Superconductivity, pairing symmetry, and disorder in the doped topological insulator Sn$_{1-x}$In$_x$Te for x $\geq$ 0.10
Authors:
M. P. Smylie,
H. Claus,
W. -K. Kwok,
E. R. Louden,
M. R. Eskildsen,
A. S. Sefat,
R. D. Zhong,
J. Schneeloch,
G. D. Gu,
E. Bokari,
P. M. Niraula,
A. Kayani,
C. D. Dewhurst,
A. Snezhko,
U. Welp
Abstract:
The temperature dependence of the London penetration depth $Δλ(T)$ in the superconducting doped topological crystalline insulator Sn$_{1-x}$In$_x$Te was measured down to 450 mK for two different doping levels, x $\approx$ 0.45 (optimally doped) and x $\approx$ 0.10 (underdoped), bookending the range of cubic phase in the compound. The results indicate no deviation from fully gapped BCS-like behavi…
▽ More
The temperature dependence of the London penetration depth $Δλ(T)$ in the superconducting doped topological crystalline insulator Sn$_{1-x}$In$_x$Te was measured down to 450 mK for two different doping levels, x $\approx$ 0.45 (optimally doped) and x $\approx$ 0.10 (underdoped), bookending the range of cubic phase in the compound. The results indicate no deviation from fully gapped BCS-like behavior, eliminating several candidate unconventional gap structures. Critical field values below 1 K and other superconducting parameters are also presented. The introduction of disorder by repeated particle irradiation with 5 MeV protons does not enhance $T_c$, indicating that ferroelectric interactions do not compete with superconductivity.
△ Less
Submitted 27 November, 2017;
originally announced November 2017.
-
Decoupling and tuning competing effects of different types of defects on flux creep in irradiated YBa$_{2}$Cu$_{3}$O$_{7-δ}$ coated conductors
Authors:
S. Eley,
M. Leroux,
M. W. Rupich,
D. J. Miller,
H. Sheng,
P. M. Niraula,
A. Kayani,
U. Welp,
W. -K. Kwok,
L. Civale
Abstract:
YBa$_{2}$Cu$_{3}$O$_{7-δ}$ coated conductors (CCs) have achieved high critical current densities ($\textit{J}_{c}$) that can be further increased through the introduction of additional defects using particle irradiation. However, these gains are accompanied by increases in the flux creep rate, a manifestation of competition between the different types of defects. Here, we study this competition to…
▽ More
YBa$_{2}$Cu$_{3}$O$_{7-δ}$ coated conductors (CCs) have achieved high critical current densities ($\textit{J}_{c}$) that can be further increased through the introduction of additional defects using particle irradiation. However, these gains are accompanied by increases in the flux creep rate, a manifestation of competition between the different types of defects. Here, we study this competition to better understand how to design pinning landscapes that simultaneously increase $\textit{J}_{c}$ and reduce creep. CCs grown by metal organic deposition show non-monotonic changes in the temperature-dependent creep rate, $\textit{S}(\textit{T})$. Notably, in low fields, there is a conspicuous dip to low $\textit{S}$ as temperature ($\textit{T}$) increases from ~20 K to ~65 K. Oxygen-, proton-, and Au-irradiation substantially increase $\textit{S}$ in this temperature range. Focusing on an oxygen-irradiated CC, we investigate the contribution of different types of irradiation-induced defects to the flux creep rate. Specifically, we study $\textit{S}(\textit{T})$ as we tune the relative density of point defects to larger defects by annealing both an as-grown and an irradiated CC in O$_{2}$ at temperatures $\textit{T}_{A}$ = 250$°$C to 600$°$C. We observe a steady decrease in $\textit{S}$($\textit{T}$ > 20 K) with increasing $\textit{T}_{A}$, unveiling the role of pre-existing nanoparticle precipitates in creating the dip in $\textit{S}(\textit{T})$ and point defects and clusters in increasing $\textit{S}$ at intermediate temperatures.
△ Less
Submitted 6 June, 2016; v1 submitted 13 February, 2016;
originally announced February 2016.
-
Rapid Doubling of the Critical Current of YBa$_2$Cu$_3$O$_{7-δ}$ Coated Conductors for Viable High-Speed Industrial Processing
Authors:
Maxime Leroux,
Karen J. Kihlstrom,
Sigrid Holleis,
Martin W. Rupich,
Srivatsan Sathyamurthy,
Steven Fleshler,
Huaping Sheng,
Dean J. Miller,
Serena Eley,
Leonardo Civale,
Asghar Kayani,
Prashantamani M. Niraula,
Ulrich Welp,
Wai-Kwong Kwok
Abstract:
We demonstrate that 3.5-MeV oxygen irradiation can markedly enhance the in-field critical current of commercial 2nd generation superconducting tapes with an exposure time of just one second per 0.8 cm2. The speed demonstrated here is now at the level required for an industrial reel-to-reel post-processing. The irradiation is made on production line samples through the protective silver coating and…
▽ More
We demonstrate that 3.5-MeV oxygen irradiation can markedly enhance the in-field critical current of commercial 2nd generation superconducting tapes with an exposure time of just one second per 0.8 cm2. The speed demonstrated here is now at the level required for an industrial reel-to-reel post-processing. The irradiation is made on production line samples through the protective silver coating and does not require any modification of the growth process. From TEM imaging, we identify small clusters as the main source of increased vortex pinning.
△ Less
Submitted 24 September, 2015;
originally announced September 2015.