Study of the effect of strain rate on the in-plane shear and transverse compression response of a composite ply using computational micromechanics
Authors:
Mario Rueda-Ruiz,
Miguel Herraez,
Federico Sket,
Francisco Galvez,
Carlos Gonzalez,
Jon Mikel Molina-Aldareguia
Abstract:
The use of composite materials for structures subjected to impacts requires a deep understanding about the dynamic behaviour of the material. To this end, a physically-based computational micromechanics simulation tool has been developed to predict failure initiation in a composite ply over a wide range of strain rates. The computational micromechanics framework incorporates constitutive models fo…
▽ More
The use of composite materials for structures subjected to impacts requires a deep understanding about the dynamic behaviour of the material. To this end, a physically-based computational micromechanics simulation tool has been developed to predict failure initiation in a composite ply over a wide range of strain rates. The computational micromechanics framework incorporates constitutive models for the fibre, matrix and fibre-matrix interface, which are partly calibrated with novel micromechanical testing techniques. The simulation tool was applied to two matrix-dominated deformation modes of the ply: transverse compression and in-plane shear. The comparison of simulation and experimental results at coupon level have revealed a change in failure initiation mechanism of the composite ply with strain rate, which was then corroborated through observation of the fracture surfaces on the samples.
△ Less
Submitted 13 February, 2023;
originally announced February 2023.
-
Effect of alloying and microstructure on formability of advanced high-strength steels processed via quenching and partitioning
Authors:
P. Xia,
F. Vercruysse,
C. Celada-Casero,
P. Verleysen,
R. H. Petrov,
I. Sabirov,
J. M. Molina-Aldareguia,
A. Smith,
B. Linke,
R. Thiessen,
D. Frometa,
S. Parareda,
A. Lara
Abstract:
The article focuses on the effect of alloying and microstructure on formability of advanced high strength steels (AHSSs) processed via quenching and partitioning (Q&P). Three different Q&P steels with different combination of alloying elements and volume fraction of retained austenite are subjected to uniaxial tensile and Nakajima testing. Tensile mechanical properties are determined, and the form…
▽ More
The article focuses on the effect of alloying and microstructure on formability of advanced high strength steels (AHSSs) processed via quenching and partitioning (Q&P). Three different Q&P steels with different combination of alloying elements and volume fraction of retained austenite are subjected to uniaxial tensile and Nakajima testing. Tensile mechanical properties are determined, and the forming limit diagrams (FLDs) are plotted. Microstructure of the tested samples is analyzed, and dramatic reduction of retained austenite fraction is detected. It is demonstrated that all steels are able to accumulate much higher amount of plastic strain when tested using Nakajima method. The observed phenomenon is related to the multiaxial stress state and strain gradients through the sheet thickness resulting in a fast transformation of retained austenite, as well as the ability of the tempered martensitic matrix to accumulate plastic strain. Surprisingly, a Q&P steel with the highest volume fraction of retained austenite and highest tensile ductility shows the lowest formability among studied grades. The latter observation is related to the highest sum of fractions of initial fresh martensite and stress/strain induced martensite promoting formation of microcracks. Their role and ability of tempered martensitic matrix to accumulate plastic deformation during forming of Q&P steels is discussed.
△ Less
Submitted 19 October, 2021;
originally announced October 2021.
-
Solid solution and precipitation strengthening effects in basal slip, extension twinning and pyramidal slip in Mg-Zn alloys
Authors:
N. Li,
C. Wang,
M. A. Monclús,
L. Yang,
J. M. Molina-Aldareguia
Abstract:
A high-throughput methodology is proposed, based on the combination of diffusion couples and advanced nanomechanical testing methods, to directly measure alloying effects on the critical resolved shear stress (CRSS) of individual deformation modes in Mg alloys. The methodology is tested in Mg-Zn alloys by assessing the alloying effects, up to Zn contents of 2 at.%, on basal slip, extension twining…
▽ More
A high-throughput methodology is proposed, based on the combination of diffusion couples and advanced nanomechanical testing methods, to directly measure alloying effects on the critical resolved shear stress (CRSS) of individual deformation modes in Mg alloys. The methodology is tested in Mg-Zn alloys by assessing the alloying effects, up to Zn contents of 2 at.%, on basal slip, extension twining and pyramidal slip in two metallurgical condition: as-quenched, for which the Zn solute atoms remain homogenously dispersed in solid solution; and peak-aged, for which the Zn atoms form rod-shape $MgZn_{2}$ precipitates. A combined approach including micromechanical testing, transmission Kikuchi diffraction, and high-resolution transmission electron microscopy was performed to reveal the corresponding deformation mechanisms. It was found that the CRSS enhancement for basal slip and extension twinning by $MgZn_{2}$ precipitates is considerably larger than the effect of Zn in solid solution, while the strengthening of pyramidal slip is similar in both cases. As a result, the anisotropy ratios remain high and similar to pure Mg in the solid solution strengthened Mg-Zn alloys. However, they are substantially reduced in precipitation strengthened Mg-Zn alloys.
