Effects of Neutron Irradiation on Carbon Doped MgB2 Wire Segments
Authors:
R. H. T. Wilke,
S. L. Bud'ko,
P. C. Canfield,
D. K. Finnemore,
Raymond J. Suplinskas,
J. Farmer,
S. T. Hannahs
Abstract:
We have studied the evolution of superconducting and normal state properties of neutron irradiated Mg(B$_{.962}$C$_{.038}$)$_2$ wire segments as a function of post exposure annealing time and temperature. The initial fluence fully suppressed superconductivity and resulted in an anisotropic expansion of the unit cell. Superconductivity was restored by post-exposure annealing. The upper critical f…
▽ More
We have studied the evolution of superconducting and normal state properties of neutron irradiated Mg(B$_{.962}$C$_{.038}$)$_2$ wire segments as a function of post exposure annealing time and temperature. The initial fluence fully suppressed superconductivity and resulted in an anisotropic expansion of the unit cell. Superconductivity was restored by post-exposure annealing. The upper critical field, H$_{c2}$(T=0), approximately scales with T$_c$ starting with an undamaged T$_c$ near 37 K and H$_{c2}$(T=0) near 32 T. Up to an annealing temperature of 400 $^ o$C the recovery of T$_c$ tends to coincide with a decrease in the normal state resistivity and a systematic recovery of the lattice parameters. Above 400 $^ o$C a decrease in order along the c- direction coincides with an increase in resistivity, but no apparent change in the evolution of T$_c$ and H$_{c2}$. To first order, it appears that carbon doping and neutron damaging effect the superconducting properties of MgB$_2$ independently.
△ Less
Submitted 12 July, 2005;
originally announced July 2005.
-
Superconducting and Normal State Properties of Neutron Irradiated MgB2
Authors:
R. H. T. Wilke,
S. L. Bud'ko,
P. C. Canfield,
J. Famer,
S. T. Hannahs
Abstract:
We have performed a systematic study of the evolution of the superconducting and normal state properties of neutron irradiated MgB$_2$ wire segments as a function of fluence and post exposure annealing temperature and time. All fluences used suppressed the transition temperature, Tc, below 5 K and expanded the unit cell. For each annealing temperature Tc recovers with annealing time and the uppe…
▽ More
We have performed a systematic study of the evolution of the superconducting and normal state properties of neutron irradiated MgB$_2$ wire segments as a function of fluence and post exposure annealing temperature and time. All fluences used suppressed the transition temperature, Tc, below 5 K and expanded the unit cell. For each annealing temperature Tc recovers with annealing time and the upper critical field, Hc2(T=0), approximately scales with Tc. By judicious choice of fluence, annealing temperature and time, the Tc of damaged MgB2 can be tuned to virtually any value between 5 and 39 K. For higher annealing temperatures and longer annealing times the recovery of Tc tends to coincide with a decrease in the normal state resistivity and a systematic recovery of the lattice parameters.
△ Less
Submitted 22 March, 2006; v1 submitted 7 July, 2005;
originally announced July 2005.
-
Synthesis of Mg(B$_{1-x}$C$_x$)$_2$ Powders
Authors:
R. H. T. Wilke,
S. L. Bud'ko,
P. C. Canfield,
D. K. Finnemore,
S. T. Hannahs
Abstract:
We have synthesized bulk Mg(B$_{1-x}$C$_x$)$_2$ from a mixture of elemental Mg, B, and the binary compound B$_4$C. Carbon incorporation was dramatically improved by a two step reaction process at an elevated temperature of 1200 $^o$C. This reaction process results in a solubility limit near x$\sim$0.07. We found that impurities in the starting B cause an additive suppression of T$_c$. We combine…
▽ More
We have synthesized bulk Mg(B$_{1-x}$C$_x$)$_2$ from a mixture of elemental Mg, B, and the binary compound B$_4$C. Carbon incorporation was dramatically improved by a two step reaction process at an elevated temperature of 1200 $^o$C. This reaction process results in a solubility limit near x$\sim$0.07. We found that impurities in the starting B cause an additive suppression of T$_c$. We combine these data with T$_c$ and H$_{c2}$(T=0) data from CVD wires as well as plasma spray synthesized powders and present a unifying H$_{c2}$ and T$_c$ versus x plot.
△ Less
Submitted 6 July, 2005;
originally announced July 2005.
