Suppression of superconductivity in layered Bi4O4S3 by Ag doping
Authors:
S. G. Tan,
P. Tong,
Y. Liu,
W. J. Lu,
L. J. Li,
B. C. Zhao,
Y. P. Sun
Abstract:
We report X-ray diffraction, magnetization and transport measurements for polycrystalline samples of the new layered superconductor Bi4-xAgxO4S3 (0<x<0.2). The superconducting transition temperature (TC) decreases gradually and finally suppressed for x>0.10. Accordingly, the resistivity changes from a metallic behavior for x<0.1 to a semiconductor-like behavior for x>0.1. The analysis of Seebeck c…
▽ More
We report X-ray diffraction, magnetization and transport measurements for polycrystalline samples of the new layered superconductor Bi4-xAgxO4S3 (0<x<0.2). The superconducting transition temperature (TC) decreases gradually and finally suppressed for x>0.10. Accordingly, the resistivity changes from a metallic behavior for x<0.1 to a semiconductor-like behavior for x>0.1. The analysis of Seebeck coefficient shows there are two types of electron-like carriers dominate at different temperature regions, indicative of a multiband effect responsible for the transport properties. The suppression of superconductivity and the increased resistivity can be attributed to a shift of the Fermi level to the lower-energy side upon doping, which reduces the density of states at EF. Further, our result indicates the superconductivity in the parent Bi4O4S3 is intrinsic and the dopant Ag prefers to enter the BiS2 layers, which may essentially modify the electronic structure.
△ Less
Submitted 27 August, 2012;
originally announced August 2012.
-
Superconducting and thermoelectric properties of new layered Superconductor Bi4O4S3
Authors:
S. G. Tan,
L. J. Li,
Y. Liu,
P. Tong,
B. C. Zhao,
W. J. Lu,
Y. P. Sun
Abstract:
Polycrystalline sample of the new layered superconductor Bi4O4S3 is successfully synthesized by solid-state reaction method by using Bi, S and Bi2O3 powders with one step reaction. The superconducting transition temperature (Tconset=4.5 K), the zero resistance transition temperature (Tc0=4.07 K) and the diamagnetic transition temperature (4.02 K at H=10 Oe) were confirmed by electrical transport a…
▽ More
Polycrystalline sample of the new layered superconductor Bi4O4S3 is successfully synthesized by solid-state reaction method by using Bi, S and Bi2O3 powders with one step reaction. The superconducting transition temperature (Tconset=4.5 K), the zero resistance transition temperature (Tc0=4.07 K) and the diamagnetic transition temperature (4.02 K at H=10 Oe) were confirmed by electrical transport and magnetic measurements. Also, our results indicate a typical type II-superconductor behavior. In addition, a large thermoelectric effect was observed with a dimensionless thermoelectric figure of merit (ZT) of about 0.03 at 300K, indicating Bi4O4S3 can be a potential thermoelectric material.
△ Less
Submitted 23 July, 2012;
originally announced July 2012.
-
Long-range Ferromagnetic Ordering and Magnetic Phase Transition in Metal-organic Frameworks
Authors:
L. Shen,
J. B. Yi,
B. C. Zhao,
S. C. Xiang,
B. L. Chen,
M. -F. Ng,
S. -W. Yang,
L. Wang,
J. Ding,
Y. P. Feng
Abstract:
The new version will be updated soon.
The new version will be updated soon.
△ Less
Submitted 18 November, 2010; v1 submitted 15 May, 2009;
originally announced May 2009.
