Effects of Neutron Irradiation on Carbon Doped MgB2 Wire Segments
Authors:
R. H. T. Wilke,
S. L. Bud'ko,
P. C. Canfield,
D. K. Finnemore,
Raymond J. Suplinskas,
J. Farmer,
S. T. Hannahs
Abstract:
We have studied the evolution of superconducting and normal state properties of neutron irradiated Mg(B$_{.962}$C$_{.038}$)$_2$ wire segments as a function of post exposure annealing time and temperature. The initial fluence fully suppressed superconductivity and resulted in an anisotropic expansion of the unit cell. Superconductivity was restored by post-exposure annealing. The upper critical f…
▽ More
We have studied the evolution of superconducting and normal state properties of neutron irradiated Mg(B$_{.962}$C$_{.038}$)$_2$ wire segments as a function of post exposure annealing time and temperature. The initial fluence fully suppressed superconductivity and resulted in an anisotropic expansion of the unit cell. Superconductivity was restored by post-exposure annealing. The upper critical field, H$_{c2}$(T=0), approximately scales with T$_c$ starting with an undamaged T$_c$ near 37 K and H$_{c2}$(T=0) near 32 T. Up to an annealing temperature of 400 $^ o$C the recovery of T$_c$ tends to coincide with a decrease in the normal state resistivity and a systematic recovery of the lattice parameters. Above 400 $^ o$C a decrease in order along the c- direction coincides with an increase in resistivity, but no apparent change in the evolution of T$_c$ and H$_{c2}$. To first order, it appears that carbon doping and neutron damaging effect the superconducting properties of MgB$_2$ independently.
△ Less
Submitted 12 July, 2005;
originally announced July 2005.
-
Superconductivity in MgB_2 doped with Ti and C
Authors:
R. H. T. Wilke,
S. L. Bud'ko,
P. C. Canfield,
M. J. Kramer,
Y. Q. Wu,
D. K. Finnemore,
R. J. Suplinskas,
J. V. Marzik,
S. T. Hannahs
Abstract:
Measurements of the superconducting upper critical field, H_{c2}, and critical current density, J_c, have been carried out for MgB_2 doped with Ti and/or C in order to explore the problems encountered if these dopants are used to enhance the superconducting performance. Carbon replaces boron in the MgB_2 lattice and apparently shortens the electronic mean free path thereby raising H_c2. Titanium…
▽ More
Measurements of the superconducting upper critical field, H_{c2}, and critical current density, J_c, have been carried out for MgB_2 doped with Ti and/or C in order to explore the problems encountered if these dopants are used to enhance the superconducting performance. Carbon replaces boron in the MgB_2 lattice and apparently shortens the electronic mean free path thereby raising H_c2. Titanium forms precipitates of either TiB or TiB_2 that enhance the flux pinning and raise J_c. Most of these precipitates are intra-granular in the MgB_2 phase. If approximately 0.5% Ti and approximately 2% C are co-deposited with B to form doped boron fibers and these fibers are in turn reacted in Mg vapor to form MgB_2, the resulting superconductor has H_{c2}(T=0) ~ 25 T and J_c ~ 10,000 A/cm**2 at 5 K and 2.2 T.
△ Less
Submitted 22 November, 2004;
originally announced November 2004.
-
Systematic effects of carbon doping on the superconducting properties of Mg(B$_{1-x}$C$_x$)$_2$
Authors:
R. H. T. Wilke,
S. L. Bud'ko,
P. C. Canfield,
D. K. Finnemore,
Raymond J. Suplinskas,
S. T. Hannahs
Abstract:
The upper critical field, $H_{c2}$, of Mg(B$_{1-x}$C$_x$)$_2$ has been measured in order to probe the maximum magnetic field range for superconductivity that can be attained by C doping. Carbon doped boron filaments are prepared by CVD techniques, and then these fibers are then exposed to Mg vapor to form the superconducting compound. The transition temperatures are depressed about $1 K/%$ C and…
▽ More
The upper critical field, $H_{c2}$, of Mg(B$_{1-x}$C$_x$)$_2$ has been measured in order to probe the maximum magnetic field range for superconductivity that can be attained by C doping. Carbon doped boron filaments are prepared by CVD techniques, and then these fibers are then exposed to Mg vapor to form the superconducting compound. The transition temperatures are depressed about $1 K/%$ C and $H_{c2}(T=0)$ rises at about $5 T/%$ C. This means that 3.5% C will depress $T_c$ from $39.2 K$ to $36.2 K$ and raise $H_{c2}(T=0)$ from $16.0 T$ to $32.5 T$. Higher fields are probably attainable in the region of 5% C to 7% C. These rises in $H_{c2}$ are accompanied by a rise in resistivity at $40 K$ from about $0.5 μΩcm$ to about $10 μΩcm$. Given that the samples are polycrystalline wire segments, the experimentally determined $H_{c2}(T)$ curves represent the upper $H_{c2}(T)$ manifold associated with $H\perp c$.