△ Less
Submitted 7 October, 2021;
originally announced October 2021.
-
Effect of Al content on the hardness and thermal stability study of AlTiN and AlTiBN coatings deposited by HiPIMS
Authors:
A. Mendez,
M. A. Monclus,
J. A. Santiago,
I. Fernandez-Martinez,
T. C. Rojas,
J. Garcia-Molleja,
M. Avella,
N. Dams,
M. Panizo-Laiz,
J. M. Molina-Aldareguia
Abstract:
The microstructure, mechanical properties and thermal stability of AlTiN and AlTiBN coatings grown by reactive high-power impulse magnetron sputtering (HiPIMS) have been analyzed as a function of Al/(Al+Ti) ratio, x, between 0.5 and 0.8. The coatings were predominantly formed by a face-centered cubic Ti(Al)N crystalline phase, both with and without B, even for x ratios as high as 0.6, which is hig…
▽ More
The microstructure, mechanical properties and thermal stability of AlTiN and AlTiBN coatings grown by reactive high-power impulse magnetron sputtering (HiPIMS) have been analyzed as a function of Al/(Al+Ti) ratio, x, between 0.5 and 0.8. The coatings were predominantly formed by a face-centered cubic Ti(Al)N crystalline phase, both with and without B, even for x ratios as high as 0.6, which is higher than the ratio typically encountered for AlTiN coatings deposited by reactive magnetron sputtering. B doping, in combination with the highly energetic deposition conditions offered by HiPIMS, results in the suppression of the columnar grain morphology typically encountered in AlTiN coatings. On the contrary, the AlTiBN coatings grown by HiPIMS present a dense nanocomposite type microstructure, formed by nanocrystalline Ti(Al)N domains and amorphous regions composed of Ti(Al)B2 and BN. As a result, high-Al content (x>0.6) AlTiBN coatings grown by HiPIMS offer higher hardness, elasticity and fracture toughness than AlTiN coatings. Moreover, the thermal stability and the hot hardness are substantially enhanced, delaying the onset of formation of the detrimental hexagonal AlN phase from 850 C in the case of AlTiN, to 1000 C in the case of AlTiBN.
△ Less
Submitted 16 July, 2021;
originally announced July 2021.
-
High throughput optimization of hard and tough TiN/Ni nanocomposite coatings by reactive magnetron sputter deposition
Authors:
Ignacio Lopez-Cabanas,
Javier LLorca,
Raquel Gonzalez-Arrabal,
Efstathios I. Meletis,
Jon M. Molina-Aldareguia
Abstract:
A combinatorial thin-film synthesis approach combined with a high throughput analysis methodology was successfully applied to synthesize TiN/Ni coatings with optimum mechanical properties. The synthesis approach consists of the deposition of TiN/Ni coatings with the Ni content ranging from around 0 to 20 at.%. by reactive magnetron sputtering with a well-defined composition gradient, so that almos…
▽ More
A combinatorial thin-film synthesis approach combined with a high throughput analysis methodology was successfully applied to synthesize TiN/Ni coatings with optimum mechanical properties. The synthesis approach consists of the deposition of TiN/Ni coatings with the Ni content ranging from around 0 to 20 at.%. by reactive magnetron sputtering with a well-defined composition gradient, so that almost all possible compositions are produced in one single coating under identical conditions, removing uncertainties from processing conditions. The analysis methodology continuously screened the microstructure, residual stresses, hardness and fracture toughness of TiN/Ni coatings. The results show that a nanocomposite microstructure of equiaxed nanograins of crystalline δ-TiN embedded in a Ni rich amorphous phase is formed in the composition window between 8 and 12 Ni at.%. This microstructure offers a superior combination of hardness and toughness and a simultaneous reduction of residual stresses with respect to TiN coatings grown in the same conditions. Higher Ni contents are however detrimental because they compromise the integrity of the coatings.
△ Less
Submitted 20 April, 2021;
originally announced April 2021.
-
A new physical simulation tool to predict the interface of dissimilar aluminum to steel welds performed by Friction Melt Bonding
Authors:
T. Sapanathan,
N. Jimenez-Mena,
I. Sabirov,
M. A. Monclus,
J. M. Molina-Aldareguia,
P. Xia,
L. Zhao,
A. Simar
Abstract:
Optimization of the intermetallic layer thickness and the suppression of interfacial defects are key elements to improve the load bearing capacity of dissimilar joints. However, till date we do not have a systematic tool to investigate the dissimilar joints and the intermetallic properties produced by a welding condition. Friction Melt Bonding (FMB) is a recently developed technique for joining di…
▽ More
Optimization of the intermetallic layer thickness and the suppression of interfacial defects are key elements to improve the load bearing capacity of dissimilar joints. However, till date we do not have a systematic tool to investigate the dissimilar joints and the intermetallic properties produced by a welding condition. Friction Melt Bonding (FMB) is a recently developed technique for joining dissimilar metals that also does not exempt to these challenges. The FMB of DP980 and Al6061-T6 is investigated using a new physical simulation tool, based on Gleeble thermo-mechanical simulator, to understand the effect of individual parameter on the intermetallic formation. The proposed method demonstrates its capability in reproducing the intermetallic characteristics, including the thickness of intermetallic bonding layer, the morphology and texture of its constituents (Fe2Al5 and Fe4Al13), as well as their nanohardness and reduced modulus. The advantages of physical simulation tool can enable novel developing routes for the development of dissimilar metal joining processes and facilitate to reach the requiring load bearing capacity of the joints.
