Effect of Frustrated Exchange Interactions and Spin-half Impurity on the Electronic Structure of Strongly Correlated NiFe$_{2}$O$_{4}$
Authors:
Kodam Ugendar,
S. Samanta,
Sudhendra Rayaprol,
V. Siruguri,
G. Markandeyulu,
B. R. K. Nanda
Abstract:
Spin-polarized density functional calculations, magnetization, and neutron diffraction measurements are carried out to investigate the magnetic exchange interactions and strong correlation effects in Yb substituted inverse spinel nickel ferrite. In the pristine form, the compound is found to be a mixed insulator under the Zaanen-Sawtazsky-Allen classification scheme as it features both charge tran…
▽ More
Spin-polarized density functional calculations, magnetization, and neutron diffraction measurements are carried out to investigate the magnetic exchange interactions and strong correlation effects in Yb substituted inverse spinel nickel ferrite. In the pristine form, the compound is found to be a mixed insulator under the Zaanen-Sawtazsky-Allen classification scheme as it features both charge transfer and Mott insulator mechanism. Estimation of magnetic exchange couplings reveals that both octahedral-octahedral and octahedral-tetrahedral spin-spin interactions are antiferromagnetic which is typical of a spin-frustrated triangular lattice. However, the latter is dominant compared to the former leading to a forced parallel alignment of the spins at the octahedral site which is in agreement with the results of neutron diffraction measurements. The substituent Yb is found to be settled in +3 charge state, as confirmed from the XPS measurements, to behave like a spin-half impurity carried by the localized $f_{z(x^2-y^2)}$ orbital. The impurity $f$ spin significantly weakens the antiferromagnetic coupling with the spins at the tetrahedral site, which explains the experimental observation of fall in Curie temperature with Yb substitution.
△ Less
Submitted 26 June, 2017; v1 submitted 8 April, 2017;
originally announced April 2017.
-
Room temperature soft ferromagnetism in the nanocrystalline form of YCo2 - a well-known bulk Pauli paramagnet
Authors:
S. Narayana Jammalamadaka,
E. V. Sampathkumaran,
V. Satya Narayana Murthy,
G. Markandeyulu
Abstract:
The Laves phase compound, YCo2, is a well-known exchange-enahnced Pauli paramagnet. We report here that, in the nanocrystalline form, this compound interestingly is an itinerant ferromagnet at room temperature with a low coercive-field. The magnitude of the saturation moment (about 1 Bohr-magneton per formula unit) is large enough to infer that the ferromagnetism is not a surface phenomenon in t…
▽ More
The Laves phase compound, YCo2, is a well-known exchange-enahnced Pauli paramagnet. We report here that, in the nanocrystalline form, this compound interestingly is an itinerant ferromagnet at room temperature with a low coercive-field. The magnitude of the saturation moment (about 1 Bohr-magneton per formula unit) is large enough to infer that the ferromagnetism is not a surface phenomenon in these nanocrystallites. Since these ferromagnetic nanocrystallines are easy to synthesize with a stable form in air, one can explore applications, particularly where hysteresis is a disadvantage.
△ Less
Submitted 12 June, 2008; v1 submitted 11 April, 2008;
originally announced April 2008.
-
Magnetic Properties of Fe75Cu4Ni4Mo2B15 Alloy
Authors:
B. Poornachandra Sekhar,
G. Markandeyulu
Abstract:
The structural and magnetic properties of ball-milled Fe75Cu4Ni4Mo2B15 alloy have been investigated through powder X-ray diffraction studies, magnetization and magnetoimpedance measurements. The particle size decreased rapidly with ball-milling up to 165 hours and then remained as a constant with further hours of milling while, the lattice expanded with milling time up to 165 hours and contracte…
▽ More
The structural and magnetic properties of ball-milled Fe75Cu4Ni4Mo2B15 alloy have been investigated through powder X-ray diffraction studies, magnetization and magnetoimpedance measurements. The particle size decreased rapidly with ball-milling up to 165 hours and then remained as a constant with further hours of milling while, the lattice expanded with milling time up to 165 hours and contracted back with further milling. Saturation magnetization is found to decrease rapidly up to 165 hours of milling and then started decreasing slowly with further milling time. Magnetoimpedance studies were carried out in pellets and thin films of Fe75Cu4Ni4Mo2B15. Magnetoimpedance in pellet is observed to be ~2.5% at 5Hz whereas, in thin films, it is observed to be ~1.5% at 3 MHz.
△ Less