Low-temperature critical current of Y1-xCaxBa2Cu3O7-delta thin films as a function of hole content and oxygen deficiency
Authors:
S. H. Naqib,
Anita Semwal
Abstract:
The effects of hole content (p) and oxygen deficiency (delta) on the zero-field critical current density, Jc0, were investigated for high-quality c-axis oriented Y1-xCaxBa2Cu3O7-delta (x = 0, 0.05, 0.10, and 0.20) thin films. Ca was used to introduce hole carriers in the CuO2 planes, independent of the oxygen deficiency in the CuO1-delta chains. Low-temperature Jc0(16K) of these films above the…
▽ More
The effects of hole content (p) and oxygen deficiency (delta) on the zero-field critical current density, Jc0, were investigated for high-quality c-axis oriented Y1-xCaxBa2Cu3O7-delta (x = 0, 0.05, 0.10, and 0.20) thin films. Ca was used to introduce hole carriers in the CuO2 planes, independent of the oxygen deficiency in the CuO1-delta chains. Low-temperature Jc0(16K) of these films above the optimum doping were found to be high (> 10^7 Amp/cm^2) and were primarily determined by the hole concentration, reaching a maximum at p ~ 0.185+/-0.005, irrespective of oxygen deficiency. This implies that oxygen disorder plays only a secondary role and the intrinsic Jc0 is mainly governed by the carrier concentration and consequently by the superconducting condensation energy which also peaks at p ~ 0.19 where the pseudogap correlation vanishes.
△ Less
Submitted 11 March, 2005; v1 submitted 9 March, 2005;
originally announced March 2005.
Doping Dependence of the Critical Current and Irreversibility Field in Y1-xCaxBa2Cu3O7-delta
Authors:
Anita Semwal,
N. M. Strickland,
A. Bubendorfer,
S. H. Naqib,
Swee Kuan Goh,
G. V. M. Williams
Abstract:
Critical current measurements were made on thin films of YBa2Cu3O7-delta and Y0.8Ca0.2Ba2Cu3O7-delta produced by sol-gel and pulsed laser deposition, respectively. Both samples have high critical currents at low temperatures and the critical current, Jc, is largest in the overdoped Y0.8Ca0.2Ba2Cu3O7-delta thin film. Annealing studies show a large increase in Jc with increasing hole concentration…
▽ More
Critical current measurements were made on thin films of YBa2Cu3O7-delta and Y0.8Ca0.2Ba2Cu3O7-delta produced by sol-gel and pulsed laser deposition, respectively. Both samples have high critical currents at low temperatures and the critical current, Jc, is largest in the overdoped Y0.8Ca0.2Ba2Cu3O7-delta thin film. Annealing studies show a large increase in Jc with increasing hole concentration and suggests that the maximum Jc should occur for overdoped samples. The very overdoped region of the superconducting phase diagram was probed by studying bulk ceramic Y0.8Ca0.2Ba2Cu3O7-delta samples, where it was found that the irreversibility field systematically increases with increasing hole concentration when scaled by the reduced temperature (t = (1 - T/Tc)).
△ Less
Submitted 12 July, 2004;
originally announced July 2004.