△ Less
Submitted 1 April, 2021;
originally announced April 2021.
-
High temperature in situ SEM assessment followed by ex situ AFM and EBSD investigation of the nucleation and early growth stages of Fe-Al intermetallics
Authors:
T. Sapanathan,
I. Sabirov,
P. Xia,
M. A. Monclus,
J. M. Molina-Aldareguia,
P. J. Jacques,
A. Simar
Abstract:
A dedicated in situ heating setup in a scanning electron microscope (SEM) followed by an ex situ atomic force microscopy (AFM) and electron backscatter diffraction (EBSD) is used to characterize the nucleation and early growth stages of Fe-Al intermetallics (IMs) at 596 °C. A location tracking is used to interpret further characterization. Ex situ AFM observations reveal a slight shrinkage and out…
▽ More
A dedicated in situ heating setup in a scanning electron microscope (SEM) followed by an ex situ atomic force microscopy (AFM) and electron backscatter diffraction (EBSD) is used to characterize the nucleation and early growth stages of Fe-Al intermetallics (IMs) at 596 °C. A location tracking is used to interpret further characterization. Ex situ AFM observations reveal a slight shrinkage and out of plane protrusion of the IM at the onset of IM nucleation followed by directional growth. The formed interfacial IM compounds were identified by ex situ EBSD. It is now clearly demonstrated that the θ-phase nucleates first prior to the diffusion-controlled growth of the η-phase. The θ-phase prevails the intermetallic layer.
△ Less
Submitted 31 March, 2021;
originally announced March 2021.
-
High-throughput nanoindentation mapping of cast IN718 nickel-based superalloys: influence of the Nb concentration
Authors:
Alberto Orozco-Caballero,
Cristina Gutierrez,
Bin Gan,
Jon M. Molina-Aldareguia
Abstract:
A high-throughput correlative study of the local mechanical properties, chemical composition and crystallographic orientation has been carried out in selected areas of cast Inconel 718 specimens subjected to three different tempers. The specimens showed a strong Nb segregation at the scale of the dendrite arms, with local Nb contents that varied between 2 wt.% in the core of the dendrite arms to 8…
▽ More
A high-throughput correlative study of the local mechanical properties, chemical composition and crystallographic orientation has been carried out in selected areas of cast Inconel 718 specimens subjected to three different tempers. The specimens showed a strong Nb segregation at the scale of the dendrite arms, with local Nb contents that varied between 2 wt.% in the core of the dendrite arms to 8 wt.% in the interdendritic regions and 25 wt.% within the second phase particles (MC carbides, Laves phases and δ phase needles). The nanohardness was found to correlate strongly with the local Nb content and the temper condition. On the contrary, the indentation elastic moduli were not influenced by the local chemical composition or temper condition, but directly correlated with the crystallographic grain orientation, due to the high elastic anisotropy of nickel alloys.
△ Less
Submitted 25 February, 2021;
originally announced February 2021.
-
Microstructure, mechanical properties, corrosion resistance and cytocompatibility of WE43 Mg alloy scaffolds fabricated by laser powder bed fusion for biomedical applications
Authors:
M. Li,
F. Benn,
T. Derra,
N. Kroeger,
M. Zinser,
R. Smeets,
J. M. Molina-Aldareguía,
A. Kopp,
J. LLorca
Abstract:
Open-porous scaffolds of WE43 Mg alloy with a body-center cubic cell pattern were manufactured by laser powder bed fusion with different strut diameters. The geometry of the unit cells was adequately reproduced during additive manufacturing and the porosity within the struts was minimized. The microstructure of the scaffolds was modified by means of thermal solution and ageing heat treatments and…
▽ More
Open-porous scaffolds of WE43 Mg alloy with a body-center cubic cell pattern were manufactured by laser powder bed fusion with different strut diameters. The geometry of the unit cells was adequately reproduced during additive manufacturing and the porosity within the struts was minimized. The microstructure of the scaffolds was modified by means of thermal solution and ageing heat treatments and was analysed in detail by means of X-ray microtomography, optical, scanning and transmission electron microscopy. Moreover, the corrosion rates and the mechanical properties of the scaffolds were measured as a function of the strut diameter and metallurgical condition. The microstructure of the as-printed scaffolds contained a mixture of Y-rich oxide particles and Rare Earth-rich intermetallic precipitates. The latter could be modified by heat treatments. The lowest corrosion rates of 2-3 mm/year were found in the as-printed and solution treated scaffolds and they could be reduced to ~0.1 mm/year by surface treatments using plasma electrolytic oxidation. The mechanical properties of the scaffolds improved with the strut diameter: the yield strength increased from 8 to 40 MPa and the elastic modulus improved from 0.2 to 0.8 GPa when the strut diameter increased from 275 μm to 800 μm. Nevertheless, the strength of the scaffolds without plasma electrolytic oxidation treatment decreased rapidly when immersed in simulated body fluid. In vitro biocompatibility tests showed surface treatments by plasma electrolytic oxidation were necessary to ensure cell proliferation in scaffolds with high surface-to-volume ratio.
