Anisotropic thermal expansion and electronic transitions in the Co$_3$BO$_5$ ludwigite
Authors:
Natalia Kazak,
Ana Arauzo,
Juan Bartolome,
Maxim Molokeev,
Vyacheslav Dudnikov,
Leonid Solovyov,
Andrey Borus,
Sergey Ovchinnikov
Abstract:
The investigations of the crystal structure, magnetic and electronic properties of the Co$_3$BO$_5$ at high temperatures were carried out using powder x-ray diffraction, magnetic susceptibility, electrical resistivity, and thermopower measurements. The orthorhombic symmetry (Sp.gr. Pbam) was established at 300 K and no evidence of structural phase transitions was found up to 1000 K. The thermal ex…
▽ More
The investigations of the crystal structure, magnetic and electronic properties of the Co$_3$BO$_5$ at high temperatures were carried out using powder x-ray diffraction, magnetic susceptibility, electrical resistivity, and thermopower measurements. The orthorhombic symmetry (Sp.gr. Pbam) was established at 300 K and no evidence of structural phase transitions was found up to 1000 K. The thermal expansion of the crystal lattice is strongly anisotropic. At $T<T_c=550$ K, a large thermal expansion along the c-axis is observed with simultaneous contraction along a-axis. The activation energy of the conductivity decreases significantly at high temperatures and follows the thermal expansion variation, that exhibits two electronic transitions at ~500 and ~700 K, in coincidence with the anomalies of the heat capacity. Electronic transport was found to be a dominant conduction mechanism in the entire temperature range. The temperature dependence of the effective magnetic moment reflects the evolution of the spin state of Co$^{3+}$ ions towards the spin crossover to a high spin state. The interrelation between the crystal structure and electronic properties is discussed.
△ Less
Submitted 23 December, 2021;
originally announced December 2021.
Effect of Fe-substitution on the structure and magnetism of single crystals Mn2-xFexBO4
Authors:
M. S. Platunov,
N. V. Kazak,
Yu. V. Knyazev,
L. N. Bezmaternykh,
E. M. Moshkina,
A. L. Trigub,
A. A. Veligzhanin,
Y. V. Zubavichus,
L. A. Solovyov,
D. A. Velikanov,
S. G. Ovchinnikov
Abstract:
Single crystalline Mn2-xFexBO4 with x = 0.3, 0.5, 0.7 grown by the flux method have been studied by means of X-ray diffraction and X-ray absorption spectroscopy at both Mn and Fe K edges. The compounds were found to crystallize in an orthorhombic warwickite structure (sp. gr. Pnam). The magnetization data have revealed a spin-glass transition at TSG= 11, 14 and 18 K for x= 0.3, 0.5 and 0.7, respec…
▽ More
Single crystalline Mn2-xFexBO4 with x = 0.3, 0.5, 0.7 grown by the flux method have been studied by means of X-ray diffraction and X-ray absorption spectroscopy at both Mn and Fe K edges. The compounds were found to crystallize in an orthorhombic warwickite structure (sp. gr. Pnam). The magnetization data have revealed a spin-glass transition at TSG= 11, 14 and 18 K for x= 0.3, 0.5 and 0.7, respectively.
△ Less
Submitted 22 June, 2017;
originally announced June 2017.