Higher borides and oxygen-enriched Mg-B-O inclusions as possible pinning centers in nanostructural magnesium diboride and the influence of additives on their formation
Authors:
Tatiana Prikhna,
Wolfgang Gawalek,
Yaroslav Savchuk,
Vasiliy Tkach,
Nikolay Danilenko,
Michael Wendt,
Jan Dellith,
Harold Weber,
Michael Eisterer,
Viktor Moshchil,
Nina Sergienko,
Artem Kozyrev,
Peter Nagorny,
Andrey Shapovalov,
Vladimir Melnikov,
Sergey Dub,
Doris Litzkendorf,
Tobias Habisreuther,
Christa Schmidt,
Athanasios Mamalis,
Vladimir Sokolovsky,
Vladimir Sverdun,
Fridrich Karau,
Alexandra Starostina
Abstract:
The study of high pressure (2 GPa) synthesized MgB2-based materials allows us to conclude that higher borides (with near MgB12 stoichiometry) and oxygen-enriched Mg-B-O inclusions can be pinning centers in nanostructural magnesium diboride matrix (with average grain sizes of 15-37 nm). It has been established that additions of Ti or SiC as well as manufacturing temperature can affect the size, a…
▽ More
The study of high pressure (2 GPa) synthesized MgB2-based materials allows us to conclude that higher borides (with near MgB12 stoichiometry) and oxygen-enriched Mg-B-O inclusions can be pinning centers in nanostructural magnesium diboride matrix (with average grain sizes of 15-37 nm). It has been established that additions of Ti or SiC as well as manufacturing temperature can affect the size, amount and distribution of these inclusions in the material structure and thus, influence critical current density. The superconducting behavior of materials with near MgB12 stoichiometry of matrix is discussed.
△ Less
Submitted 12 January, 2010;
originally announced January 2010.
Effect of higher borides and inhomogeneity of oxygen distribution on critical current density of undoped and doped magnesium diboride
Authors:
T. A. Prikhna,
W. Gawalek,
V. M. Tkach,
N. I. Danilenko,
Ya M. Savchuk,
S. N. Dub,
V. E. Moshchil,
A. V. Kozyrev,
N. V. Sergienko,
M. Wendt,
V. S. Melnikov,
J. Dellith,
H Weber,
M Eisterer,
Ch Schmidt,
T Habisreuther,
D Litzkendorf,
J Vajda,
A. P. Shapovalov,
V. Sokolovsky,
P. A. Nagorny,
V. B. Sverdun,
J. Kosa,
F. Karau,
A. V. Starostina
Abstract:
The effect of doping with Ti, Ta, SiC in complex with synthesis temperature on the amount and distribution of structural inhomogeneities in MgB2 matrix of high-pressuresynthesized-materials (2 GPa) which can influence pining: higher borides (MgB12) and oxygen-enriched Mg-B-O inclusions, was established and a mechanism of doping effect on jc increase different from the generally accepted was prop…
▽ More
The effect of doping with Ti, Ta, SiC in complex with synthesis temperature on the amount and distribution of structural inhomogeneities in MgB2 matrix of high-pressuresynthesized-materials (2 GPa) which can influence pining: higher borides (MgB12) and oxygen-enriched Mg-B-O inclusions, was established and a mechanism of doping effect on jc increase different from the generally accepted was proposed. Near theoretically dense SiC-doped material exhibited jc= 1000000 A/sq. cm in 1T field and Hirr =8.5 T at 20 K. The highest jc in fields above 9, 6, and 4 T at 10, 20, and 25 K, respectively, was demonstrated by materials synthesized at 2 GPa, 600 oC from Mg and B without additions (at 20 K jc= 100 A/sq. cm in 10 T field). Materials synthesized from Mg and B taken up to 1:20 ratio were superconductive. The highest jc (60000 A/sq. cm at 20 K in zero field, Hirr= 5 T) and the amount of SC phase (95.3 percents of shielding fraction), Tc being 37 K were demonstrated by materials having near MgB12 composition of the matrix. The materials with MgB12 matrix had a doubled microhardness of that with MgB2 matrix (25 GPa and 13.08 GPa, at a load of 4.9 N, respectively).
△ Less