△ Less
Submitted 8 October, 2020;
originally announced October 2020.
-
Nanomechanical characterization of the fracture toughness of Al/SiC nanolaminates
Authors:
L. W. Yang,
C. R. Mayer,
N. Chawla,
J. LLorca,
J. M. Molina-Aldareguía
Abstract:
The fracture toughness of Al/SiC nanolaminates with different layer thicknesses (in the range 10 to 100 nm) was measured by means of micropillar splitting and bending of a notched beam. The crack plane was perpendicular to the layers in the former while notched beams with the notch parallel and perpendicular to the layers were milled in the latter. It was found that crack propagation parallel to t…
▽ More
The fracture toughness of Al/SiC nanolaminates with different layer thicknesses (in the range 10 to 100 nm) was measured by means of micropillar splitting and bending of a notched beam. The crack plane was perpendicular to the layers in the former while notched beams with the notch parallel and perpendicular to the layers were milled in the latter. It was found that crack propagation parallel to the layers took place along the metal-ceramic interfaces and the toughness increased with the layer thickness due to the contribution of the plastic deformation of the Al layers. Crack propagation perpendicular to the layers showed evidence of crack deflection/arrest at the interface. The toughness in this orientation increased as the layer thickness decreased due to the higher density of interfaces except for the nanolaminates with 10 nm layer thickness. In the latter case, crack propagation took place along the weak columnar grain boundaries, leading to a marked reduction in toughness.
△ Less
Submitted 14 August, 2020;
originally announced August 2020.
-
High temperature strength retention of Cu/Nb nanolaminates through dynamic strain ageing
Authors:
Zhilin Liu,
J. Snel,
T. Boll,
J. -Y. Wang,
M. A. Monclús,
J. M. Molina-Aldareguía,
J. LLorca
Abstract:
The mechanical properties of Cu/Nb metallic nanolaminates with different layer thickness (7, 16, 34 and 63 nm) were studied by means of micropillar compression tests from room temperature to 400 C. Both strain-rate jump and constant strain rate tests were carried out and they showed evidence of dynamic strain ageing in the nanolaminates with 7, 16 and 34 nm layer thickness deformed at 200 C. Dynam…
▽ More
The mechanical properties of Cu/Nb metallic nanolaminates with different layer thickness (7, 16, 34 and 63 nm) were studied by means of micropillar compression tests from room temperature to 400 C. Both strain-rate jump and constant strain rate tests were carried out and they showed evidence of dynamic strain ageing in the nanolaminates with 7, 16 and 34 nm layer thickness deformed at 200 C. Dynamic strain ageing was accompanied by a reduction of the strain rate sensitivity to 0, high strength retention at 200 C and the development of shear localization of the deformation at low strains (5%-6%) that took place along the Nb layers in the nanolaminates. Atom probe tomography of the deformed specimens revealed the presence of O in solid solution in the Nb layers but not in the Cu layers. Thus, diffusion of O atoms to the mobile dislocations in Nb was found to be the origin of the dynamic strain ageing in the Cu/Nb nanolaminates around 200 C. This mechanism was not found at higher temperatures (400 C) because deformation was mainly controlled by stress-assisted diffusion in the Cu layers. This discovery shows a novel strategy to enhance the strength retention at high temperature of metallic nanolaminates through dynamic strain ageing of one the phases.
△ Less
Submitted 14 August, 2020;
originally announced August 2020.
