Ferroelectric switched all-metallic-oxide $p$-$n$ junctions
Authors:
J. Yuan,
H. Wu,
L. Zhao,
K. Jin,
L. X. Cao,
B. Y. Zhu,
S. J. Zhu,
J. P. Zhong,
J. Miao,
H. Yang,
B. Xu,
X. Y. Qi,
Y. Han,
X. G. Qiu,
X. F. Duan,
B. R. Zhao
Abstract:
We report the first formation of the metallic $p$-$n$ junctions, the ferroelectric (Ba,Sr)TiO$_3$ (BST) switched optimally electron-doped ($n$-type) metallic T'-phase superconductor, (La,Ce)$_2$CuO$_4$ (LCCO), and hole-doped ($p$-type) metallic CMR manganite (La,Sr)MnO$_3$ (LSMO) junctions. In contrast with the previous semiconductor $p$-$n$ ($p$-$I$-$n$) junctions which are switched by the buil…
▽ More
We report the first formation of the metallic $p$-$n$ junctions, the ferroelectric (Ba,Sr)TiO$_3$ (BST) switched optimally electron-doped ($n$-type) metallic T'-phase superconductor, (La,Ce)$_2$CuO$_4$ (LCCO), and hole-doped ($p$-type) metallic CMR manganite (La,Sr)MnO$_3$ (LSMO) junctions. In contrast with the previous semiconductor $p$-$n$ ($p$-$I$-$n$) junctions which are switched by the built-in field $V_0$, the present metallic oxides $p$-$I$-$n$ junctions are switched by double barrier fields, the built-in field $V_0$, and the ferroelectric reversed polarized field $V_{rp}$, both take together to lead the junctions to possess definite parameters, such as definite negligible reversed current ($10^{-9}$ A), large breakdown voltage ($>$7 V), and ultrahigh rectification ($>2\times10^4$) in the bias voltage 1.2 V to 2.0 V and temperature range from 5 to over 300 K. The related transport feature, barrier size effect, and temperature effect are also observed and defined.
△ Less
Submitted 19 November, 2006;
originally announced November 2006.
Coexistence of Superconductivity and Ferromagnetism in Dilute Co-doped $La_{1.89} Ce_{0.11} Cu O_{4\pm\d}$ System
Authors:
K. Jin,
J. Yuan,
L. Zhao,
H. Wu,
X. Y. Qi,
B. Y. Zhu,
L. X. Cao,
X. G. Qiu,
B. Xu,
X. F. Duan,
B. R. Zhao
Abstract:
Thin films of the optimally electron-doped $T'$-phase superconductor La$_{1.89}$Ce$_{0.11}$CuO$_{4\pm \d}$ are investigated by dilute Co doping, formed as La$_{1.89}$Ce$_{0.11}$(Cu$_{1-x}$Co$_{x}$)O$_{4\pm\d}$ (LCCCO) with $x$ = 0.01 -- 0.05. The following results are obtained for the first time: for the whole dilute Co doping range, LCCCO thin films show long-range ferromagnetic ordering at the…
▽ More
Thin films of the optimally electron-doped $T'$-phase superconductor La$_{1.89}$Ce$_{0.11}$CuO$_{4\pm \d}$ are investigated by dilute Co doping, formed as La$_{1.89}$Ce$_{0.11}$(Cu$_{1-x}$Co$_{x}$)O$_{4\pm\d}$ (LCCCO) with $x$ = 0.01 -- 0.05. The following results are obtained for the first time: for the whole dilute Co doping range, LCCCO thin films show long-range ferromagnetic ordering at the temperature range from 5 K to 300 K, which is likely due to the RKKY interaction; in the very dilute Co doping, $x$ = 0.01 and 0.02, the superconductivity is maitained, the system shows the coexistence of superconductivity and ferromagnetism in the CuO$_{2}$ plane. This may be based on the nature of the charge carriers in electron-doped high-$T_{c}$ cuprate superconductors.
△ Less
Submitted 15 August, 2006;
originally announced August 2006.