Showing 1–2 of 2 results for author: Korupolu, S

Re-assembly and test of a COMB dipole magnet with STAR wires

Authors: V. V. Kashikhin, S. Cohan, J. DiMarco, O. Kiemschies, S. Krave, V. Lombardo, V. Marinozzi, D. Orris, S. Stoynev, D. Turrioni, A. K. Chavda, U. Sambangi, S. Korupolu, J. Peram, A. Arjun, C. Goel, J. Sai Sandra, V. Yerraguravagari, R. Schmidt, V. Selvamanickam, G. Majkic, E. Galstyan, N. Mai, K. Selvamanickam

Abstract: Rare-Earth Barium Copper Oxide (REBCO) coated conductors are an attractive option for application in high field accelerator magnets due to their high critical field and the convenience of fabrication without heat treatment compared to some other superconductors. A small REBCO accelerator magnet was previously fabricated and tested in liquid nitrogen, demonstrating over 90% critical current retenti… ▽ More Rare-Earth Barium Copper Oxide (REBCO) coated conductors are an attractive option for application in high field accelerator magnets due to their high critical field and the convenience of fabrication without heat treatment compared to some other superconductors. A small REBCO accelerator magnet was previously fabricated and tested in liquid nitrogen, demonstrating over 90% critical current retention in the coils. This paper describes the magnet re-assembly with a different support structure and its test in liquid helium at 1.8-4.5 K. The magnet quench history along with the instrumentation data is presented and discussed. △ Less

Submitted 5 December, 2024; originally announced December 2024.

Comments: 2024 Applied Superconductivity Conference; Journal submitted to IEEE Trans.Appl.Supercond

Report number: FERMILAB-CONF-24-0712-TD

Accelerator Magnet Development Based on COMB Technology with STAR Wires

Authors: V. V. Kashikhin, S. Cohan, V. Lombardo, D. Turrioni, N. Mai, A. K. Chavda, U. Sambangi, S. Korupolu, J. Peram, A. Anil, C. Goel, J. Sai Sandra, V. Yerraguravagari, R. Schmidt, V. Selvamanickam, G. Majkic, E. Galstyan, K. Selvamanickam

Abstract: This paper reports progress in the development of COMB magnet technology with STAR wires. A two-layer dipole magnet with 60 mm clear bore has been recently fabricated and tested in liquid nitrogen. The purpose of the test was to determine what kind of critical current degradation occurs in the process of winding the STAR wire into the COMB structure. This paper reports progress in the development of COMB magnet technology with STAR wires. A two-layer dipole magnet with 60 mm clear bore has been recently fabricated and tested in liquid nitrogen. The purpose of the test was to determine what kind of critical current degradation occurs in the process of winding the STAR wire into the COMB structure. △ Less

Submitted 7 August, 2023; v1 submitted 24 July, 2023; originally announced July 2023.

Comments: CEC/ICMC23

Report number: FERMILAB-CONF-23-361-TD