-
High temperature mechanical properties and microstructure of hard TaSiN coatings
Authors:
M. A. Monclús,
L. Yang,
I. López-Cabañas,
M. Castillo-Rodríguez,
A. Zaman,
J. Wang,
E. I. Meletis,
R. González-Arrabal,
J. LLorca,
J. M. Molina-Aldareguía
Abstract:
Room and high temperature mechanical properties of reactive magnetron sputtered TaSiN coatings were measured using nanoindentation (between 25C and 500C). Fracture toughness was also evaluated at a similar temperature range using the micropillar splitting method. The influence of the nitrogen concentration on the evolving phases and microstructure of the TaSiN coatings, before and after the high t…
▽ More
Room and high temperature mechanical properties of reactive magnetron sputtered TaSiN coatings were measured using nanoindentation (between 25C and 500C). Fracture toughness was also evaluated at a similar temperature range using the micropillar splitting method. The influence of the nitrogen concentration on the evolving phases and microstructure of the TaSiN coatings, before and after the high temperature testing, were examined by X-ray diffraction (XRD) and transmission electron microscopy (TEM) analysis. XRD spectra showed broad peaks with hexagonal $γ$-Ta2N as the main phase, with the cubic $δ$-TaN phase emerging for higher N contents. Phase composition remained unchanged before and after the 500C tests. However, after the high temperature tests, TEM analysis showed the presence of an oxide surface layer, with a thickness that decreased (from 42 to 15 nm) with N content, due to residual oxygen diffusion, which replaces nitrogen to form amorphous SiOx. Beneath the oxide-rich surface layer, coatings exhibited a stable nanocrystalline columnar microstructure. Hardness and fracture toughness increased with N content, initially due to the formation of an amorphous Si-N tissue at grain boundaries, and for even higher N contents, due to the appearance of the hard cubic $δ$-TaN phase. Hardness at 500C decreased only by 15%, while fracture toughness followed the opposite trend, due to increased plasticity with temperature. The optimum composition turned out to be Ta55Si10N35, which retained a hardness of 30 GPa at 500C, being also the toughest. These observations make this system very interesting for high temperature applications.
△ Less
Submitted 29 July, 2020;
originally announced July 2020.
-
High strain rate compression of epoxy micro pillars
Authors:
Mario Rueda-Ruiz,
Miguel A. Monclús,
Ben D. Beake,
Francisco Gálvez,
Jon M. Molina-Aldareguia
Abstract:
The study of the high strain rate mechanical behaviour of materials using micropillar compression tests has been hindered so far due to the lack of suitable instrumentation. In the present study, a novel high strain rate micropillar compression set-up is introduced. The high speed tests are carried out with the impact configuration of a pendulum-based nanoindentation device that was instrumented w…
▽ More
The study of the high strain rate mechanical behaviour of materials using micropillar compression tests has been hindered so far due to the lack of suitable instrumentation. In the present study, a novel high strain rate micropillar compression set-up is introduced. The high speed tests are carried out with the impact configuration of a pendulum-based nanoindentation device that was instrumented with force-sensing capability by means of a piezoelectric load cell. This is necessary due to the considerable inertia effects that make the actual applied force on the sample much higher than the actuated one. The proposed novel technique was successfully applied to study the mechanical behaviour of an epoxy resin over a wide range of strain rates. The results reveal a significant strain rate sensitivity that correlates well with that obtained for the same material at the macroscale, validating the novel set-up.
△ Less
Submitted 5 August, 2020; v1 submitted 28 July, 2020;
originally announced July 2020.
-
Effect of Al content on the critical resolved shear stress for twin nucleation and growth in Mg alloys
Authors:
Jingya Wang,
Jon M. Molina-Aldareguía,
Javier LLorca
Abstract:
The effect of Al atoms in solid solution on the critical resolved shear stress for twin nucleation and growth was analyzed by means of the combination of diffusion couples with compression tests in micropillars oriented for twinning. The critical resolved shear stress for twin nucleation was higher than that for twin growth and both increased by the same amount with the Al content. Nevertheless, t…
▽ More
The effect of Al atoms in solid solution on the critical resolved shear stress for twin nucleation and growth was analyzed by means of the combination of diffusion couples with compression tests in micropillars oriented for twinning. The critical resolved shear stress for twin nucleation was higher than that for twin growth and both increased by the same amount with the Al content. Nevertheless, the increase was small ( approx. 10 MPa) for 4 at.%Al but large (up to 60-70 MPa) for 9 at.%Al. These results were in agreement with Labusch-models based on first principles calculations in the dilute regime (< 5 at.%Al) [51]. Comparison with recent data in the literature showed that Al atoms are more effective in increasing the critical resolved shear stresses for twin nucleation and growth than for basal slip [21]. Finally, compression tests in micropillars oriented along [0001] showed the critical shear stress for pyramidal slip increased rapidly with the Al content from 98 MPa in pure Mg to 250 MPa in Mg-9 at.%Al. Thus, the addition of Al increased the plastic anisotropy of Mg alloys.
△ Less
Submitted 2 February, 2020;
originally announced February 2020.
-
Mechanical behavior of InP twinning superlattice nanowires
Authors:
Z. Liu,
I. Papadimitriou,
M. Castillo-Rodríguez,
C. Wang,
G. Esteban-Manzanares,
X. Yuan,
H. H. Tan,
J. M. Molina-Aldareguía,
J. LLorca
Abstract:
Taper-free InP twinning superlattice (TSL) nanowires with an average twin spacing of ~ 13 nm were grown along the zinc-blende close-packed [111] direction using metalorganic vapor phase epitaxy. The mechanical properties and fracture mechanisms of individual InP TSL nanowires in tension were ascertained by means of in situ uniaxial tensile tests in a transmission electron microscope. The elastic m…
▽ More
Taper-free InP twinning superlattice (TSL) nanowires with an average twin spacing of ~ 13 nm were grown along the zinc-blende close-packed [111] direction using metalorganic vapor phase epitaxy. The mechanical properties and fracture mechanisms of individual InP TSL nanowires in tension were ascertained by means of in situ uniaxial tensile tests in a transmission electron microscope. The elastic modulus, failure strain and tensile strength along the [111] direction were determined. No evidence of inelastic deformation mechanisms was found before fracture, which took place in a brittle manner along the twin boundary. The experimental results were supported by molecular dynamics simulations of the tensile deformation of the nanowires that also showed that the fracture of twinned nanowires occurred in the absence of inelastic deformation mechanisms by the propagation of a crack from the nanowire surface along the twin boundary.
