Versatile Hall magnetometer with variable sensitivity assembly for characterization of the magnetic properties of nanoparticles
Authors:
Jefferson F. D. F. Araujo,
Daniel R. P. Vieira,
Fredy Osorio,
Walmir E. Pöttker,
Felipe A. La Porta,
Patricia de la Presa,
Geronimo Perez,
Antonio C. Bruno
Abstract:
A Hall magnetometer with variable sensitivity is constructed to measure the magnetic properties of magnetic nanoparticles manufactured by different methods. This novel magnetometer can also be used to measure bulk materials and samples in liquids. The magnetometer is constructed with two commercial Hall-effect sensors in an acrylic structure, which serves as the support for a micrometer and the ci…
▽ More
A Hall magnetometer with variable sensitivity is constructed to measure the magnetic properties of magnetic nanoparticles manufactured by different methods. This novel magnetometer can also be used to measure bulk materials and samples in liquids. The magnetometer is constructed with two commercial Hall-effect sensors in an acrylic structure, which serves as the support for a micrometer and the circuit board with the sensors. For operation, the magnetometer it acquires a complete magnetization curve in a few minutes. If has a magnetic moment sensitivity of 1.3*10-9 Am2 to sensitivity of 493 mV/mT, the sensitivity can be adjustable in the range of 10 to 493 mV/mT. Its performance is tested with magnetic nanoparticles. As an application example, we estimate the mean diameter of the nanoparticles using the magnetic curves. The results are compared with those obtained by other techniques, such as transmission electron microscopy (TEM), X-ray diffraction (XRD) and dynamic light scattering (DLS). The magnetization results are also compared with those obtained by independent commercial magnetometers, which reveals errors of approximately 0.31 Am2/kg (i.e., 0.6%) in the saturation region.
△ Less
Submitted 17 June, 2019; v1 submitted 14 May, 2019;
originally announced May 2019.
-
Magnetic capsules for NMR imaging: Effect of magnetic nanoparticles spatial distribution and aggregation
Authors:
Azhar Zahoor Abbasi,
Lucía Gutiérrez,
Loretta L. del Mercato,
Fernando Herranz,
Oksana Chubykalo-Fesenko,
Sabino Veintemillas-Verdaguer,
Wolfgang J. Parak,
M Puerto Morales,
Jesús M González,
Antonio Hernandoe,
Patricia de la Presa
Abstract:
Magnetic and NMR relaxivity properties of γ-Fe2O3 nanoparticles embedded into the walls of polyelectrolyte multilayer capsules and freely dispersed in a sodium borate buffer solution have been investigated. The different geometric distribution of both configurations provides the opportunity to study the relationship of water accessibility and magnetic properties of particles on the NMR relaxivity.…
▽ More
Magnetic and NMR relaxivity properties of γ-Fe2O3 nanoparticles embedded into the walls of polyelectrolyte multilayer capsules and freely dispersed in a sodium borate buffer solution have been investigated. The different geometric distribution of both configurations provides the opportunity to study the relationship of water accessibility and magnetic properties of particles on the NMR relaxivity. Changes in their blocking temperature and average dipolar field were modeled as a function of packing fraction in the ensemble of free and entrapped nanoparticles. For free nanoparticles with relatively low concentration, relaxivity values increase with packing fraction according to an increase in the dipolar field and larger water accessibility. However for embedded NPs in the capsule wall, packing fractions should be limited to optimise the efficiency of this system as magnetic resonance imaging (MRI) contrast agent.
△ Less
Submitted 13 March, 2011;
originally announced March 2011.
-
Thermal evolution of Pt-rich FePt/Fe3O4 heterodimers studied using x-ray absorption near edge spectroscopy
Authors:
S. J. A. Figueroa,
S. J. Stewart,
T. Rueda,
A. Hernando,
P. de la Presa
Abstract:
FePt/Fe3O4 nanoparticles can be used as building blocks to obtain, upon thermal annealing, magnetic nanocomposites with combined magnetic properties. Although the pre- and post-annealed samples are usually well characterized, a detailed investigation during annealing is necessary to reveal the role of intermediate processes to produce a desirable composite. We present an alternative method using i…
▽ More
FePt/Fe3O4 nanoparticles can be used as building blocks to obtain, upon thermal annealing, magnetic nanocomposites with combined magnetic properties. Although the pre- and post-annealed samples are usually well characterized, a detailed investigation during annealing is necessary to reveal the role of intermediate processes to produce a desirable composite. We present an alternative method using in situ XANES to investigate the thermal evolution of oleic acid and oleylamine coated Pt-rich FePt/Fe3O4 heterodimers. As the temperature increases, a progressive reduction of Fe3O4 to FeO occurs helped by the thermolysis of the surfactants; while above 550 K Fe3Pt starts to be formed. At 840 K an abrupt increase of FeO further drives the phase transformation to stabilize the iron platinum soft phase. Thus, the Fe3O4 reduction acts as catalyst that promotes the Fe and Pt interdiffusion between the Pt-rich FePt and Fe3O4/FeO to form Fe3Pt instead of exchange coupled FePt/Fe3O4 with hard magnetic properties. In addition, the role of the interface of the heterodimer ends is discussed. The pre- and post-annealed samples were also characterized by TEM, XRD, EXAFS, magnetometry and Mössbauer spectroscopy.
△ Less
Submitted 25 February, 2011;
originally announced February 2011.