-
Structural, magnetic and transport properties in the Pr-doped manganites La0.9-xPrxTe0.1MnO3
Authors:
J. Yang,
W. H. Song,
Y. Q. Ma,
R. L. Zhang,
B. C. Zhao,
Z. G. Sheng,
G. H. Zheng,
J. M. Dai,
Y. P. Sun
Abstract:
The effect of Pr-doping on structural, magnetic and transport properties in electron-doped manganites La0.9-xPrxTe0.1MnO3 with fixed carrier concentration are investigated. The room temperature structural transition from rhombohedral (R3C) to orthorhombic (Pbnm) symmetry is found in the samples with by the Rietveld refinement of x-ray powder diffraction patterns. The Curie temperature of samples…
▽ More
The effect of Pr-doping on structural, magnetic and transport properties in electron-doped manganites La0.9-xPrxTe0.1MnO3 with fixed carrier concentration are investigated. The room temperature structural transition from rhombohedral (R3C) to orthorhombic (Pbnm) symmetry is found in the samples with by the Rietveld refinement of x-ray powder diffraction patterns. The Curie temperature of samples decreases and the transition becomes broader with increasing Pr-doping level. For the samples with, there exist insulator-metal (I-M) transition. And the low-temperature I-M transition is observed at about 66K for the sample with x = 0.36, which may be related to the opening of a new percolation channel. For the samples with, r(T) curves display the semiconducting behavior (dρ/dT < 0) in both high-temperature PM phase and low-temperature FM phase. The results are discussed in terms of the increased bending of the Mn-O-Mn bond with decreasing the average ionic radius of the A-site element <r_A> and the tolerance factor, resulting in the narrowing of the bandwidth, the decrease of the mobility of electrons and the weakening of DE interaction caused by the substitution of smaller Pr3+ ions for larger La3+ ion.
△ Less
Submitted 13 August, 2004;
originally announced August 2004.
-
Insulator-metal transition and the magnetic phase diagram of La1-xTexMnO3
Authors:
J. Yang,
W. H. Song,
Y. Q. Ma,
R. L. Zhang,
B. C. Zhao,
Z. G. Sheng,
G. H. Zheng,
J. M. Dai,
Y. P. Sun
Abstract:
The structural, electrical transport and magnetic properties of perovskite oxides La1-xTexMnO3 have been investigated and thus the magnetic phase diagram of La1-xTexMnO3 compounds as a function of temperature and the doping level x has been obtained. All samples have rhombohedral structure and undergo paramagnetic-ferromagnetic (PM-FM) transition accompanied with metal-insulator transition (MIT)…
▽ More
The structural, electrical transport and magnetic properties of perovskite oxides La1-xTexMnO3 have been investigated and thus the magnetic phase diagram of La1-xTexMnO3 compounds as a function of temperature and the doping level x has been obtained. All samples have rhombohedral structure and undergo paramagnetic-ferromagnetic (PM-FM) transition accompanied with metal-insulator transition (MIT). Whereas a charge ordering (CO) transition begins to appear at for the sample with x=0.60. Moreover, the variation of the Curie temperature and the MIT temperature is quite complex and the results are discussed in terms of three factors including the average A-site cation radius <rA>, the size mismatch and the Te content. In addition, there has an evident magnetoresistance (MR) at low temperatures for all samples.
△ Less
Submitted 13 August, 2004;
originally announced August 2004.
-
The effect of grain size on electrical transport and magnetic properties of La0.9Te0.1MnO3
Authors:
J. Yang,
B. C. Zhao,
R. L. Zhang,
Y. Q. Ma,
Z. G. Sheng,
W. H. Song,
Y. P. Sun
Abstract:
The effect of grain size on structural, magnetic and transport properties in electron-doped manganites La0.9Te0.1MnO3 has been investigated. All samples show a rhombohedral structure with the space group at room temperature. It shows that the Mn-O-Mn bond angle decreases and the Mn-O bond length increases with the increase of grain size. All samples undergo paramagnetic (PM)-ferromagnetic (FM) p…
▽ More
The effect of grain size on structural, magnetic and transport properties in electron-doped manganites La0.9Te0.1MnO3 has been investigated. All samples show a rhombohedral structure with the space group at room temperature. It shows that the Mn-O-Mn bond angle decreases and the Mn-O bond length increases with the increase of grain size. All samples undergo paramagnetic (PM)-ferromagnetic (FM) phase transition and an interesting phenomenon that both magnetization and the Curie temperature decrease with increasing grain size is observed, which is suggested to mainly originate from the increase of the Mn-O bond length . Additionally, obviously increases with decreasing grain size due to the increase of both the height and width of tunneling barriers with decreasing the grain size. The results indicate that both the intrinsic colossal magnetoresistance (CMR) and the extrinsic the extrinsic interfacial magnetoresistance (IMR) can be effectively tuned in La0.9Te0.1MnO3 by changing grain size.