△ Less
Submitted 29 August, 2019;
originally announced August 2019.
-
Effect of solute content and temperature on the deformation mechanisms and critical resolved shear stress in Mg-Al and Mg-Zn alloys
Authors:
J-Y. Wang,
N. Li,
R. Alizadeh,
M. A. Monclús,
Y. W. Cui,
J. M. Molina-Aldareguía,
J. LLorca
Abstract:
The influence of solute atoms (Al and Zn) on the deformation mechanisms and the critical resolved shear stress for basal slip in Mg alloys at 298 K and 373 K was ascertained by micropillar compression tests in combination with high-throughput processing techniques based on the diffusion couples. It was found that the presence of solute atoms enhances the size effect at 298 K as well as the localiz…
▽ More
The influence of solute atoms (Al and Zn) on the deformation mechanisms and the critical resolved shear stress for basal slip in Mg alloys at 298 K and 373 K was ascertained by micropillar compression tests in combination with high-throughput processing techniques based on the diffusion couples. It was found that the presence of solute atoms enhances the size effect at 298 K as well as the localization of deformation in slip bands, which is associated with large strain bursts in the resolved shear stress ($τ_{RSS}$)-strain ($ε$) curves. Deformation in pure Mg and Mg alloys was more homogeneous at 373 K and the influence of the micropillar size on the critical resolved shear stress was much smaller. In this latter case, it was possible to determine the effect of solute content on the critical resolved shear stress for basal slip in Mg-Al and Mg-Zn alloys.
△ Less
Submitted 20 March, 2019;
originally announced March 2019.
-
The role of slip transfer at grain boundaries in the propagation of microstructurally short fatigue cracks in Ni-based superalloys
Authors:
M. Jiménez,
W. Ludwig,
D. Gonzalez,
J. M. Molina-Aldareguia
Abstract:
Crack initiation and propagation under high-cycle fatigue conditions have been investigated for a polycrystalline Ni-based superalloy by in-situ synchrotron assisted diffraction and phase contrast tomography. The cracks nucleated along the longest coherent twin boundaries pre-existing on the specimen surface, that were well oriented for slip and that presented a large elastic incompatibility acros…
▽ More
Crack initiation and propagation under high-cycle fatigue conditions have been investigated for a polycrystalline Ni-based superalloy by in-situ synchrotron assisted diffraction and phase contrast tomography. The cracks nucleated along the longest coherent twin boundaries pre-existing on the specimen surface, that were well oriented for slip and that presented a large elastic incompatibility across them. Moreover, the propagation of microstructurally short cracks was found to be determined by the easy slip transfer paths across the pre-existing grain boundaries. This information can only be obtained by characterization techniques like the ones presented here that provide the full set of 3D microstructural information.
△ Less
Submitted 26 November, 2018;
originally announced November 2018.
-
Tensile deformation and fracture mechanisms of Cu/Nb nanolaminates studied by in situ TEM mechanical tests
Authors:
Z. Liu,
M. A. Monclús,
L. W. Yang,
M. Castillo-Rodríguez,
J. M. Molina-Aldareguía,
J. LLorca
Abstract:
The mechanisms of deformation and failure of Cu/Nb nanolaminates manufactured by accumulated roll bonding were analysed using in-situ TEM mechanical tests. Dog-bone small-scale tensile specimens were prepared using a FIB-based technique with the layers parallel and perpendicular to the loading axis. Load, deformation and TEM micrographs were recorded during the in-situ TEM mechanical tests. The sp…
▽ More
The mechanisms of deformation and failure of Cu/Nb nanolaminates manufactured by accumulated roll bonding were analysed using in-situ TEM mechanical tests. Dog-bone small-scale tensile specimens were prepared using a FIB-based technique with the layers parallel and perpendicular to the loading axis. Load, deformation and TEM micrographs were recorded during the in-situ TEM mechanical tests. The specimens deformed parallel to the layers presented very high strain hardening and ductility while those deformed in the perpendicular orientation were more brittle. These results were rationalized in terms of the deformation and fracture mechanisms observed during the tests.
△ Less
Submitted 21 October, 2018;
originally announced October 2018.
