Residual resistance ratio of Cu stabilizer in commercial REBCO tapes
Authors:
Jun Lu,
Yan Xin,
Vince Toplosky,
Jeremy Levitan,
Ke Han,
Jane Wadhams,
Munir Humayun,
Dmytro Abraimov,
Hongyu Bai
Abstract:
Residual resistance ratio (RRR) of Cu stabilizer in REBCO coated conductor is an important design parameter for REBCO magnets. In this work, we measured RRR of electroplated Cu stabilizer in commercial REBCO tapes. Over 130 samples were measured for the quality assurance programs of REBCO magnet projects at the National High Magnetic Field Laboratory, USA (NHMFL). The average RRR value was above 5…
▽ More
Residual resistance ratio (RRR) of Cu stabilizer in REBCO coated conductor is an important design parameter for REBCO magnets. In this work, we measured RRR of electroplated Cu stabilizer in commercial REBCO tapes. Over 130 samples were measured for the quality assurance programs of REBCO magnet projects at the National High Magnetic Field Laboratory, USA (NHMFL). The average RRR value was above 50. In order to investigate the factors that influence RRR, several samples were analyzed by using scanning electron microscopy, secondary ion mass spectroscopy, and inductively coupled plasma mass spectroscopy. We found that, in our samples, RRR was strongly correlated with the grain size. We demonstrated that RRR was primarily determined by grain boundary resistivity. Lower RRR was also strongly correlated with higher concentration of chlorine impurity. This is explained by that higher chlorine impurity hindered the grain growth in the room temperature self annealing process resulting smaller grain. Smaller grain resulted in lower RRR. In addition, thermal annealing significantly enhanced RRR. An activation energy of 0.4 eV was obtained from the annealing experiment which corresponds to the activation of Cu grain growth.
△ Less
Submitted 13 October, 2024;
originally announced October 2024.
Low temperature physical properties of Co-35Ni-20Mo-10Cr alloy MP35N
Authors:
J. Lu,
V. J. Toplosky,
R. E. Goddard,
K. Han
Abstract:
Multiphase Co-35Ni-20Mo-10Cr alloy MP35N is a high strength alloy with excellent corrosion resistance. Its applications span chemical, medical, and food processing industries. Thanks to its high modulus and high strength, it found applications in reinforcement of ultra-high field pulsed magnets. Recently, it has also been considered for reinforcement in superconducting wires used in ultra-high fie…
▽ More
Multiphase Co-35Ni-20Mo-10Cr alloy MP35N is a high strength alloy with excellent corrosion resistance. Its applications span chemical, medical, and food processing industries. Thanks to its high modulus and high strength, it found applications in reinforcement of ultra-high field pulsed magnets. Recently, it has also been considered for reinforcement in superconducting wires used in ultra-high field superconducting magnets. For these applications, accurate measurement of its physical properties at cryogenic temperatures is very important. In this paper, physical properties including electrical resistivity, specific heat, thermal conductivity, and magnetization of as-received and aged samples are measured from 2 to 300 K. The electrical resistivity of the aged sample is slightly higher than the as-received sample, both showing a weak linear temperature dependence in the entire range of 2 - 300 K. The measured specific heat Cp of 0.43 J/g-K at 295 K agrees with a theoretical prediction, but is significantly smaller than the values in the literature. The thermal conductivity between 2 and 300 K is in good agreement with the literature which is only available above 77 K. Magnetic property of MP35N changes significantly with aging. The as-received sample exhibits Curie paramagnetism with a Curie constant C = 0.175 K. While the aged sample contains small amounts of a ferromagnetic phase even at room temperature. The measured MP35N properties will be useful for the engineering design of pulsed magnets and superconducting magnets using MP35N as reinforcement.
△ Less