Effect of higher borides and inhomogeneity of oxygen distribution on critical current density of undoped and doped magnesium diboride
Authors:
T. A. Prikhna,
W. Gawalek,
V. M. Tkach,
N. I. Danilenko,
Ya M. Savchuk,
S. N. Dub,
V. E. Moshchil,
A. V. Kozyrev,
N. V. Sergienko,
M. Wendt,
V. S. Melnikov,
J. Dellith,
H Weber,
M Eisterer,
Ch Schmidt,
T Habisreuther,
D Litzkendorf,
J Vajda,
A. P. Shapovalov,
V. Sokolovsky,
P. A. Nagorny,
V. B. Sverdun,
J. Kosa,
F. Karau,
A. V. Starostina
Abstract:
The effect of doping with Ti, Ta, SiC in complex with synthesis temperature on the amount and distribution of structural inhomogeneities in MgB2 matrix of high-pressuresynthesized-materials (2 GPa) which can influence pining: higher borides (MgB12) and oxygen-enriched Mg-B-O inclusions, was established and a mechanism of doping effect on jc increase different from the generally accepted was prop…
▽ More
The effect of doping with Ti, Ta, SiC in complex with synthesis temperature on the amount and distribution of structural inhomogeneities in MgB2 matrix of high-pressuresynthesized-materials (2 GPa) which can influence pining: higher borides (MgB12) and oxygen-enriched Mg-B-O inclusions, was established and a mechanism of doping effect on jc increase different from the generally accepted was proposed. Near theoretically dense SiC-doped material exhibited jc= 1000000 A/sq. cm in 1T field and Hirr =8.5 T at 20 K. The highest jc in fields above 9, 6, and 4 T at 10, 20, and 25 K, respectively, was demonstrated by materials synthesized at 2 GPa, 600 oC from Mg and B without additions (at 20 K jc= 100 A/sq. cm in 10 T field). Materials synthesized from Mg and B taken up to 1:20 ratio were superconductive. The highest jc (60000 A/sq. cm at 20 K in zero field, Hirr= 5 T) and the amount of SC phase (95.3 percents of shielding fraction), Tc being 37 K were demonstrated by materials having near MgB12 composition of the matrix. The materials with MgB12 matrix had a doubled microhardness of that with MgB2 matrix (25 GPa and 13.08 GPa, at a load of 4.9 N, respectively).
△ Less