△ Less
Submitted 26 August, 2004; v1 submitted 13 August, 2004;
originally announced August 2004.
-
Structural, magnetic and transport properties in the Cu-doped manganites La0.85Te0.15Mn1-xCuxO3 (0 \leq x \leq 0.20)
Authors:
J. Yang,
W. H. Song,
Y. Q. Ma,
R. L. Zhang,
B. C. Zhao,
Z. G. Sheng,
G. H. Zheng,
J. M. Dai,
Y. P. Sun
Abstract:
The effect of Cu-doping at Mn-site on structural, magnetic and transport properties in electron-doped manganites La0.85Te0.15Mn1-xCuxO3 has been investigated. Based on the analysis of structural parameter variations, the valence state of the Cu ion in Cu-doped manganites is suggested to be +2. All samples undergo the paramagnetic-ferromagnetic (PM-FM) phase transition. The Curie temperature decr…
▽ More
The effect of Cu-doping at Mn-site on structural, magnetic and transport properties in electron-doped manganites La0.85Te0.15Mn1-xCuxO3 has been investigated. Based on the analysis of structural parameter variations, the valence state of the Cu ion in Cu-doped manganites is suggested to be +2. All samples undergo the paramagnetic-ferromagnetic (PM-FM) phase transition. The Curie temperature decreases and the transition becomes broader with increasing Cu-doping level, in contrast, the magnetization magnitude of Cu-doping samples at low temperatures increase as x \leq 0.15. The insulator-metal (I-M) transition moves to lower temperatures with increasing Cu-doping content and disappears as x > 0.1. In addition, the higher temperature resistivity r peak in double-peak-like r(T) curves observed in no Cu-doping sample is completely suppressed as Cu-doping level x = 0.1 and r(T) curve only shows single I-M transition at the low temperature well below . The results are discussed according to the change of magnetic exchange interaction caused by Cu-doping.
△ Less
Submitted 20 September, 2004; v1 submitted 12 August, 2004;
originally announced August 2004.
-
The effect of oxygen stoichiometry on electrical transport and magnetic properties of La0.9Te0.1MnOy
Authors:
J. Yang,
W. H. Song,
R. L. Zhang,
Y. Q. Ma,
B. C. Zhao,
Z. G. Sheng,
G. H. Zheng,
J. M. Dai,
Y. P. Sun
Abstract:
The effect of the variation of oxygen content on structural, magnetic and transport properties in the electron-doped manganites La0.9Te0.1MnOy has been investigated. All samples show a rhombohedral structure with the space group . The Curie temperature decreases and the paramagnetic-ferromagnetic (PM-FM) transition becomes broader with the reduction of oxygen content. The resistivity of the anne…
▽ More
The effect of the variation of oxygen content on structural, magnetic and transport properties in the electron-doped manganites La0.9Te0.1MnOy has been investigated. All samples show a rhombohedral structure with the space group . The Curie temperature decreases and the paramagnetic-ferromagnetic (PM-FM) transition becomes broader with the reduction of oxygen content. The resistivity of the annealed samples increases slightly with a small reduction of oxygen content. Further reduction in the oxygen content, the resistivity maximum increases by six orders of magnitude compared with that of the as-prepared sample, and the r(T) curves of samples with y = 2.86 and y = 2.83 display the semiconducting behavior () in both high-temperature PM phase and low-temperature FM phase, which is considered to be related to the appearance of superexchange ferromagnetism (SFM) and the localization of carriers. The results are discussed in terms of the combined effects of the increase in the Mn2+/(Mn2++Mn3+) ratio, the partial destruction of double exchange (DE) interaction, and the localization of carriers due to the introduction of oxygen vacancies in the Mn-O-Mn network.
△ Less
Submitted 12 August, 2004;
originally announced August 2004.