Continuous magnetic and structural phase transitions in Fe1+yTe
Authors:
I. A. Zaliznyak,
Z. J. Xu,
J. S. Wen,
J. M. Tranquada,
G. D. Gu,
V. Solovyov,
V. N. Glazkov,
A. I. Zheludev,
V. O. Garlea,
M. B. Stone
Abstract:
We report a sequence of continuous phase transformations in iron telluride, Fe1+yTe (y~0.1), which is observed by combining neutron diffraction, magnetic susceptibility, and specific heat measurements on single crystal samples. While a gradual increase of magnetic scattering near the wave vector (0.5, 0, 0.5) is seen below T = 70 K, a temperature where the discontinuous first order magneto-structu…
▽ More
We report a sequence of continuous phase transformations in iron telluride, Fe1+yTe (y~0.1), which is observed by combining neutron diffraction, magnetic susceptibility, and specific heat measurements on single crystal samples. While a gradual increase of magnetic scattering near the wave vector (0.5, 0, 0.5) is seen below T = 70 K, a temperature where the discontinuous first order magneto-structural phase transition is found in systems with small y (< 0.06), the reduction of the lattice symmetry in Fe1.1Te only occurs at Ts = 63 K. Below TN = 57.5 K the long-range magnetic order develops, whose incommensurate wave vector Qm varies with temperature. Finally, at Tm ~ 45 K the system enters the low-T phase, where Qm is locked at (0.48, 0, 0.5). We conclude that these instabilities are weak compared to the strength of the underlying interactions, and we suggest that the impact of the Fe interstitials on the transitions can be treated with random-field models.
△ Less
Submitted 1 December, 2011; v1 submitted 30 August, 2011;
originally announced August 2011.
-
Iron-chalcogenide FeSe$_{0.5}$Te$_{0.5}$ coated superconducting tapes for high field applications
Authors:
Weidong Si,
Juan Zhou,
Qing Jie,
Ivo Dimitrov,
V. Solovyov,
P. D. Johnson,
J. Jaroszynski,
V. Matias,
C. Sheehan,
Qiang Li
Abstract:
The high upper critical field characteristic of the recently discovered iron-based superconducting chalcogenides opens the possibility of developing a new type of non-oxide high-field superconducting wires. In this work, we utilize a buffered metal template on which we grow a textured FeSe$_{0.5}$Te$_{0.5}$ layer, an approach developed originally for high temperature superconducting coated conduct…
▽ More
The high upper critical field characteristic of the recently discovered iron-based superconducting chalcogenides opens the possibility of developing a new type of non-oxide high-field superconducting wires. In this work, we utilize a buffered metal template on which we grow a textured FeSe$_{0.5}$Te$_{0.5}$ layer, an approach developed originally for high temperature superconducting coated conductors. These tapes carry high critical current densities (>1$\times10^{4}$A/cm$^{2}$) at about 4.2K under magnetic field as high as 25 T, which are nearly isotropic to the field direction. This demonstrates a very promising future for iron chalcogenides for high field applications at liquid helium temperatures. Flux pinning force analysis indicates a point defect pinning mechanism, creating prospects for a straightforward approach to conductor optimization.
△ Less
Submitted 13 June, 2011;
originally announced June 2011.
-
Response of fractal penetration of magnetic flux to disorder landscape in superconducting films
Authors:
Zuxin Ye,
Qiang Li,
W. D. Si,
M. Suenaga,
V. F. Solovyov,
P. D. Johnson
Abstract:
Magnetic flux front and induction contours in superconducting YBa2Cu3O7-d films with defect size s ~ l (superconducting coherence length) and s > l are studied by magneto-optical imaging. Robust self-affine spatial correlation was observed using scaling analysis in the small pinning-dominated (s ~ l) disorderd films. The roughness exponent was determined to be ~ 0.66, independent of numbers of d…
▽ More
Magnetic flux front and induction contours in superconducting YBa2Cu3O7-d films with defect size s ~ l (superconducting coherence length) and s > l are studied by magneto-optical imaging. Robust self-affine spatial correlation was observed using scaling analysis in the small pinning-dominated (s ~ l) disorderd films. The roughness exponent was determined to be ~ 0.66, independent of numbers of defects (or the film thickness). When the disorder landscape also included a distribution of large defects (s >> l), the flux front and induction contours exhibited self-similarity, with a fractal dimension to be ~ 1.33 using the box-counting method. The remarkably different flux penetration patterns were shown to be the manifestation of self-organized criticality at different length scales.
△ Less
Submitted 20 August, 2005;
originally announced August 2005.