Study of depth profile of hydrogen in hydrogenated diamond like carbon thin film using ion beam analysis techniques
Authors:
J Datta,
H S Biswas,
P Rao,
G L N Reddy,
S Kumar,
N R Ray,
D P Chowdhury,
A V R Reddy
Abstract:
The Hydrogenated Diamond Like Carbon (HDLC) thin films are deposited on Silicon substrate at room temperature using asymmetric capacitively coupled RF plasma with varying flow rates of methane. These films are undergone annealing at high vacuum and high temperature furnace. The as-prepared and annealed HDLC films have been depth profiled for hydrogen using the resonance at 6.44 MeV in nuclear reac…
▽ More
The Hydrogenated Diamond Like Carbon (HDLC) thin films are deposited on Silicon substrate at room temperature using asymmetric capacitively coupled RF plasma with varying flow rates of methane. These films are undergone annealing at high vacuum and high temperature furnace. The as-prepared and annealed HDLC films have been depth profiled for hydrogen using the resonance at 6.44 MeV in nuclear reaction between fluoride ion beam and HDLC. The as prepared films exhibit non-uniform depth distribution of hydrogen: it decreases with depth. Annealing in vacuum brings about a significant desorption of hydrogen from the films. Loss of hydrogen, albeit in much lower proportions, is also induced by the bombarding beam. The films also experience a mild loss of carbon, as shown by proton backscattering spectrometry, during high vacuum annealing. The depth profiles of hydrogen in the annealed films are indicative of the prevalence of graphitic carbon near interface between film and substrate.
△ Less
Submitted 28 November, 2013;
originally announced November 2013.
-
Rietveld refinement and electron density distribution in CuxV2O5
Authors:
R. Nithya,
Sharat Chandra,
G. L. N. Reddy,
H. K. Sahu,
V. Sankara Sastry
Abstract:
Room temperature powder x-ray diffraction measurements have been carried out on polycrystalline samples of CuxV2O5 with x = 0.33, 0.40, 0.50, 0.55 and 0.60, prepared by solid state reaction in evacuated quartz tubes. All the samples were found to be in single-phase monoclinic structure. Rietveld full profile refinement of the x-ray diffraction data yielded the lattice parameters and fractional a…
▽ More
Room temperature powder x-ray diffraction measurements have been carried out on polycrystalline samples of CuxV2O5 with x = 0.33, 0.40, 0.50, 0.55 and 0.60, prepared by solid state reaction in evacuated quartz tubes. All the samples were found to be in single-phase monoclinic structure. Rietveld full profile refinement of the x-ray diffraction data yielded the lattice parameters and fractional atom coordinates. Maximum entropy inversion of the diffraction data was done in order to obtain the variation in the spatial electron density distribution as a function of copper composition. These density maps show progressive positional and charge disorders in the V-O network induced by addition of copper. It is shown that the electrons donated by copper atoms are transferred to the specific vanadium atom sites.
△ Less
Submitted 4 August, 2004;
originally announced August 2004.
-
Systematics in the superconducting and normal state properties in chemically substituted MgB$_{2}$
Authors:
S. Jemima Balaselvi,
A. Bharathi,
V. Sankara Sastry,
G. L. N. Reddy,
Y. Hariharan
Abstract:
The superconducting transition temperature, T$_{C}$, the residual resistivity $ρ_{0}$ and the slope of resistivity curve at high temperature, d$ρ$/dT, have been measured in a series of MgB$_{2}$ samples that have been chemically substituted to varying degree with Li or Cu at the Mg-site and by Li or Cu at the Mg-site along with C substitution at the B-site. DC resistivity and ac susceptibility m…
▽ More
The superconducting transition temperature, T$_{C}$, the residual resistivity $ρ_{0}$ and the slope of resistivity curve at high temperature, d$ρ$/dT, have been measured in a series of MgB$_{2}$ samples that have been chemically substituted to varying degree with Li or Cu at the Mg-site and by Li or Cu at the Mg-site along with C substitution at the B-site. DC resistivity and ac susceptibility measurements were employed to extract the above parameters. T$_{C}$ versus the electron count (estimated from simple chemical valence count arguments) shows a universal behaviour, with T$_{C}$ being constant at the MgB$_{2}$ value for electron counts lower than in MgB$_{2}$ but rapidly decreasing for larger electron counts. The temperature dependence of resistivity in the normal state fits to the Bloch- Gruneisen formula, from which the Debye temperature, $θ_{D}$, and the $ρ_{0}$ are extracted. $θ_{D}$ variation with T$_{C}$ is not systematic, whereas $ρ_{0}$ versus T$_{C}$ shows a systematic variation that depends on the type of the chemical substituent. This dependence has a signature of the nature of the intraband/interband scattering affected by the chemical substitutions. d$ρ$/dT increases with C substitution, but decreases with Li and Cu substitution, implying that C substitution leads to the domination of conductivity by the $σ$ band, while in the Li/Cu substituted samples the $π$ band dominates conduction.
△ Less
Submitted 3 March, 2003;
originally announced March 2003.
