Co-evolution of point defects and Cr-rich nano-phase in binary Fe-20 at.% Cr alloy: A comprehensive investigation using positron annihilation spectroscopy and atom probe tomography
Authors:
Sudip Kumar Sarkar,
Priya Maheshwari,
P. K. Pujari,
Aniruddha Biswas
Abstract:
The role of point defects in temporal evolution of Cr-rich alpha-prime phase separation in binary Fe-20 at.% Cr alloy is elucidated by intercepting the long term (upto 1000 h at 773 K) aging at regular intervals and probing by a combination of atom probe tomography (APT) and positron annihilation spectroscopy (PAS). Since the Cr concentration of nano-scale α/ phase in Fe-20 at.% Cr alloy increases…
▽ More
The role of point defects in temporal evolution of Cr-rich alpha-prime phase separation in binary Fe-20 at.% Cr alloy is elucidated by intercepting the long term (upto 1000 h at 773 K) aging at regular intervals and probing by a combination of atom probe tomography (APT) and positron annihilation spectroscopy (PAS). Since the Cr concentration of nano-scale α/ phase in Fe-20 at.% Cr alloy increases continually on aging, the point defects play active role throughout the aging duration. The near-atomic resolution of APT and self-seeking ability of positrons towards point defects make this analysis possible. The difference of positron affinities between Fe and Cr enables identification of the Cr-rich nano-phases that are specifically associated with defects; they would otherwise be indiscernible in the absence of defect. Thus, the temporal evolution of Cr-rich nano-phase along with the associated point defects can be fully characterized at each stage of aging using APT and PAS, respectively. The combined APT-PAS study shows that Cr-rich alpha-prime precipitation is preceded by vacancy-Cr complexes that act as nucleation sites for Cr clusters, which in turn, cause an early rise in micro-hardness due to cluster hardening. Interestingly, this is accompanied by a significant rise in point defect concentration. Our results depict that the vacancies present in the core of the alpha-prime precipitates migrate towards the precipitates interface during the course of aging and eventually get recovered resulting in virtually defect-free precipitates. This study chronicles the way the point defects shape the process of alpha-prime phase separation throughout the entire length of aging.
△ Less
Submitted 6 May, 2022;
originally announced May 2022.
-
Hikami-Larkin-Nagaoka (HLN) Fitting of Magneto Transport of Bi2Se3 Single Crystal in Different Magnetic Field Ranges
Authors:
Deepak Sharma,
P. Rani,
P. K. Maheshwari,
V. Nagpal,
R. S. Meena,
S. S. Islam,
S. Patnaik,
V. P. S. Awana
Abstract:
We report the detailed study of structural micro-structuraland high magnetic field magneto transport propertiesof Bi2Se3single crystal. Bi2Se3 single crystal is grown through conventional solid-state reaction route via the self-flux method. Rietveld analysis on Powder X-ray Diffraction showed that the studied Bi2Se3 crystal is crystallized in single-phase without any impurity. The surface morpholo…
▽ More
We report the detailed study of structural micro-structuraland high magnetic field magneto transport propertiesof Bi2Se3single crystal. Bi2Se3 single crystal is grown through conventional solid-state reaction route via the self-flux method. Rietveld analysis on Powder X-ray Diffraction showed that the studied Bi2Se3 crystal is crystallized in single-phase without any impurity. The surface morphology analyzed through Scanning Electron Microscopy study which shows that as-grown single crystal exhibit layered type structure and the quantitative weight of the atomic constituents (Bi and Se) are found to be closeto the stoichiometric amount in energy-dispersive X-ray spectroscopy analysis. Low temperature (2.5K) magneto-resistance (MR) exhibited a v-type cusp around origin at lower magnetic field, which is the sign of weak anti-localization effect. Further, Bi2Se3 single crystal magneto conductivity data is fitted by well-known HLN equation in different magnetic field range of 2Tesla, 4Tesla and 6Tesla and the resultant found that the conduction mechanism of Bi2Se3 is dominated by WAL state.
△ Less
Submitted 28 October, 2019;
originally announced October 2019.
