Optical net gain measurement on Al$_{0.07}$Ga$_{0.93}$N/GaN multi-quantum well
Authors:
Quang Minh Thai,
Sergi Cuesta,
Lou Denaix,
Sylvain Hermelin,
Olivier Boisron,
Stephen T. Purcell,
Le Si Dang,
Eva Monroy
Abstract:
We present net gain measurements at room temperature in Al$_{0.07}$Ga$_{0.93}$N/GaN 10-period multi-quantum well emitting at 367 nm, using the variable stripe length method. Measurements were conducted at two different positions on the sample, where the net gain threshold was attained at 218 kW/cm$^{2}$ and 403 kW/cm$^{2}$. At the position with higher threshold, we observed an anomalous amplificat…
▽ More
We present net gain measurements at room temperature in Al$_{0.07}$Ga$_{0.93}$N/GaN 10-period multi-quantum well emitting at 367 nm, using the variable stripe length method. Measurements were conducted at two different positions on the sample, where the net gain threshold was attained at 218 kW/cm$^{2}$ and 403 kW/cm$^{2}$. At the position with higher threshold, we observed an anomalous amplification of the photoluminescence intensity that occurs for long stripe lengths (superior to 400 $μ$m) and high pumping power (superior to 550 kW/cm$^{2}$), leading to an overestimation of the gain value. We attribute such a phenomenon to the feedback provided by the reflection from cracks, which were created during the epitaxial growth due to the strong lattice mismatch between different layers. The highest gain value without anomalous amplification was 131 cm$^{-1}$, obtained at the maximum pumping power density of the experimental setup (743 kW/cm$^{2}$). Using the intrinsic efficiency limit of the cathodoluminescence process, we estimate a lower limit for electron beam pumped laser threshold at room temperature of 390 kW/cm$^{2}$ for this multi-quantum well structure.
△ Less
Submitted 4 August, 2021; v1 submitted 1 August, 2021;
originally announced August 2021.
-
AlGaN/GaN asymmetric graded-index separate confinement heterostructures designed for electron-beam pumped UV lasers
Authors:
Sergi Cuesta,
Yoann Curé,
Fabrice Donatini,
Lou Denaix,
Edith Bellet-Amalric,
Catherine Bougerol,
Vincent Grenier,
Quang-Minh Thai,
Gilles Nogues,
Stephen T. Purcell,
Le Si Dang,
Eva Monroy
Abstract:
We present a study of undoped AlGaN/GaN separate confinement heterostructures designed to operate as electron beam pumped ultraviolet lasers. We discuss the effect of spontaneous and piezoelectric polarization on carrier diffusion, comparing the results of cathodoluminescence with electronic simulations of the band structure and Monte Carlo calculations of the electron trajectories. Carrier collec…
▽ More
We present a study of undoped AlGaN/GaN separate confinement heterostructures designed to operate as electron beam pumped ultraviolet lasers. We discuss the effect of spontaneous and piezoelectric polarization on carrier diffusion, comparing the results of cathodoluminescence with electronic simulations of the band structure and Monte Carlo calculations of the electron trajectories. Carrier collection is significantly improved using an asymmetric graded-index separate confinement heterostructure (GRINSCH). The graded layers avoid potential barriers induced by polarization differences in the heterostructure and serve as strain transition buffers which reduce the mosaicity of the active region and the linewidth of spontaneous emission.
△ Less
Submitted 16 March, 2021; v1 submitted 6 January, 2021;
originally announced January 2021.
-
Internal quantum efficiency of AlGaN/AlN quantum dot superlattices for electron-pumped ultraviolet sources
Authors:
A. Harikumar,
F. Donatini,
C. Bougerol,
E. Bellet-Amalric,
Q. -M. Thai,
C. Dujardin,
I. Dimkou,
S. T. Purcell,
E. Monroy
Abstract:
In this paper, we describe the growth and characterization of 530-nm-thick superlattices (100 periods) of AlxGa1-xN/AlN (x = 0, 0.1) Stranski-Krastanov quantum dots for application as the active region of electron-beam pumped ultraviolet lamps. Highly dense (>10e11 cm-2) quantum dot layers are deposited by molecular beam epitaxy, and we explore the effect of the III/V ratio during the growth proce…
▽ More
In this paper, we describe the growth and characterization of 530-nm-thick superlattices (100 periods) of AlxGa1-xN/AlN (x = 0, 0.1) Stranski-Krastanov quantum dots for application as the active region of electron-beam pumped ultraviolet lamps. Highly dense (>10e11 cm-2) quantum dot layers are deposited by molecular beam epitaxy, and we explore the effect of the III/V ratio during the growth process on their optical performance. The study considers structures emitting in the 244-335 nm range at room temperature, with a relative linewidth in the 6-11% range, mainly due to the QD diameter dispersion inherent in self-assembled growth. Under electron pumping, the emission efficiency remains constant for acceleration voltages below 9 kV. The correlation of this threshold with the total thickness of the superlattice and the penetration depth of the electron beam confirms the homogeneity of the nanostructures along the growth axis. Below the threshold, the emission intensity scales linearly with the injected current. The internal quantum efficiency is characterized at low injection, which reveals the material properties in terms of non-radiative processes, and high injection, which emulates carrier injection in operation conditions. In quantum dots synthesized with III/V ratio < 0.75, the internal quantum efficiency remains around 50% from low injection to pumping power densities as high as 200 kW/cm2, being the first kind of nanostructures that present such stable behaviour.
△ Less
Submitted 29 May, 2020;
originally announced May 2020.
-
Optically pumped GeSn micro-disks with 16 % Sn lasing at 3.1 um up to 180K
Authors:
V. Reboud,
A. Gassenq,
N. Pauc,
J. Aubin,
L. Milord,
Q. M. Thai,
M. Bertrand,
K. Guilloy,
D. Rouchon,
J. Rothman,
T. Zabel,
F. Armand Pilon,
H. Sigg,
A. Chelnokov,
J. M. Hartmann,
V. Calvo
Abstract:
Recent demonstrations of optically pumped lasers based on GeSn alloys put forward the prospect of efficient laser sources monolithically integrated on a Si photonic platform. For instance, GeSn layers with 12.5% of Sn were reported to lase at 2.5 um wavelength up to 130 K. In this work, we report a longer emitted wavelength and a significant improvement in lasing temperature. The improvements resu…
▽ More
Recent demonstrations of optically pumped lasers based on GeSn alloys put forward the prospect of efficient laser sources monolithically integrated on a Si photonic platform. For instance, GeSn layers with 12.5% of Sn were reported to lase at 2.5 um wavelength up to 130 K. In this work, we report a longer emitted wavelength and a significant improvement in lasing temperature. The improvements resulted from the use of higher Sn content GeSn layers of optimized crystalline quality, grown on graded Sn content buffers using Reduced Pressure CVD. The fabricated GeSn micro-disks with 13% and 16% of Sn showed lasing operation at 2.6 um and 3.1 um wavelengths, respectively. For the longest wavelength (i.e 3.1 um), lasing was demonstrated up to 180 K, with a threshold of 377 kW/cm2 at 25 K.
△ Less
Submitted 21 April, 2017;
originally announced April 2017.