-
Effect of electron and hole doping on the superconducting and normal state properties of MgB2
Authors:
S. Jemima Balaselvi,
A. Bharathi,
V. Sankara Sastry,
G. L. N. Reddy,
Y. Hariharan
Abstract:
The variation of TC in MgB2 has been systematically investigated for monovalent cation substitution in Mg1-xLixB2 and in Mg1-xCuxB2 and simultaneous cation and Carbon substitution in Mg0.80Li0.20B2-xCx and Mg0.95Cu0.05B2-xCx using dc resistivity and ac susceptibility techniques. TC seems to be uniquely determined by the electron count in the sample, being constant at the MgB2 value for electron…
▽ More
The variation of TC in MgB2 has been systematically investigated for monovalent cation substitution in Mg1-xLixB2 and in Mg1-xCuxB2 and simultaneous cation and Carbon substitution in Mg0.80Li0.20B2-xCx and Mg0.95Cu0.05B2-xCx using dc resistivity and ac susceptibility techniques. TC seems to be uniquely determined by the electron count in the sample, being constant at the MgB2 value for electron counts lower than MgB2 but rapidly decreasing for larger electron counts. The Debye temperature extracted from fitting normal state resistivity to the Bloch-Gruneisen formula shows no systematics with TC while the residual resistivity versus TC indicates that interband/intraband scattering is affected by the substitutions.
△ Less
Submitted 9 September, 2002;
originally announced September 2002.
-
Synthesis and search for superconductivity in LiBC
Authors:
A. Bharathi,
S. Jemima Balaselvi,
M. Premila,
T. N. Sairam,
G. L. N. Reddy,
C. S. Sundar,
Y. Hariharan
Abstract:
Following the recent theoretical prediction of superconductivity in hole doped LiBC by Rosner et al [1], we have attempted to synthesise Li deficient LixBC (x = 1, 0.8, 0.6 and 0.4) and look for superconductivity in this system. Our synthesis procedure, following the recipe for MgB2, involves reaction of elemental components in a Ta crucible at 900o C under 50 bar of argon pressure. X-ray diffra…
▽ More
Following the recent theoretical prediction of superconductivity in hole doped LiBC by Rosner et al [1], we have attempted to synthesise Li deficient LixBC (x = 1, 0.8, 0.6 and 0.4) and look for superconductivity in this system. Our synthesis procedure, following the recipe for MgB2, involves reaction of elemental components in a Ta crucible at 900o C under 50 bar of argon pressure. X-ray diffraction measurements indicate the formation of P63/mmc structure up to x=0.6. However, no diamagnetic signal or zero resistance, corresponding to the superconducting transition, was observed in the temperature range of 300 to 4 K. This is possibly related to the presence of disorder in the B-C stacking; evidence for which is suggested from a study of the vibrational modes of LixBC through infrared spectroscopy.
△ Less
Submitted 18 July, 2002;
originally announced July 2002.
-
Carbon solubility and superconductivity in MgB2
Authors:
A. Bharathi,
S. Jemima Balaselvi,
S. Kalavathi,
G. L. N. Reddy,
V. Sankara Sastry,
Y. Hariharan,
T. S. Radhakrishnan
Abstract:
Successful replacement of B by C in the series MgB2-xCx for values of x upto 0.3 are reported. Resistivity and ac susceptibility measurements have been carried out in the samples. Solubility of carbon, inferred from the observed change in the lattice parameter with carbon content indicates that carbon substitutes upto x=0.30 into the MgB2 lattice. The superconducting transition temperature, TC m…
▽ More
Successful replacement of B by C in the series MgB2-xCx for values of x upto 0.3 are reported. Resistivity and ac susceptibility measurements have been carried out in the samples. Solubility of carbon, inferred from the observed change in the lattice parameter with carbon content indicates that carbon substitutes upto x=0.30 into the MgB2 lattice. The superconducting transition temperature, TC measured both by zero resistivity and the onset of the diamagnetic signal shows a systematic decrease with increase in carbon content upto x=0.30, beyond which the volume fraction decreases drastically. The temperature dependence of resistivity in the normal state fits to the Bloch-Gruneisen formula for all the carbon compositions studied. The Debye temperatures, extracted from the fit is seen to decrease with carbon content from 900K to 525K, whereas the electron-phonon interaction parameter, obtained from the McMillan equation using the measured TC and the Debye temperature, is seen to increase monotonically from 0.8 in MgB2 to 0.9 in the x=0.50 sample. The ratio of the resistivities between 300K and 40K versus TC is seen to follow the Testardi correlation for the C substituted samples. The decrease in TC is argued to mainly arise due to large decrease in the Debye temperature with C concentration and a decrease in the hole density of states at N(EF).
△ Less
Submitted 2 February, 2002;
originally announced February 2002.
-
Infrared absorption in superconducting MgB2
Authors:
C. S. Sundar,
A. Bharathi,
M. Premila,
T. N. sairam,
S. Kalavathi,
G. L. N. Reddy,
V. S. Sastry,
Y. Hariharan,
T. S. Radhakrishnan
Abstract:
Infrared absorption measurements in the range of 125 to 700 cm^(-1) have been carried out as a function of temperature upto 5 K in MgB2. The absorption spectrum is characterised by a broad band centred at 485 cm^{-1}, with shoulders at 333 and 387 cm^{-1}. Studies on the temperature dependence of absorption, indicate that these modes initially harden with the lowering of temperature, and this tr…
▽ More
Infrared absorption measurements in the range of 125 to 700 cm^(-1) have been carried out as a function of temperature upto 5 K in MgB2. The absorption spectrum is characterised by a broad band centred at 485 cm^{-1}, with shoulders at 333 and 387 cm^{-1}. Studies on the temperature dependence of absorption, indicate that these modes initially harden with the lowering of temperature, and this trend is arrested at ~ 100 K, below which they soften. Further, in the case of the mode at 333 cm^{-1}, there is a distinct softening associated with the superconducting transition at 39 K. The implications of these experimental results in the context of superconductivity in MgB2 are discussed.
△ Less
Submitted 19 April, 2001;
originally announced April 2001.