Ultrafast crystallization and sintering of Li1.5Al0.5Ge1.5(PO4)3 glass and its impact on ion conduction
Authors:
Antonino Curcio,
Antonio Gianfranco Sabato,
Marc Nuñez Eroles,
Juan Carlos GonzalezRosillo,
Alex Morata,
Albert Tarancónb,
Francesco Ciucci
Abstract:
Li1.5Al0.5Ge1.5(PO4)3 (LAGP) is among the most promising solid electrolytes for the next generation all-solid-state lithium batteries. However, preparing LAGP electrolytes is timeand energy-intensive. In this work, LAGP glassy powders were sintered and crystallized in 180 seconds by ultrafast high-temperature sintering (UHS) under conditions attractive for continuous industrial processes (i.e., am…
▽ More
Li1.5Al0.5Ge1.5(PO4)3 (LAGP) is among the most promising solid electrolytes for the next generation all-solid-state lithium batteries. However, preparing LAGP electrolytes is timeand energy-intensive. In this work, LAGP glassy powders were sintered and crystallized in 180 seconds by ultrafast high-temperature sintering (UHS) under conditions attractive for continuous industrial processes (i.e., ambient pressure and atmosphere). The fast heating rates characteristic of UHS significantly delay crystallization, potentially decoupling crystallization and sintering. Furthermore, EIS characterizations reveal that LAGP sintered and crystallized by UHS has an ionic conductivity of 1.15 10-4 S/cm, slightly lower than conventionally annealed samples (1.75 10-4 S/cm). The lower conductivity can be attributed to poorer intergrain contact. To overcome this issue, additives such as B2O3 and Li3BO3 are used, resulting in 2 and 5 times higher grain boundary conductivity for LAGP+1 wt B2O3 and LAGP+1 wt Li3BO3, respectively, compared to LAGP. Overall, this work provides insights into unraveling the impact of UHS sintering on the LAGP Li+ conduction mechanism.
△ Less
Submitted 15 November, 2022;
originally announced November 2022.
Functional thin films as cathode/electrolyte interlayers: a strategy to enhance the performance and durability of solid oxide fuel cells
Authors:
Marina Machado,
Federico Baiutti,
Lucile Bernadet,
Alex Morata,
Marc Nuñez,
Jan Pieter Ouweltjes,
Fabio Coral Fonseca,
Marc Torrell,
Albert Tarancónb
Abstract:
Electrochemical devices such as solid oxide fuel cells (SOFC) may greatly benefit from the implementation of nanoengineered thin-film multifunctional layers providing, alongside enhanced electrochemical activity, improved mechanical, and long-term stability. In this study, an ultrathin (400 nm) bilayer of samarium-doped ceria and a self-assembled nanocomposite made of Sm0.2Ce0.8O1.9-La0.8Sr0.2MnO3…
▽ More
Electrochemical devices such as solid oxide fuel cells (SOFC) may greatly benefit from the implementation of nanoengineered thin-film multifunctional layers providing, alongside enhanced electrochemical activity, improved mechanical, and long-term stability. In this study, an ultrathin (400 nm) bilayer of samarium-doped ceria and a self-assembled nanocomposite made of Sm0.2Ce0.8O1.9-La0.8Sr0.2MnO3-$δ$ was fabricated by pulsed laser deposition and is employed as a functional oxygen electrode in an anode-supported solid oxide fuel cell. Introducing the functional bilayer in the cell architecture results in a simple processing technique for the fabrication of high-performance fuel cells (power density 1.0 W.cm-2 at 0.7 V and 750 $^\circ$C). Durability tests were carried out for up to 1500 h, showing a small degradation under extreme operating conditions of 1 A.cm-2, while a stable behaviour at 0.5 A.cm-2. Post-test analyses, including scanning and transmission electron microscopy and electrochemical impedance spectroscopy, demonstrate that the nanoengineered thin film layers remain mostly morphologically stable after the operation.
△ Less
Submitted 28 September, 2022;
originally announced September 2022.