RF surface resistance tuning of superconducting niobium via thermal diffusion of native oxide
Authors:
Eric Lechner,
Jonathan Angle,
Fred Stevie,
Michael Kelley,
Charles Reece,
Ari Palczewski
Abstract:
Recently, Nb superconducting radio frequency cavities vacuum heat treated between 300-400 C for a few hours have exhibited very high quality factors (~5x10^10 at 2.0 K). New secondary ion mass spectrometry measurements of O, N and C show this enhancement in RF surface conductivity is primarily associated with interstitial O alloying via dissolution and diffusion of the native oxide. We use a theor…
▽ More
Recently, Nb superconducting radio frequency cavities vacuum heat treated between 300-400 C for a few hours have exhibited very high quality factors (~5x10^10 at 2.0 K). New secondary ion mass spectrometry measurements of O, N and C show this enhancement in RF surface conductivity is primarily associated with interstitial O alloying via dissolution and diffusion of the native oxide. We use a theory of oxide decomposition and O diffusion to quantify previously unknown parameters crucial in modeling this process. RF measurements of a vacuum heat treated Nb superconducting radio frequency cavity confirm the minimized surface resistance (higher Q0) previously expected only from 800 C diffusive alloying with N.
△ Less
Submitted 26 July, 2021; v1 submitted 11 June, 2021;
originally announced June 2021.
Effect of high temperature heat treatments on the quality factor of a large-grain superconducting radio-frequency niobium cavity
Authors:
P. Dhakal,
G. Ciovati,
G. R. Myneni,
K. E. Gray,
N. Groll,
P. Maheshwari,
D. M. McRae,
R. Pike,
T. Proslier,
F. Stevie,
R. P. Walsh,
Q. Yang,
J. Zasadzinzki
Abstract:
Large-grain Nb has become a viable alternative to fine-grain Nb for the fabrication of superconducting radio-frequency cavities. In this contribution we report the results from a heat treatment study of a large-grain 1.5 GHz single-cell cavity made of "medium purity" Nb. The baseline surface preparation prior to heat treatment consisted of standard buffered chemical polishing. The heat treatment i…
▽ More
Large-grain Nb has become a viable alternative to fine-grain Nb for the fabrication of superconducting radio-frequency cavities. In this contribution we report the results from a heat treatment study of a large-grain 1.5 GHz single-cell cavity made of "medium purity" Nb. The baseline surface preparation prior to heat treatment consisted of standard buffered chemical polishing. The heat treatment in the range 800 - 1400 C was done in a newly designed vacuum induction furnace. Q0 values of the order of 2x1010 at 2.0 K and peak surface magnetic field (Bp) of 90 mT were achieved reproducibly. A Q0-value of (5+-1)1010 at 2.0 K and Bp = 90 mT was obtained after heat treatment at 1400 C. This is the highest value ever reported at this temperature, frequency and field. Samples heat treated with the cavity at 1400 C were analyzed by secondary ion mass spectrometry, secondary electron microscopy, energy dispersive X-ray, point contact tunneling and X-ray diffraction and revealed a complex surface composition which includes titanium oxide, increased carbon and nitrogen content but reduced hydrogen concentration compared to a non heat-treated sample.
△ Less
Submitted 25 March, 2013; v1 submitted 25 October, 2012;
originally announced October 2012.