-
Detailed physical property characterization of FeTe1-xSex x = 0.0 to 0.50 single crystals
Authors:
P. K. Maheshwari,
V. Raghavendra Reddy,
Bhasker Gahtori,
V. P. S. Awana
Abstract:
Here, we report self flux single crystal growth of FeTe1-xSex for x = 0 to 0.50 series via solid state reaction route,the resulted crystals as seen are shiny. X Ray diffraction performed on the surface of crystals elucidated the growth in 00l plane, i.e. orientation in c direction only. Scanning electron microscopy (SEM) images showed slab like morphology and EDX (Energy dispersive X ray analyzer)…
▽ More
Here, we report self flux single crystal growth of FeTe1-xSex for x = 0 to 0.50 series via solid state reaction route,the resulted crystals as seen are shiny. X Ray diffraction performed on the surface of crystals elucidated the growth in 00l plane, i.e. orientation in c direction only. Scanning electron microscopy (SEM) images showed slab like morphology and EDX (Energy dispersive X ray analyzer) confirmed that the crystals are closed to their designed compositions. Rietveld analysis of the XRD patterns of crushed crystal powders showed that the cell parameters decrease with Se content increase. Coupled magnetic and structural phase transition temperature, seen as a step in resistivity for the lower Se concentration and it is not detected for higher x values. Superconductivity is observed by resistivity measurement for higher Se concentration with a maximum temperature of 14K at x = 0.50. Thermally Activated Flux Flow (TAFF) analysis based on high field transport measurements in superconducting region done for x = 0.20 crystal. Raman spectroscopy at room temperature of synthesized samples exhibits all the allowed phonon modes with slight shift to higher frequency with Se content. Mossbauer spectra of FeTe1-xSex crystals series were recorded at 300 and 5K. At 5K, the average hyperfine field decreases systematically with Se content increase from 10.6 to 6.1Tesla for x = 0.0 to x = 0.20 samples. This indicates a possibility of co-existing magnetism and superconductivity in x = 0.07 to 0.20 crystals. For x = 0.50 sample, no hyperfine field related to magnetic ordering is seen. Based on above results, detailed phase diagram of the FeTe1-xSex compounds is defined in the present study.
△ Less
Submitted 14 January, 2019;
originally announced January 2019.
-
Heat capacity and Mosssbauer study of Self flux grown FeTe Single Crystal
Authors:
P. K Maheshwari,
V. Raghavendra Reddy,
V. P. S. Awana
Abstract:
We report mainly the heat capacity and Mossbauer study of self flux grown FeTe single crystal, which is ground state compound of the Fe chalcogenides superconducting series, i.e., FeTe1-x(Se/S)x. The as grown FeTe single crystal is large enough to the tune of few cm and the same crystallizes in tetragonal structure having space group of P4/nmm. FeTe shows the structural/magnetic phase transition a…
▽ More
We report mainly the heat capacity and Mossbauer study of self flux grown FeTe single crystal, which is ground state compound of the Fe chalcogenides superconducting series, i.e., FeTe1-x(Se/S)x. The as grown FeTe single crystal is large enough to the tune of few cm and the same crystallizes in tetragonal structure having space group of P4/nmm. FeTe shows the structural/magnetic phase transition at 70K in both magnetic and resistivity measurements. Heat capacity measurement also confirms the coupled structural/magnetic transition at the same temperature. The Debye model fitting of low temperature (below 70K) heat capacity exhibited Debye temperature to be 324K. MÖssbauer spectra are performed at 300K and 5K. The 300K spectra showed two paramagnetic doublets and the 5K spectra exhibited hyperfine magnetic sextet with an average hyperfine field of 10.6Tesla matching with the results of Yoshikazu Mizuguchi et al.
△ Less
Submitted 30 May, 2018; v1 submitted 13 March, 2018;
originally announced March 2018.
