Enhanced superconducting properties of pre-doped B powder type MgB2 strands
Authors:
M. A. Susner,
Y. Yang,
M. D. Sumption,
M. A. Rindfleisch,
M. J. Tomsic,
J. V. Marzik,
E. W. Collings
Abstract:
Conventional doping methods that directly add C or a C-bearing species to Mg+B powder have the disadvantage of adding C inhomogeneously, yielding either under-reacted regions or blocking phases. Pre-doped B powder provides a more homogeneous distribution of the C dopant in MgB2. Powders containing varying amounts of C were used to produce in-situ MgB2 strands which showed high values of transport…
▽ More
Conventional doping methods that directly add C or a C-bearing species to Mg+B powder have the disadvantage of adding C inhomogeneously, yielding either under-reacted regions or blocking phases. Pre-doped B powder provides a more homogeneous distribution of the C dopant in MgB2. Powders containing varying amounts of C were used to produce in-situ MgB2 strands which showed high values of transport Jc (104 A/cm2 at 13.3T). Compared to SiC-added and malic acid-treated strands the pre-doped MgB2 showed both higher values of Birr and transport Jc, indicating that the pre-doping of B leads to more efficient C substitution into the B-sublattice.
△ Less
Submitted 18 August, 2010;
originally announced August 2010.
Superconductivity in MgB_2 doped with Ti and C
Authors:
R. H. T. Wilke,
S. L. Bud'ko,
P. C. Canfield,
M. J. Kramer,
Y. Q. Wu,
D. K. Finnemore,
R. J. Suplinskas,
J. V. Marzik,
S. T. Hannahs
Abstract:
Measurements of the superconducting upper critical field, H_{c2}, and critical current density, J_c, have been carried out for MgB_2 doped with Ti and/or C in order to explore the problems encountered if these dopants are used to enhance the superconducting performance. Carbon replaces boron in the MgB_2 lattice and apparently shortens the electronic mean free path thereby raising H_c2. Titanium…
▽ More
Measurements of the superconducting upper critical field, H_{c2}, and critical current density, J_c, have been carried out for MgB_2 doped with Ti and/or C in order to explore the problems encountered if these dopants are used to enhance the superconducting performance. Carbon replaces boron in the MgB_2 lattice and apparently shortens the electronic mean free path thereby raising H_c2. Titanium forms precipitates of either TiB or TiB_2 that enhance the flux pinning and raise J_c. Most of these precipitates are intra-granular in the MgB_2 phase. If approximately 0.5% Ti and approximately 2% C are co-deposited with B to form doped boron fibers and these fibers are in turn reacted in Mg vapor to form MgB_2, the resulting superconductor has H_{c2}(T=0) ~ 25 T and J_c ~ 10,000 A/cm**2 at 5 K and 2.2 T.
△ Less
Submitted 22 November, 2004;
originally announced November 2004.