Effect of columnar defects on the pinning properties of NdFeAsO0.85 conglomerate particles
Authors:
J. D. Moore,
L. F. Cohen,
Y. Yeshurun,
A. D. Caplin,
K. Morrison,
K. A. Yates,
C. M. McGilvery,
J. M. Perkins,
D. W. McComb,
C. Trautmann,
Z. A. Ren,
J. Yang,
W. Lu,
X. L. Dong,
Z. X. Zhao
Abstract:
Oxypnictide superconductor NdFeAsO0.85 sample was irradiated with 2 GeV Ta ions at a fluence of 5x10^10 ions/cm2. High resolution transmission electron microscopy study revealed that the irradiation produced columnar-like defects. The effect of these defects on the irreversible magnetisation in polycrystalline randomly oriented fragments was studied as a function of field angle and field sweep r…
▽ More
Oxypnictide superconductor NdFeAsO0.85 sample was irradiated with 2 GeV Ta ions at a fluence of 5x10^10 ions/cm2. High resolution transmission electron microscopy study revealed that the irradiation produced columnar-like defects. The effect of these defects on the irreversible magnetisation in polycrystalline randomly oriented fragments was studied as a function of field angle and field sweep rate. We find that the critical current density is enhanced at fields below the matching field (~1 Tesla) but only marginally. The pinning enhancement is anisotropic and maximum along the defect direction at high temperatures but the pinning then becomes more isotropic at low temperatures. The creep rate is suppressed at high temperatures and at fields below the matching field, indicating the columnar defects are efficient pinning sites at these H and T conditions.
△ Less
Submitted 1 July, 2009;
originally announced July 2009.
Evidence for Supercurrent Connectivity in Conglomerate Particles in NdFeAsO1-d
Authors:
J D Moore,
K Morrison,
K A Yates,
A D Caplin,
Y Yeshurun,
L F Cohen,
J M Perkins,
C M McGilvery,
D W McComb,
Z A Ren,
J Yang,
W Lu,
X L Dong,
Z X Zhao
Abstract:
Here we use global and local magnetometry and Hall probe imaging to investigate the electromagnetic connectivity of the superconducting current path in the oxygen-deficient fluorine-free Nd-based oxypnictides. High resolution transmission electron microscopy and scanning electron microscopy show strongly-layered crystallites, evidence for a ~ 5nm amorphous oxide around individual particles, and…
▽ More
Here we use global and local magnetometry and Hall probe imaging to investigate the electromagnetic connectivity of the superconducting current path in the oxygen-deficient fluorine-free Nd-based oxypnictides. High resolution transmission electron microscopy and scanning electron microscopy show strongly-layered crystallites, evidence for a ~ 5nm amorphous oxide around individual particles, and second phase neodymium oxide which may be responsible for the large paramagnetic background at high field and at high temperatures.
From global magnetometry and electrical transport measurements it is clear that there is a small supercurrent flowing on macroscopic sample dimensions (mm), with a lower bound for the average (over this length scale) critical current density of the order of 103 A/cm2. From magnetometry of powder samples and local Hall probe imaging of a single large conglomerate particle ~120 microns it is clear that on smaller scales, there is better current connectivity with a critical current density of the order of 5 x 104 A/cm2. We find enhanced flux creep around the second peak anomaly in the magnetisation curve and an irreversibility line significantly below Hc2(T) as determined by ac calorimetry.
△ Less
Submitted 4 June, 2008;
originally announced June 2008.