-
Superconductivity in MgB_2 doped with Ti and C
Authors:
R. H. T. Wilke,
S. L. Bud'ko,
P. C. Canfield,
M. J. Kramer,
Y. Q. Wu,
D. K. Finnemore,
R. J. Suplinskas,
J. V. Marzik,
S. T. Hannahs
Abstract:
Measurements of the superconducting upper critical field, H_{c2}, and critical current density, J_c, have been carried out for MgB_2 doped with Ti and/or C in order to explore the problems encountered if these dopants are used to enhance the superconducting performance. Carbon replaces boron in the MgB_2 lattice and apparently shortens the electronic mean free path thereby raising H_c2. Titanium…
▽ More
Measurements of the superconducting upper critical field, H_{c2}, and critical current density, J_c, have been carried out for MgB_2 doped with Ti and/or C in order to explore the problems encountered if these dopants are used to enhance the superconducting performance. Carbon replaces boron in the MgB_2 lattice and apparently shortens the electronic mean free path thereby raising H_c2. Titanium forms precipitates of either TiB or TiB_2 that enhance the flux pinning and raise J_c. Most of these precipitates are intra-granular in the MgB_2 phase. If approximately 0.5% Ti and approximately 2% C are co-deposited with B to form doped boron fibers and these fibers are in turn reacted in Mg vapor to form MgB_2, the resulting superconductor has H_{c2}(T=0) ~ 25 T and J_c ~ 10,000 A/cm**2 at 5 K and 2.2 T.
△ Less
Submitted 22 November, 2004;
originally announced November 2004.
-
Effect of pressure on the superconducting transition temperature of doped and neutron-damaged MgB2
Authors:
S. L. Bud'ko,
R. H. T. Wilke,
M. Angst,
P. C. Canfield
Abstract:
Measurements of the superconducting transition temperatures for Al-doped, C-doped and neutron-damaged-annealed MgB2 samples under pressure up to ~8 kbar are presented. The dT_c/dP values change systematically with the decrease of the ambient pressure T_c in a regular fashion. The evolution of the pressure derivatives can be understood assuming that the change in phonon spectrum is a dominant con…
▽ More
Measurements of the superconducting transition temperatures for Al-doped, C-doped and neutron-damaged-annealed MgB2 samples under pressure up to ~8 kbar are presented. The dT_c/dP values change systematically with the decrease of the ambient pressure T_c in a regular fashion. The evolution of the pressure derivatives can be understood assuming that the change in phonon spectrum is a dominant contribution to dT_c/dP.
△ Less
Submitted 5 November, 2004;
originally announced November 2004.
-
The different development of the anisotropic upper critical field in MgB2 by aluminum and carbon doping
Authors:
M. Angst,
S. L. Bud'ko,
R. H. T. Wilke,
P. C. Canfield
Abstract:
The temperature dependence of the upper critical field, Hc2, for both field directions in partially substituted polycrystalline MgB2 was determined. Whereas the suppression of Tc is similar for aluminum and carbon substituted samples, Hc2 is affected by the substitution in profoundly different ways. In the case of Al substitution changes can tentatively be described by intrinsic effects (shift o…
▽ More
The temperature dependence of the upper critical field, Hc2, for both field directions in partially substituted polycrystalline MgB2 was determined. Whereas the suppression of Tc is similar for aluminum and carbon substituted samples, Hc2 is affected by the substitution in profoundly different ways. In the case of Al substitution changes can tentatively be described by intrinsic effects (shift of the Fermi level). In the C substituted samples, Hc2 is increased drastically, and extrinsic effects (disorder) have to play a major role. The strong contrast between the two substitutions is discussed, taking into account three relevant scattering rates.
△ Less
Submitted 27 October, 2004;
originally announced October 2004.
-
Systematic study of the two band/two gap superconductivity in carbon-substituted MgB2 by point-contact spectroscopy
Authors:
Z. Holanova,
P. Szabo,
P. Samuely,
R. H. T. Wilke,
S. L. Bud'ko,
P. C. Canfield
Abstract:
Point-contact measurements on the carbon-substituted Mg(B$_{1-x}$C$_x$)$_2$ filament/powder samples directly reveal a retention of the two superconducting energy gaps in the whole doping range from $x = 0$ to $x \approx 0.1$. The large gap on the $σ$-band is decreased in an essentially linear fashion with increasing the carbon concentrations. The changes in the the small gap $Δ_π$ up to 3.8 % C…
▽ More
Point-contact measurements on the carbon-substituted Mg(B$_{1-x}$C$_x$)$_2$ filament/powder samples directly reveal a retention of the two superconducting energy gaps in the whole doping range from $x = 0$ to $x \approx 0.1$. The large gap on the $σ$-band is decreased in an essentially linear fashion with increasing the carbon concentrations. The changes in the the small gap $Δ_π$ up to 3.8 % C are proportionally smaller and are more difficult to detect but for the heavily doped sample with $x \approx 0.1$ and $T_c = 22$ K both gaps are still present, and significantly reduced, consistent with a strong essentially linear, reduction of each gap with the transition temperature.
△ Less
Submitted 5 April, 2004;
originally announced April 2004.