-
High Field (up to 140kOe) Angle Dependent Magneto Transport of Bi2Te3 Single Crystals
Authors:
Rabia Sultana,
P. K. Maheshwari,
Brajesh Tiwari,
V. P. S. Awana
Abstract:
We report the angle dependent high field (up to 140kOe) magneto transport of Bi2Te3 single crystals, a well-known topological insulator. The crystals were grown from melt of constituent elements via solid state reaction route by self-flux method. Details of crystal growth along with their brief characterization up to 5 Tesla applied field was reported by some of us recently [J. Magn. Mag. Mater. 4…
▽ More
We report the angle dependent high field (up to 140kOe) magneto transport of Bi2Te3 single crystals, a well-known topological insulator. The crystals were grown from melt of constituent elements via solid state reaction route by self-flux method. Details of crystal growth along with their brief characterization up to 5 Tesla applied field was reported by some of us recently [J. Magn. Mag. Mater. 428, 213 (2017)]. The angle dependence of the magneto-resistance (MR) of Bi2Te3 follows the cos Theta function i.e., MR is responsive, when the applied field is perpendicular (tilt angle Theta = o and/or 180) to the transport current. The low field (10 kOe) MR showed the signatures of weak anti localization (WAL) character with typical cusp near origin at 5 K. Further, the MR is linear right up to highest applied field of 140 kOe. The large positive MR are observed up to high temperatures and are above 250 and 150 percent at 140 kOe in perpendicular fields at 50 K and 100 K respectively. Heat capacity CP(T) measurements revealed the value of Debye temperature to be 135 K. ARPES (angle resolved photoemission spectroscopy) data clearly showed that the bulk Bi2Te3 single crystal consists of a single Dirac cone.
△ Less
Submitted 13 December, 2017;
originally announced December 2017.
-
Novel solid state vacuum quartz encapsulated growth of p-Terphenyl: the parent High Tc Oraganic Superconductor (HTOS)
Authors:
P. K. Maheshwari,
R. S. Meena,
Bhasker Gahtori,
Reena Goyal,
Rabia Sultana,
Poonam Rani,
V. P. S. Awana
Abstract:
We report an easy and versatile route for the synthesis of the parent phase of newest superconducting wonder material i.e. p-Terphenyl. Doped p-terphenyl has recently shown superconductivity with transition temperature as high as 120K. For crystal growth, the commercially available p-Terphenyl powder is pelletized, encapsulated in evacuated (10-4 Torr) quartz tube and subjected to high temperature…
▽ More
We report an easy and versatile route for the synthesis of the parent phase of newest superconducting wonder material i.e. p-Terphenyl. Doped p-terphenyl has recently shown superconductivity with transition temperature as high as 120K. For crystal growth, the commercially available p-Terphenyl powder is pelletized, encapsulated in evacuated (10-4 Torr) quartz tube and subjected to high temperature (260C) melt followed by slow cooling at 5C/hour. Simple temperature controlled heating furnace is used during the process. The obtained crystal is one piece, shiny and plate like. Single crystal surface XRD (X-ray Diffraction) showed unidirectional (00l) lines, indicating that the crystal is grown along c-direction. Powder XRD of the specimen showed that as grown p-Terphenyl is crystallized in monoclinic structure with space group P21/a space group, having lattice parameters a = 8.08(2) A, b = 5.62(5) A and c= 13.58(3) A. Scanning electron microscopy (SEM) pictures of the crystal showed clear layered slab like growth without any visible contamination from oxygen. Characteristic reported Raman active modes related to C-C-C bending, C-H bending, C-C stretching and C-H stretching vibrations are seen clearly for the studied p-Terphenyl crystal. The physical properties of crystal are yet underway. The short letter reports an easy and versatile crystal growth method for obtaining quality p-terphenyl. The same growth method may probably be applied to doped p-terphenyl and to subsequently achieve superconductivity to the tune of as high 120K for the newest superconductivity wonder i.e., High Tc Oraganic Superconductor (HTOS).
△ Less
Submitted 8 June, 2017; v1 submitted 6 June, 2017;
originally announced June 2017.
