Near-infrared excitation of nitrogen-doped ultrananocrystalline diamond photoelectrodes in saline solution
Authors:
Andre Chambers,
Arman Ahnood,
Samira Falahatdoost,
Steve Yianni,
David Hoxley,
Brett C. Johnson,
David J. Garrett,
Snjezana Tomljenovic-Hanic,
Steven Prawer
Abstract:
Nitrogen-doped ultrananocrystalline diamond (N-UNCD) is a promising material for a variety of neural interfacing applications, due to its unique combination of high conductivity, bioinertness, and durability. One emerging application for N-UNCD is as a photoelectrode material for high-precision optical neural stimulation. This may be used for the treatment of neurological disorders and for implant…
▽ More
Nitrogen-doped ultrananocrystalline diamond (N-UNCD) is a promising material for a variety of neural interfacing applications, due to its unique combination of high conductivity, bioinertness, and durability. One emerging application for N-UNCD is as a photoelectrode material for high-precision optical neural stimulation. This may be used for the treatment of neurological disorders and for implantable bionic devices such as cochlear ear implants and retinal prostheses. N-UNCD is a well-suited material for stimulation photoelectrodes, exhibiting a photocurrent response to light at visible wavelengths with a high charge injection density [A. Ahnood, A. N. Simonov, J. S. Laird, M. I. Maturana, K. Ganesan, A. Stacey, M. R. Ibbotson, L. Spiccia, and S. Prawer, Appl. Phys. Lett. 108, 104103 (2016)]. In this study, the photoresponse of N-UNCD to near-infrared (NIR) irradiation is measured. NIR light has greater optical penetration through tissue than visible wavelengths, opening the possibility to stimulate previously inaccessible target cells. It is found that N-UNCD exhibits a photoresponsivity which diminishes rapidly with increasing wavelength and is attributed to transitions between mid-gap states and the conduction band tail associated with the graphitic phase present at the grain boundaries. Oxygen surface termination on the diamond films provides further enhancement of the injected charge per photon, compared to as-grown or hydrogen terminated surfaces. Based on the measured injected charge density, we estimate that the generated photocurrent of oxygen terminated N-UNCD is sufficient to achieve extracellular stimulation of brain tissue within the safe optical exposure limit.
△ Less
Submitted 20 November, 2018;
originally announced November 2018.
-
Dynamic stabilization of the optical resonances of single nitrogen-vacancy centers in diamond
Authors:
V. M. Acosta,
C. Santori,
A. Faraon,
Z. Huang,
K. -M. C. Fu,
A. Stacey,
D. A. Simpson,
S. Tomljenovic-Hanic,
K. Ganesan,
A. D. Greentree,
S. Prawer,
R. G. Beausoleil
Abstract:
We report electrical tuning by the Stark effect of the excited-state structure of single nitrogen-vacancy (NV) centers located less than ~100 nm from the diamond surface. The zero-phonon line (ZPL) emission frequency is controllably varied over a range of 300 GHz. Using high-resolution emission spectroscopy, we observe electrical tuning of the strengths of both cycling and spin-altering transition…
▽ More
We report electrical tuning by the Stark effect of the excited-state structure of single nitrogen-vacancy (NV) centers located less than ~100 nm from the diamond surface. The zero-phonon line (ZPL) emission frequency is controllably varied over a range of 300 GHz. Using high-resolution emission spectroscopy, we observe electrical tuning of the strengths of both cycling and spin-altering transitions. Under resonant excitation, we apply dynamic feedback to stabilize the ZPL frequency. The transition is locked over several minutes and drifts of the peak position on timescales greater than ~100 ms are reduced to a fraction of the single-scan linewidth, with standard deviation as low as 16 MHz (obtained for an NV in bulk, ultra-pure diamond). These techniques should improve the entanglement success probability in quantum communications protocols.
△ Less
Submitted 3 April, 2012; v1 submitted 22 December, 2011;
originally announced December 2011.
-
Depletion of nitrogen-vacancy color centers in diamond via hydrogen passivation
Authors:
A. Stacey,
T. J. Karle,
L. P. McGuinness,
B. C. Gibson,
K. Ganesan,
S. Tomljenovic-Hanic,
A. D. Greentree,
S. Prawer,
R. G. Beausoleil,
A. Hoffman
Abstract:
We show a marked reduction in the emission from nitrogen-vacancy (NV) color centers in single crystal diamond due to exposure of the diamond to hydrogen plasmas ranging from 700°C to 1000°C. Significant fluorescence reduction was observed beneath the exposed surface to at least 80mm depth after ~10 minutes, and did not recover after post-annealing in vacuum for seven hours at 1100°C. We attribute…
▽ More
We show a marked reduction in the emission from nitrogen-vacancy (NV) color centers in single crystal diamond due to exposure of the diamond to hydrogen plasmas ranging from 700°C to 1000°C. Significant fluorescence reduction was observed beneath the exposed surface to at least 80mm depth after ~10 minutes, and did not recover after post-annealing in vacuum for seven hours at 1100°C. We attribute the fluorescence reduction to the formation of NVH centers by the plasma induced diffusion of hydrogen. These results have important implications for the formation of nitrogen-vacancy centers for quantum applications, and inform our understanding of the conversion of nitrogen-vacancy to NVH, whilst also providing the first experimental evidence of long range hydrogen diffusion through intrinsic high-purity diamond material.
△ Less
Submitted 30 August, 2011;
originally announced August 2011.