-
Synthesis and characterization of FePt/Au core-shell nanoparticles
Authors:
P. de la Presa,
M. Multigner,
M. P. Morales,
T. Rueda,
E. Fernandez-Pinel,
A. Hernando
Abstract:
In this work, the structural and magnetic properties of the gold-coated FePt nanoparticles synthesized from high-temperature solution phase are presented. The amount of gold was optimized to obtain most of the FePt particles coated. The particle diameter increases from 4 to 10 nm as observed by TEM. The magnetic properties are largely affected by the coating. At low temperature, the coercive fie…
▽ More
In this work, the structural and magnetic properties of the gold-coated FePt nanoparticles synthesized from high-temperature solution phase are presented. The amount of gold was optimized to obtain most of the FePt particles coated. The particle diameter increases from 4 to 10 nm as observed by TEM. The magnetic properties are largely affected by the coating. At low temperature, the coercive field Hc of the coated nanoparticles decreases about three times respect to the uncoated and the blocking temperature reduces to the half. The changes of the magnetic behavior are discussed in terms of the effect of the gold atoms at the FePt core surface.
△ Less
Submitted 25 November, 2009;
originally announced November 2009.
-
Ligand exchange in gold-coated FePt nanoparticles
Authors:
P. de la Presa,
T. Rueda,
M. P. Morales,
A. Hernando
Abstract:
In this work we present the magnetic properties of gold coated FePt nanoparticles and the study of stable aqueous dispersions of FePt@Au and FePt synthesized after ligand exchange with mercaptoundecanoic acid. The particle size determined from TEM micrographs goes from 4 nm for the uncoated nanoparticles to a maximum of 10 nm for the gold coated ones indicating that the thickness of the shell ra…
▽ More
In this work we present the magnetic properties of gold coated FePt nanoparticles and the study of stable aqueous dispersions of FePt@Au and FePt synthesized after ligand exchange with mercaptoundecanoic acid. The particle size determined from TEM micrographs goes from 4 nm for the uncoated nanoparticles to a maximum of 10 nm for the gold coated ones indicating that the thickness of the shell ranges from 1 to 3 nm. The magnetic characterization consists in hysteresis cycles at 10 and 300 K. The results show that, at low field and room temperature, the magnetic behavior of uncoated and coated nanoparticles are surprisingly quite similar. Since the gold coated nanoparticles keep the magnetic properties of FePt and the presence of gold improves the functionalization of nanoparticles, the system is suitable for biological application. Mercaptoundecanoic ligand transfer was used to render water stable nanoparticles in a wide pH range. Transmission electron microscopy and dynamic light scattering results show the nanoparticles slightly agglomerate after ligand exchange. Fourier transform infrared spectroscopy results suggest that thiol bind to the gold atoms of the surface.
△ Less
Submitted 23 November, 2009;
originally announced November 2009.
-
Magnetic Nanoparticles for Power Absorption: optimizing size, shape and magnetic properties
Authors:
M. A. Gonzalez-Fernandez,
T. Torres,
M. Andres-Verges,
R. Costo,
P. de la Presa,
C. J. Serna,
M. P. Morales,
C. Marquina,
M. R. Ibarra,
G. F. Goya
Abstract:
We present a study on the magnetic properties of naked and silica-coated Fe3O4 nanoparticles with sizes between 5 and 110 nm. Their efficiency as heating agents was assessed through specific power absorption (SPA) measurements as a function of particle size and shape. The results show a strong dependence of the SPA with the particle size, with a maximum around 30 nm, as expected for a Neel relax…
▽ More
We present a study on the magnetic properties of naked and silica-coated Fe3O4 nanoparticles with sizes between 5 and 110 nm. Their efficiency as heating agents was assessed through specific power absorption (SPA) measurements as a function of particle size and shape. The results show a strong dependence of the SPA with the particle size, with a maximum around 30 nm, as expected for a Neel relaxation mechanism in single-domain particles. The SiO2 shell thickness was found to play an important role in the SPA mechanism by hindering the heat outflow, thus decreasing the heating efficiency. It is concluded that a compromise between good heating efficiency and surface functionality for biomedical purposes can be attained by making the SiO2 functional coating as thin as possible.
△ Less
Submitted 25 January, 2009;
originally announced January 2009.
-
Anisotropic relaxations introduced by Cd impurities in Rutile TiO2: first-principles calculations and experimental support
Authors:
L. A. Errico,
G. Fabricius,
M. Rentería,
P. de la Presa,
M. Forker
Abstract:
We present an ab initio study of the relaxations introduced in TiO2 when a Cd impurity substitutes a Ti atom and the experimental test of this calculation by a perturbed-angular-correlation (PAC) measurement of the orientation of the electric-field gradient (EFG) tensor at the Cd site. The ab-initio calculation predicts strong anisotropic relaxations of the nearest oxygen neighbors of the impuri…
▽ More
We present an ab initio study of the relaxations introduced in TiO2 when a Cd impurity substitutes a Ti atom and the experimental test of this calculation by a perturbed-angular-correlation (PAC) measurement of the orientation of the electric-field gradient (EFG) tensor at the Cd site. The ab-initio calculation predicts strong anisotropic relaxations of the nearest oxygen neighbors of the impurity and a change of the orientation of the largest EFG tensor component, V33, from the [001] to the [110] direction upon substitution of a Ti atom by a Cd impurity. The last prediction is confirmed by the PAC experiment that shows that V33 at the Cd site is parallel to either the [110] or the [1\bar{1}0] crystal axis.
△ Less
Submitted 21 June, 2002; v1 submitted 15 April, 2002;
originally announced April 2002.