Absence of Morphotropic Phase Boundary Effects in BiFeO3-PbTiO3 Thin Films Grown via a Chemical Multilayer Deposition Method
Authors:
Ashish Garg,
Shashaank Gupta,
Shuvrajyoti Bhattacharjee,
Dhananjai Pandey,
Vipul Bansal,
Suresh K Bhargava,
Ju Lin Peng
Abstract:
Here, we report the unusual behaviour shown by the (BiFeO3)1-x-(PbTiO3)x (BF-xPT) films prepared using a multilayer deposition approach by chemical solution deposition method. Thin film samples of various compositions were prepared by depositing several bilayers of BF and PT precursors by varying the BF or PT layer thicknesses. X-ray diffraction showed that final samples of all compositions show m…
▽ More
Here, we report the unusual behaviour shown by the (BiFeO3)1-x-(PbTiO3)x (BF-xPT) films prepared using a multilayer deposition approach by chemical solution deposition method. Thin film samples of various compositions were prepared by depositing several bilayers of BF and PT precursors by varying the BF or PT layer thicknesses. X-ray diffraction showed that final samples of all compositions show mixing of the two compounds resulting in a single phase mixture, also confirmed by transmission electron microscopy. In contrast to bulk equilibrium compositions, our samples show a monoclinic (MA type) structure suggesting disappearance of morphotropic phase boundary (MPB) about x = 0.30 as observed in the bulk. This is accompanied by the lack of any enhancement of remnant polarization at MPB as shown by the ferroelectric measurements. Magnetic measurements show that the magnetization of the samples increases with increasing BF content. Significant magnetization of the samples indicates melting of spin spirals in the BF-xPT arising from random distribution of iron atoms across the film. Absence of Fe2+ ions in the films was corroborated by X-ray photoelectron spectroscopy measurements. The results illustrate that used thin film processing methodology significantly changes the structural evolution in contrast to predictions from the equilibrium phase diagram as well as modify the functional characteristics of BP-xPT system dramatically.
△ Less
Submitted 23 June, 2010;
originally announced June 2010.
-
Magnetoresistance of metallic perovskite oxide LaNiO$_{3-δ}$
Authors:
N. Gayathri,
A. K. Raychaudhuri,
X. Q. Xu,
J. L. Peng,
R. L. Greene
Abstract:
We report a study of the magnetoresistance (MR) of the metallic perovskite oxide LaNiO$_{3-δ}$ as a function of the oxygen stoichiometry $δ$ ($δ\leq$ 0.14), magnetic field (H $\leq 6T$) and temperature (1.5K $\leq $ T $\leq $ 25K). We find a strong dependence of the nature of MR on the oxygen stoichiometry. The MR at low temperatures change from positive to negative as the sample becomes more ox…
▽ More
We report a study of the magnetoresistance (MR) of the metallic perovskite oxide LaNiO$_{3-δ}$ as a function of the oxygen stoichiometry $δ$ ($δ\leq$ 0.14), magnetic field (H $\leq 6T$) and temperature (1.5K $\leq $ T $\leq $ 25K). We find a strong dependence of the nature of MR on the oxygen stoichiometry. The MR at low temperatures change from positive to negative as the sample becomes more oxygen deficient (i.e, $δ$ increases). Some of the samples which are more resistive, show a resistivity minima at $T_{min}$ $\approx$ 20K. We find that in these samples the MR is positive at T > $T_{min}$ and negative for T < $T_{min}$. We conclude that in the absence of strong magnetic interaction, the negative MR in these oxides can arise from weak localisation effects.
△ Less
Submitted 24 July, 1998;
originally announced July 1998.