-
Influence of temperature on the strain rate sensitivity and deformation mechanisms of nanotwinned Cu
Authors:
L. W. Yang,
C. Y. Wang,
M. A. Monclús,
L. Lu,
J. M. Molina-Aldareguía,
J. LLorca
Abstract:
The mechanical behavior of nanotwinned Cu was studied through indentation creep and constant strain rate indentation tests from 25 $^\circ$C to 200 $^\circ$C. The results showed an enhanced strain rate sensitivity of nanotwinned Cu with temperature, which was higher than that found in coarse-grained Cu. Transmission electron microscopy revealed the same deformation mechanism in the whole temperatu…
▽ More
The mechanical behavior of nanotwinned Cu was studied through indentation creep and constant strain rate indentation tests from 25 $^\circ$C to 200 $^\circ$C. The results showed an enhanced strain rate sensitivity of nanotwinned Cu with temperature, which was higher than that found in coarse-grained Cu. Transmission electron microscopy revealed the same deformation mechanism in the whole temperature range: confined dislocation slip between coherent twin boundaries and formation of dislocation pile-ups at the coherent twin boundaries. The mechanisms responsible for large increase in strain rate sensitivity of nanotwinned Cu with temperature were discussed to the light of experimental observations.
△ Less
Submitted 12 May, 2018;
originally announced May 2018.
-
Deformation mechanism map of Cu/Nb nanoscale metallic multilayers as a function of temperature and layer thickness
Authors:
J. Snel,
M. A. Monclús,
M. Castillo-Rodríguez,
N. Mara,
I. J. Beyerlein,
J. LLorca,
J. M. Molina-Aldareguía
Abstract:
The mechanical properties and deformation mechanisms of Cu/Nb nanoscale metallic multilayers (NMMs) manufactured by accumulative roll bonding (ARB) are studied at 25C and 400C. Cu/Nb NMMs with individual layer thicknesses between 7 and 63 nm were tested by in-situ micropillar compression inside a scanning electron microscope Yield strength, strain-rate sensitivities and activation volumes were obt…
▽ More
The mechanical properties and deformation mechanisms of Cu/Nb nanoscale metallic multilayers (NMMs) manufactured by accumulative roll bonding (ARB) are studied at 25C and 400C. Cu/Nb NMMs with individual layer thicknesses between 7 and 63 nm were tested by in-situ micropillar compression inside a scanning electron microscope Yield strength, strain-rate sensitivities and activation volumes were obtained from the pillar compression tests. The deformed micropillars were examined under scanning and transmission electron microscopy in order to examine the deformation mechanisms active for different layer thicknesses and temperatures. The analysis suggests that room temperature deformation was determined by dislocation glide at larger layer thicknesses and interface-related mechanisms at the thinner layer thicknesses. The high temperature compression tests, in contrast, revealed superior thermo-mechanical stability and strength retention for the NMMs with larger layer thicknesses with deformation controlled by dislocation glide. A remarkable transition in deformation mechanism occurred as the layer thickness decreased, to a deformation response controlled by diffusion processes along the interfaces, which resulted in temperature-induced softening. A deformation mechanism map, in terms of layer thickness and temperature, is proposed from the results obtained in this investigation.
△ Less
Submitted 11 August, 2017;
originally announced August 2017.
-
Effects of layer thickness on the mechanical behavior of oxidation-strengthened Zr/Nb nanoscale multilayers
Authors:
M. A. Monclús,
M. Callisti,
T. Polcar,
L. W. Yang,
J. M. Molina-Aldareguía,
J. LLorca
Abstract:
The mechanical behaviour and deformation mechanisms of magnetron-sputtered Zr/Nb nanoscale multilayers were analysed as a function of the periodicity (L = 10 and 75 nm) and annealing time at 350C (2-336 hrs). The strength of the as-deposited multilayers was independent of the layer thickness and it was controlled by the co-deformation of the Zr and Nb layers. Annealing led to transformation of the…
▽ More
The mechanical behaviour and deformation mechanisms of magnetron-sputtered Zr/Nb nanoscale multilayers were analysed as a function of the periodicity (L = 10 and 75 nm) and annealing time at 350C (2-336 hrs). The strength of the as-deposited multilayers was independent of the layer thickness and it was controlled by the co-deformation of the Zr and Nb layers. Annealing led to transformation of the Zr layers into ZrO2 after a few hours, while the Nb layers oxidised at a much slower rate. The volumetric expansion associated with the oxidation led to the formation of cracks at the interfaces and within the ZrO2 layers for the multilayers with L = 75 nm but not in the case of L = 10 nm. The nanoindentation hardness increased significantly after annealing due to the contribution of the residual stresses associated with the volume increase due to oxidation and to the higher strength of the oxides. The strength increase after annealing, as measured by micropillar compression tests, was smaller than that measured by nanoindentation, as it did not include the contribution of the residual stresses, which were relieved during micropillar fabrication. The nanolaminate with L = 10 nm presented the highest strength and toughness as damage during oxidation was suppressed, and a deformation mechanism controlled by the formation of shear bands.
△ Less
Submitted 10 October, 2017; v1 submitted 13 May, 2017;
originally announced May 2017.
