Enhancement of Flux Pinning in Neutron Irradiated MgB$_{2}$ Superconductor
Authors:
E. Babic,
Dj. Miljanic,
K. Zadro,
I. Kusevic,
Z. Marohnic,
Dj. Drobac,
X. L. Wang,
S. X. Dou
Abstract:
m-H loops for virgin and neutron irradiated bulk and powder samples of MgB_{2} were measured in the temperature range 5-30 K in magnetic field B<= 1 T. The irradiation at thermal neutron fluences 9*10^{13} and 4.5*10^{14} cm^{-2} caused very small enhancement of m-H loops at lower temperatures (T<20 K), whereas the effect at high temperatures was unclear due to difficulty in achieving exactly th…
▽ More
m-H loops for virgin and neutron irradiated bulk and powder samples of MgB_{2} were measured in the temperature range 5-30 K in magnetic field B<= 1 T. The irradiation at thermal neutron fluences 9*10^{13} and 4.5*10^{14} cm^{-2} caused very small enhancement of m-H loops at lower temperatures (T<20 K), whereas the effect at high temperatures was unclear due to difficulty in achieving exactly the same measurement temperature prior and after irradiation. However, the irradiation at 4.5*10^{15} cm^{-2} produced clear enhancement of m-H loops (hence J_{c}) at all investigated temperatures, which provides the evidence for the enhancement of flux pinning in MgB_{2} due to ion tracks resulting from n+^{10}B reaction. The potential of this technique for the enhancement of flux pinning in high temperature superconductors is briefly discussed.
△ Less
Submitted 10 December, 2001;
originally announced December 2001.