△ Less
Submitted 10 December, 2003;
originally announced December 2003.
-
Intra-granular Ti precipitates in MgB2
Authors:
M. J. Kramer,
S. L. Bud'ko,
P. C. Canfield,
R. H. T. Wilke,
D. K. Finnemore,
R. J. Suplinskas
Abstract:
Superconducting magnesium diboride has been prepared with intra-granular TiB precipitates that have appropriate size and spacing for the pinning of superconducting vortices. The TiB particles have a size ranging from 1 nm to 20 nm and a spacing about 5 times as large. By co-depositing Ti and B on a commercial carbon coated silicon carbide substrate with chemical vapor deposition methods, it was…
▽ More
Superconducting magnesium diboride has been prepared with intra-granular TiB precipitates that have appropriate size and spacing for the pinning of superconducting vortices. The TiB particles have a size ranging from 1 nm to 20 nm and a spacing about 5 times as large. By co-depositing Ti and B on a commercial carbon coated silicon carbide substrate with chemical vapor deposition methods, it was possible to obtain a starting fiber with Ti well dispersed in the B. Reacting these fibers in a Mg vapor then transformed the fiber into a superconductor capable of carrying 10,000 A/cm^2 at 25K and 1 T. The Ti-B bonds are strong enough that there is relatively little migration of the Ti as the MgB2 grains form around the TiB precipitates. TiB2 precipitates, if they are present, can not be seen in the selected area diffraction pictures that show the TiB precipitates.
△ Less
Submitted 21 February, 2003;
originally announced February 2003.
-
Titanium additions to MgB2 conductors
Authors:
N. E. Anderson, Jr.,
W. E. Straszheim,
S. L. Bud'ko,
P. C. Canfield,
D. K. Finnemore,
R. J. Suplinskas
Abstract:
A series of doping experiments are reported for MgB2 conductors that have been synthesized using doped boron fibers prepared by chemical vapor deposition(CVD) methods. Undoped MgB2 samples prepared from CVD prepared fibers consistently give critical current densities, Jc, in the range of 500,000 A/cm^2 in low field at 5K. These values fall by a factor of about 100 as the magnetic field increases…
▽ More
A series of doping experiments are reported for MgB2 conductors that have been synthesized using doped boron fibers prepared by chemical vapor deposition(CVD) methods. Undoped MgB2 samples prepared from CVD prepared fibers consistently give critical current densities, Jc, in the range of 500,000 A/cm^2 in low field at 5K. These values fall by a factor of about 100 as the magnetic field increases to 3T. For heavily Ti-doped boron fibers where the B/Ti ratio is comparable to 1, there is a substantial suppression of both Tc, superconducting volume fraction, and Jc values. If, however, a sample with a few percent Ti in B is deposited on a carbon coated SiC substrate and reacted at 1100 degrees C for 15 min, then Tc is suppressed only a couple of degrees Kelvin and critical current densities are found to be approximately 2-5 x 10^6 A/cm^2 for superconducting layers ranging from 4-10 micrometers thick. These materials show Jc values over 10,000 A/cm^2 at 25K and 1.3 T.
△ Less
Submitted 12 February, 2003;
originally announced February 2003.
-
CVD routes to MgB2 conductors
Authors:
D. K. Finnemore,
W. E. Straszheim,
S. L. Bud'ko,
P. C. Canfield,
N. E. Anderson Jr,
R. J. Suplinskas
Abstract:
Processing methods are described for the development of magnesium diboride wire using the chemical vapor deposition (CVD) to produce long lengths of suitably doped starting boron fiber. It is found that titanium can be co-deposited with the boron to make long lengths of doped fiber that contain both TiB and TiB2. When this fiber is reacted in Mg vapor to transform boron into MgB2, the resulting…
▽ More
Processing methods are described for the development of magnesium diboride wire using the chemical vapor deposition (CVD) to produce long lengths of suitably doped starting boron fiber. It is found that titanium can be co-deposited with the boron to make long lengths of doped fiber that contain both TiB and TiB2. When this fiber is reacted in Mg vapor to transform boron into MgB2, the resulting conductor has a superconducting critical current density of about 5 times 10^6 A/cm^2 at 5K and self field. The critical current density at 25K and 1 Tesla is 10,000 A/cm^2. Using optical methods to define grain boundaries and energy dispersive X-rays to determine Ti and Mg concentration, these samples show a fine dispersion of $Ti$ through out the grains and no conspicuous precipitation of TiB2 on the MgB2 grain boundaries. This is to be contrasted with the precipitation of TiB2 on MgB2 grain boundaries observed for samples prepared by solid state reaction of Ti, Mg, and B powders. Introducing Ti impurities into the B during the CVD deposition of the B gives a distribution of TiB2 in the resulting MgB2 different from solid state reaction of powders.
△ Less
Submitted 12 February, 2003;
originally announced February 2003.