-
Structural composites for multifunctional applications: current challenges and future trends
Authors:
C. González,
J. J. Vilatela,
J. M. Molina-Aldareguía,
C. S. Lopes,
J. LLorca
Abstract:
This review paper summarizes the current state-of-art and challenges for the future developments of fiber-reinforced composites for structural applications with multifunctional capabilities. After a brief analysis of the reasons of the successful incorporation of fiber-reinforced composites in many different industrial sectors, the review analyzes three critical factors that will define the future…
▽ More
This review paper summarizes the current state-of-art and challenges for the future developments of fiber-reinforced composites for structural applications with multifunctional capabilities. After a brief analysis of the reasons of the successful incorporation of fiber-reinforced composites in many different industrial sectors, the review analyzes three critical factors that will define the future of composites. The first one is the application of novel fiber-deposition and preforming techniques together with innovative liquid moulding strategies, which will be combined by optimization tools based on novel multiscale modelling approaches, so fiber-reinforced composites with optimized properties can be designed and manufactured for each application. In addition, composite applications will be enhanced by the incorporation of multifunctional capabilities. Among them, electrical conductivity, energy storage (structural supercapacitors and batteries) and energy harvesting (piezoelectric and solar energy) seem to be the most promising ones.
△ Less
Submitted 10 April, 2017; v1 submitted 29 March, 2017;
originally announced March 2017.
-
Selective oxidation-induced strengthening of Zr/Nb nanoscale multilayers
Authors:
M. A. Monclús,
M. Callisti,
T. Polcar,
L. W. Yang,
J. LLorca,
J. M. Molina-Aldareguía
Abstract:
The paper presents a new approach, based on controlled oxidation of nanoscale metallic multilayers, to produce strong and hard oxide/metal nanocomposite coatings with high strength and good thermal stability. The approach is demonstrated by performing long term annealing on sputtered Zr/Nb nanoscale metallic multilayers and investigating the evolution of their microstructure and mechanical propert…
▽ More
The paper presents a new approach, based on controlled oxidation of nanoscale metallic multilayers, to produce strong and hard oxide/metal nanocomposite coatings with high strength and good thermal stability. The approach is demonstrated by performing long term annealing on sputtered Zr/Nb nanoscale metallic multilayers and investigating the evolution of their microstructure and mechanical properties by combining analytical transmission electron microscopy, nano-mechanical tests and finite element models. As-deposited multilayers were annealed at 350 C in air for times ranging between 1 - 336 hours. The elastic modulus increased by approx. 20% and the hardness by approx. 42% after 15 hours of annealing. Longer annealing times did not lead to changes in hardness, although the elastic modulus increased up to 35% after 336 hrs. The hcp Zr layers were rapidly transformed into monoclinic ZrO2 (in the first 15 hours), while the Nb layers were progressively oxidised, from top surface down towards the substrate, to form an amorphous oxide phase at a much lower rate. The sequential oxidation of Zr and Nb layers was key for the oxidation to take place without rupture of the multi-layered structure and without coating spallation, as the plastic deformation of the metallic Nb layers allowed for the partial relieve of the residual stresses developed as a result of the volumetric expansion of the Zr layers upon oxidation. Moreover, the development of residual stresses induced further changes in mechanical properties in relation to the annealing time, as revealed by finite element simulations.
△ Less
Submitted 22 September, 2016;
originally announced September 2016.
-
A 3D dislocation dynamics analysis of the size effect on the strength of [111] LiF micropillars at 300K and 600K
Authors:
H. -J. Chang,
J. Segurado,
J. M. Molina-Aldareguía,
R. Soler,
J. LLorca
Abstract:
The mechanical behavior in compression of [111] LiF micropillars with diameters in the range 0.5 $μ$m to 2.0 $μ$m was analyzed by means of discrete dislocation dynamics at ambient and elevated temperature. The dislocation velocity was obtained from the Peach-Koehler force acting on the dislocation segments from a thermally-activated model that accounted for the influence of temperature on the latt…
▽ More
The mechanical behavior in compression of [111] LiF micropillars with diameters in the range 0.5 $μ$m to 2.0 $μ$m was analyzed by means of discrete dislocation dynamics at ambient and elevated temperature. The dislocation velocity was obtained from the Peach-Koehler force acting on the dislocation segments from a thermally-activated model that accounted for the influence of temperature on the lattice resistance. A size effect of the type "smaller is stronger" was predicted by the simulations, which was in quantitative agreement with previous experimental results by the authors \cite{SWC14}. The contribution of the different physical deformation mechanisms to the size effect (namely, nucleation of dislocations, dislocation exhaustion and forest hardening) could be ascertained from the simulations and the dominant deformation mode could be assessed as a function of the specimen size and temperature. These results shed light into the complex interaction among size, lattice resistance and dislocation mobility in the mechanical behavior of $μ$m-sized single crystals.
△ Less
Submitted 28 July, 2016;
originally announced July 2016.