture, secondary phase precipitation, and hardness. Indentation and porosity results were compared against a regular sample. The smaller-sized regions (3 mm x 4 mm) in the combinatorial sample have a lower hardness compared to a larger regular sample (20 mm x 20 mm) with similar porosity (< 0.03 %). Despite this difference, meaningful trends were identified with the combinatorial sample for grain size, crystallographic texture, and porosity versus laser power and scan speed as well as trends with hardness versus stress-relief condition.
△ Less
Submitted 3 August, 2021; v1 submitted 2 March, 2021;
originally announced March 2021.
Deuterium retention and thermal conductivity in ion-beam displacement-damaged tungsten
Authors:
George R. Tynan,
Russell P. Doerner,
J. Barton,
R. Chen,
S. Cui,
M. Simmonds,
Y. Wang,
J. S. Weaver,
N. Mara,
S. Pathak
Abstract:
Retention of plasma-implanted D is studied in W targets damaged by a Cu ion beam at up to 0.2 dpa with sample temperatures between 300 K and 1200 K. At a D plasma ion fluence of $10^{24}/m^2$ on samples damaged to 0.2 dpa at 300 K, the retained D retention inventory is $4.6x10^{20} D/m^2$, about ~5.5 times higher than in undamaged samples. The retained inventory drops to $9x10^{19} D/m^2$ for samp…
▽ More
Retention of plasma-implanted D is studied in W targets damaged by a Cu ion beam at up to 0.2 dpa with sample temperatures between 300 K and 1200 K. At a D plasma ion fluence of $10^{24}/m^2$ on samples damaged to 0.2 dpa at 300 K, the retained D retention inventory is $4.6x10^{20} D/m^2$, about ~5.5 times higher than in undamaged samples. The retained inventory drops to $9x10^{19} D/m^2$ for samples damaged to 0.2 dpa at 1000 K, consistent with onset of vacancy annealing at a rate sufficient to overcome the elevated rate of ion beam damage; at a damage temperature of 1200 K retention is nearly equal to values seen in undamaged materials. A nano-scale technique provides thermal conductivity measurements from the Cu- ion beam displacement damaged region. We find the thermal conductivity of W damaged to 0.2 dpa at room temperature drops from the un-irradiated value of 182 +/- 3.3 W/m-K to 53 +/- 8 W/m-K.
△ Less
Submitted 25 May, 2017;
originally announced May 2017.