Nanoscale damage during fracture in silica glass

Authors: Daniel Bonamy, Silke Prades, Cindy Rountree, Laurent Ponson, Davy Dalmas, Elisabeth Bouchaud, K. Ravi-Chandar, Claude Guillot

Abstract: We report here atomic force microscopy experiments designed to uncover the nature of failure mechanisms occuring within the process zone at the tip of a crack propagating into a silica glass specimen under stress corrosion. The crack propagates through the growth and coalescence of nanoscale damage spots. This cavitation process is shown to be the key mechanism responsible for damage spreading w… ▽ More We report here atomic force microscopy experiments designed to uncover the nature of failure mechanisms occuring within the process zone at the tip of a crack propagating into a silica glass specimen under stress corrosion. The crack propagates through the growth and coalescence of nanoscale damage spots. This cavitation process is shown to be the key mechanism responsible for damage spreading within the process zone. The possible origin of the nucleation of cavities, as well as the implications on the selection of both the cavity size at coalescence and the process zone extension are finally discussed. △ Less

Submitted 31 August, 2006; originally announced August 2006.

Comments: 12 pages

Journal ref: International Journal of Fracture 140 (2006) 3-13

Scaling exponents for fracture surfaces in homogenous glass and glassy ceramics

Authors: Daniel Bonamy, Laurent Ponson, Silke Prades, Elisabeth Bouchaud, Claude Guillot

Abstract: We investigate the scaling properties of post-mortem fracture surfaces in silica glass and glassy ceramics. In both cases, the 2D height-height correlation function is found to obey Family-Viseck scaling properties, but with two sets of critical exponents, in particular a roughness exponent $ζ\simeq 0.75$ in homogeneous glass and $ζ\simeq 0.4$ in glassy ceramics. The ranges of length-scales over… ▽ More We investigate the scaling properties of post-mortem fracture surfaces in silica glass and glassy ceramics. In both cases, the 2D height-height correlation function is found to obey Family-Viseck scaling properties, but with two sets of critical exponents, in particular a roughness exponent $ζ\simeq 0.75$ in homogeneous glass and $ζ\simeq 0.4$ in glassy ceramics. The ranges of length-scales over which these two scalings are observed are shown to be below and above the size of process zone respectively. A model derived from Linear Elastic Fracture Mechanics (LEFM) in the quasistatic approximation succeeds to reproduce the scaling exponents observed in glassy ceramics. The critical exponents observed in homogeneous glass are conjectured to reflect damage screening occurring for length-scales below the size of the process zone. △ Less

Submitted 8 August, 2006; originally announced August 2006.

Journal ref: Physical Review Letters 97, 135504 (2006)

Crack fronts and damage in glass at the nanometer scale

Authors: C. Marliere, S. Prades, F. Celarie, D. Dalmas, D. Bonamy, C. Guillot, E. Bouchaud

Abstract: We have studied the low speed fracture regime for different glassy materials with variable but controlled length scales of heterogeneity in a carefully mastered surrounding atmosphere. By using optical and atomic force microscopy (AFM) techniques we tracked in real-time the crack tip propagation at the nanometer scale on a wide velocity range (mm/s - pm/s and below). The influence of the heterog… ▽ More We have studied the low speed fracture regime for different glassy materials with variable but controlled length scales of heterogeneity in a carefully mastered surrounding atmosphere. By using optical and atomic force microscopy (AFM) techniques we tracked in real-time the crack tip propagation at the nanometer scale on a wide velocity range (mm/s - pm/s and below). The influence of the heterogeneities on this velocity is presented and discussed. Our experiments reveal also -for the first time- that the crack progresses through nucleation, growth and coalescence of nanometric damage cavities within the amorphous phase. This may explain the large fluctuations observed in the crack tip velocities for the smallest values. This behaviour is very similar to what is involved, at the micrometric scale, in ductile fracture. The only difference is very likely due to the related length scales (nanometric instead of micrometric). Consequences of such a nano-ductile fracture mode observed at a temperature far below the glass transition temperature in glass is finally discussed. △ Less

Submitted 4 September, 2003; v1 submitted 28 February, 2003; originally announced February 2003.

Comments: 12 pages, 8 figures, submitted to Journal of Physics: Condensed Matter; Invited talk at Glass and Optical Materials Division Fall 2002 Meeting, Pittsburgh, Pa, USA

Journal ref: J. of Phys.: Cond. Matter 15 p.S2377 (2003)

Fracture of glassy materials as detected by real-time Atomic Force Microscopy (AFM) experiments

Authors: F. Celarie, S. Prades, D. Bonamy, A. Dickele, L. Ferrero, E. Bouchaud, C. Guillot, C. Marliere

Abstract: We have studied the low speed fracture regime for different glassy materials with variable but controlled length scales of heterogeneity in a carefully mastered surrounding atmosphere. By using optical and atomic force (AFM) microscopy techniques we tracked in real-time the crack tip propagation at the nanometer scale on a wide velocity range (1 mm/s and 0.1 nm/s and below). The influence of the… ▽ More We have studied the low speed fracture regime for different glassy materials with variable but controlled length scales of heterogeneity in a carefully mastered surrounding atmosphere. By using optical and atomic force (AFM) microscopy techniques we tracked in real-time the crack tip propagation at the nanometer scale on a wide velocity range (1 mm/s and 0.1 nm/s and below). The influence of the heterogeneities on this velocity is presented and discussed. Our experiments revealed also -for the first time- that the crack advance proceeds through nucleation, growth and coalescence of nanometric damage cavities inside the amorphous phase, which generate large velocity fluctuations. The implications of the existence of such a nano-ductile fracture mode in glass are discussed. △ Less

Submitted 24 July, 2002; originally announced July 2002.

Comments: 6 pages, 5 figures, submitted to Applied surface Science

Journal ref: Appl. Surf. Sci. 212-213 p.92 (2003)

Glass breaks like metals, but at the nanometer scale

Authors: F. Celarie, S. Prades, D. Bonamy, L. Ferrero, E. Bouchaud, C. Guillot, C. Marliere

Abstract: We report in situ Atomic Force Microscopy experiments which reveal the presence of nanoscale damage cavities ahead of a stress-corrosion crack tip in glass. Their presence might explain the departure from linear elasticity observed in the vicinity of a crack tip in glass. Such a ductile fracture mechanism, widely observed in the case of metallic materials at the micrometer scale, might be also a… ▽ More We report in situ Atomic Force Microscopy experiments which reveal the presence of nanoscale damage cavities ahead of a stress-corrosion crack tip in glass. Their presence might explain the departure from linear elasticity observed in the vicinity of a crack tip in glass. Such a ductile fracture mechanism, widely observed in the case of metallic materials at the micrometer scale, might be also at the origin of the striking similarity of the morphologies of fracture surfaces of glass and metallic alloys at different length scales. △ Less

Submitted 13 January, 2003; v1 submitted 18 July, 2002; originally announced July 2002.

Comments: 4 pages, 4 figures, to appear in Phys. Rev. Lett, few minor corrections, Fig. 1b changed

Journal ref: Phys. Rev. Lett. 90 p.075504 (2003)