-
Systematic effects of carbon doping on the superconducting properties of Mg(B$_{1-x}$C$_x$)$_2$
Authors:
R. H. T. Wilke,
S. L. Bud'ko,
P. C. Canfield,
D. K. Finnemore,
Raymond J. Suplinskas,
S. T. Hannahs
Abstract:
The upper critical field, $H_{c2}$, of Mg(B$_{1-x}$C$_x$)$_2$ has been measured in order to probe the maximum magnetic field range for superconductivity that can be attained by C doping. Carbon doped boron filaments are prepared by CVD techniques, and then these fibers are then exposed to Mg vapor to form the superconducting compound. The transition temperatures are depressed about $1 K/%$ C and…
▽ More
The upper critical field, $H_{c2}$, of Mg(B$_{1-x}$C$_x$)$_2$ has been measured in order to probe the maximum magnetic field range for superconductivity that can be attained by C doping. Carbon doped boron filaments are prepared by CVD techniques, and then these fibers are then exposed to Mg vapor to form the superconducting compound. The transition temperatures are depressed about $1 K/%$ C and $H_{c2}(T=0)$ rises at about $5 T/%$ C. This means that 3.5% C will depress $T_c$ from $39.2 K$ to $36.2 K$ and raise $H_{c2}(T=0)$ from $16.0 T$ to $32.5 T$. Higher fields are probably attainable in the region of 5% C to 7% C. These rises in $H_{c2}$ are accompanied by a rise in resistivity at $40 K$ from about $0.5 μΩcm$ to about $10 μΩcm$. Given that the samples are polycrystalline wire segments, the experimentally determined $H_{c2}(T)$ curves represent the upper $H_{c2}(T)$ manifold associated with $H\perp c$.
△ Less
Submitted 10 December, 2003;
originally announced December 2003.
-
Intra-granular Ti precipitates in MgB2
Authors:
M. J. Kramer,
S. L. Bud'ko,
P. C. Canfield,
R. H. T. Wilke,
D. K. Finnemore,
R. J. Suplinskas
Abstract:
Superconducting magnesium diboride has been prepared with intra-granular TiB precipitates that have appropriate size and spacing for the pinning of superconducting vortices. The TiB particles have a size ranging from 1 nm to 20 nm and a spacing about 5 times as large. By co-depositing Ti and B on a commercial carbon coated silicon carbide substrate with chemical vapor deposition methods, it was…
▽ More
Superconducting magnesium diboride has been prepared with intra-granular TiB precipitates that have appropriate size and spacing for the pinning of superconducting vortices. The TiB particles have a size ranging from 1 nm to 20 nm and a spacing about 5 times as large. By co-depositing Ti and B on a commercial carbon coated silicon carbide substrate with chemical vapor deposition methods, it was possible to obtain a starting fiber with Ti well dispersed in the B. Reacting these fibers in a Mg vapor then transformed the fiber into a superconductor capable of carrying 10,000 A/cm^2 at 25K and 1 T. The Ti-B bonds are strong enough that there is relatively little migration of the Ti as the MgB2 grains form around the TiB precipitates. TiB2 precipitates, if they are present, can not be seen in the selected area diffraction pictures that show the TiB precipitates.
△ Less
Submitted 21 February, 2003;
originally announced February 2003.
-
Spectral ergodicity and normal modes in ensembles of sparse matrices
Authors:
A. D. Jackson,
C. Mejia-Monasterio,
T. Rupp,
M. Saltzer,
T. Wilke
Abstract:
We investigate the properties of sparse matrix ensembles with particular regard for the spectral ergodicity hypothesis, which claims the identity of ensemble and spectral averages of spectral correlators. An apparent violation of the spectral ergodicity is observed. This effect is studied with the aid of the normal modes of the random matrix spectrum, which describe fluctuations of the eigenvalu…
▽ More
We investigate the properties of sparse matrix ensembles with particular regard for the spectral ergodicity hypothesis, which claims the identity of ensemble and spectral averages of spectral correlators. An apparent violation of the spectral ergodicity is observed. This effect is studied with the aid of the normal modes of the random matrix spectrum, which describe fluctuations of the eigenvalues around their average positions. This analysis reveals that spectral ergodicity is not broken, but that different energy scales of the spectra are examined by the two averaging techniques. Normal modes are shown to provide a useful complement to traditional spectral analysis with possible applications to a wide range of physical systems.
△ Less
Submitted 21 September, 2000;
originally announced September 2000.
-
Stochastic field theory for a Dirac particle propagating in gauge field disorder
Authors:
T. Guhr,
T. Wilke,
H. A. Weidenmueller
Abstract:
Recent theoretical and numerical developments show analogies between quantum chromodynamics (QCD) and disordered systems in condensed matter physics. We study the spectral fluctuations of a Dirac particle propagating in a finite four dimensional box in the presence of gauge fields. We construct a model which combines Efetov's approach to disordered systems with the principles of chiral symmetry…
▽ More
Recent theoretical and numerical developments show analogies between quantum chromodynamics (QCD) and disordered systems in condensed matter physics. We study the spectral fluctuations of a Dirac particle propagating in a finite four dimensional box in the presence of gauge fields. We construct a model which combines Efetov's approach to disordered systems with the principles of chiral symmetry and QCD. To this end, the gauge fields are replaced with a stochastic white noise potential, the gauge field disorder. Effective supersymmetric non-linear sigma-models are obtained. Spontaneous breaking of supersymmetry is found. We rigorously derive the equivalent of the Thouless energy in QCD. Connections to other low-energy effective theories, in particular the Nambu-Jona-Lasinio model and chiral perturbation theory, are found.
△ Less
Submitted 14 October, 1999;
originally announced October 1999.