Creep properties and deformation mechanisms of single-crystalline $γ^\prime$-strengthened superalloys in dependence of the Co/Ni ratio
Authors:
Nicklas Volz,
Christopher H. Zenk,
Nicolas Karpstein,
Malte Lenz,
Erdmann Spiecker,
Mathias Göken,
Steffen Neumeier
Abstract:
Co-base superalloys are considered as promising high temperature materials besides the well-established Ni-base superalloys. However, Ni appears to be an indispensable alloying element also in Co-base superalloys. To address the influence of the base elements on the deformation behavior, high-temperature compressive creep experiments were performed on a single crystal alloy series that was designe…
▽ More
Co-base superalloys are considered as promising high temperature materials besides the well-established Ni-base superalloys. However, Ni appears to be an indispensable alloying element also in Co-base superalloys. To address the influence of the base elements on the deformation behavior, high-temperature compressive creep experiments were performed on a single crystal alloy series that was designed to exhibit a varying Co/Ni ratio and a constant Al, W and Cr content. Creep tests were performed at 900 °C and 250 MPa and the resulting microstructures and defect configurations were characterized via electron microscopy. The minimum creep rates differ by more than one order of magnitude with changing Co/Ni ratio. An intermediate CoNi-base alloy exhibits the overall highest creep strength. Several strengthening contributions like solid solution strengthening of the $γ$ phase, effective diffusion coefficients or stacking fault energies were quantified. Precipitate shearing mechanisms differ significantly when the base element content is varied. While the Ni-rich superalloys exhibit SISF and SESF shearing, the Co-rich alloys develop extended APBs when the $γ^\prime$ phase is cut. This is mainly attributed to a difference in planar fault energies, caused by a changing segregation behavior. As result, it is assumed that the shearing resistivity and the occurring deformation mechanisms in the $γ^\prime$ phase are crucial for the creep properties of the investigated alloy series.
△ Less
Submitted 14 September, 2021;
originally announced September 2021.
Understanding creep of a single-crystalline Co-Al-W-Ta superalloy by studying the deformation mechanism, segregation tendency and stacking fault energy
Authors:
Nicklas Volz,
Fei Xue,
Christopher H. Zenk,
Andreas Bezold,
Stefan Gabel,
Aparna P. A. Subramanyam,
Ralf Drautz,
Thomas Hammerschmidt,
Surendra K. Makineni,
Baptiste Gault,
Mathias Göken,
Steffen Neumeier
Abstract:
A systematic study of the compression creep properties of a single-crystalline Co-base superalloy (Co-9Al-7.5W-2Ta) was conducted at 950 °C, 975 °C and 1000 °C to reveal the influence of temperature and the resulting diffusion velocity of solutes like Al, W and Ta on the deformation mechanisms. Two creep rate minima are observed at all temperatures indicating that the deformation mechanisms causin…
▽ More
A systematic study of the compression creep properties of a single-crystalline Co-base superalloy (Co-9Al-7.5W-2Ta) was conducted at 950 °C, 975 °C and 1000 °C to reveal the influence of temperature and the resulting diffusion velocity of solutes like Al, W and Ta on the deformation mechanisms. Two creep rate minima are observed at all temperatures indicating that the deformation mechanisms causing these minima are quite similar. Atom-probe tomography analysis reveals elemental segregation to stacking faults, which had formed in the $γ\prime$ phase during creep. Density-functional-theory calculations indicate segregation of W and Ta to the stacking fault and an associated considerable reduction of the stacking fault energy. Since solutes diffuse faster at a higher temperature, segregation can take place more quickly. This results in a significantly faster softening of the alloy, since cutting of the $γ\prime$ precipitate phase by partial dislocations is facilitated through segregation already during the early stages of creep. This is confirmed by transmission electron microscopy analysis. Therefore, not only the smaller precipitate fraction at higher temperatures is responsible for the worse creep properties, but also faster diffusion-assisted shearing of the $γ\prime$ phase by partial dislocations. The understanding of these mechanisms will help in future alloy development by offering new design criteria.
△ Less
Submitted 1 June, 2021; v1 submitted 31 May, 2021;
originally announced May 2021.