-
Electrical, Thermal and Spectroscopic Characterization of Bulk Bi2Se3 Topological Insulator
Authors:
Rabia Sultana,
Geet Awana,
Banabir Pal,
P. K. Maheshwari,
Monu Mishra,
Govind Gupta,
Anurag Gupta,
S. Thirupathaiah,
V. P. S. Awana
Abstract:
We report electrical (angular magneto-resistance, and Hall), thermal (heat capacity) and spectroscopic (Raman, x-ray photo electron, angle resolved photo electron) characterization of bulk Bi2Se3 topological insulator, which is being is grown by self flux method through solid state reaction from high temperature (950C) melt and slow cooling (2C/hour) of constituent elements. Bi2Se3 exhibited metal…
▽ More
We report electrical (angular magneto-resistance, and Hall), thermal (heat capacity) and spectroscopic (Raman, x-ray photo electron, angle resolved photo electron) characterization of bulk Bi2Se3 topological insulator, which is being is grown by self flux method through solid state reaction from high temperature (950C) melt and slow cooling (2C/hour) of constituent elements. Bi2Se3 exhibited metallic behaviour down to 5K. Magneto transport measurements revealed linear up to 400% and 30% MR at 5K under 14 Tesla field in perpendicular and parallel field direction respectively. We noticed that the magneto-resistance (MR) of Bi2Se3 is very sensitive to the angle of applied field. MR is maximum when the field is normal to the sample surface, while it is minimum when the field is parallel. Hall coefficient (RH) is seen nearly invariant with negative carrier sign down to 5K albeit having near periodic oscillations above 100K. Heat capacity (Cp) versus temperature plot is seen without any phase transitions down to 5K and is well fitted (Cp = gammaT + betaT3) at low temperature with calculated Debye temperature (ThetaD) value of 105.5K. Clear Raman peaks are seen at 72, 131 and 177 cm-1 corresponding to A1g1, Eg2 and A1g2 respectively. Though, two distinct asymmetric characteristic peak shapes are seen for Bi 4f7/2 and Bi 4f5/2, the Se 3d region is found to be broad displaying the overlapping of spin - orbit components of the same. Angle-resolved photoemission spectroscopy (ARPES) data of Bi2Se3 revealed distinctly the bulk conduction bands (BCB), surface state (SS), Dirac point (DP) and bulk valence bands (BVB) and 3D bulk conduction signatures are clearly seen. Summarily, host of physical properties for as grown Bi2Se3 crystal are reported here.
△ Less
Submitted 18 March, 2017; v1 submitted 16 March, 2017;
originally announced March 2017.
-
Crystal Growth and Magneto-transport of Bi2Se3 Single crystals
Authors:
Geet Awana,
Rabia Sultana,
P. K. Maheshwari,
Reena Goyal,
Bhasker Gahtori,
Anurag Gupta,
V. P. S. Awana
Abstract:
In this letter, we report growth and characterization of bulk Bi2Se3 single crystals. The studied Bi2Se3 crystals are grown by self flux method through solid state reaction from high temperature (950C) melt of constituent elements and slow cooling (2C/hour). The resultant crystals are shiny and grown in [00l] direction, as evidenced from surface XRD. Detailed Reitveld analysis of PXRD (powder x-ra…
▽ More
In this letter, we report growth and characterization of bulk Bi2Se3 single crystals. The studied Bi2Se3 crystals are grown by self flux method through solid state reaction from high temperature (950C) melt of constituent elements and slow cooling (2C/hour). The resultant crystals are shiny and grown in [00l] direction, as evidenced from surface XRD. Detailed Reitveld analysis of PXRD (powder x-ray diffraction) of the crystals showed that these are crystallized in rhombohedral crystal structure with space group of R3m (D5) and the lattice parameters are a = 4.14(2)A, b = 4.14 (2) A and c = 28.7010(7) A. Temperature versus resistivity (R-T) plots revealed metallic conduction down to 2K, with typical room temperature resistivity (R300K) of around 0.53 mohm-cm and residual resistivity of 0.12 mohm-cm. Resistivity under magnetic field ] measurements exhibited large +Ve magneto resistance right from 2K to 200K. Isothermal magneto resistance [RH] measurements at 2K, 100K and 200K exhibited magneto resistance (MR) of up to 240, 130 and 60 percent respectively at 14 Tesla. Further the MR plots are non saturating and linear with field at all temperature. At 2K the MR plots showed clear quantum oscillations at above say 10 Tesla applied field. Also the Kohler plots i.e., were seen consolidating on one plot. Interestingly, the studied Bi2Se3 single crystal exhibited the Shubnikov-de Haas oscillations (SdH) at 2K under different applied magnetic fields ranging from 4Tesla to 14 Tesla
△ Less
Submitted 18 March, 2017; v1 submitted 23 January, 2017;
originally announced January 2017.
-
Impact of Fe site Co substitution on superconductivity of Fe1-xCoxSe0.5Te0.5 (x = 0.0 to 0.10): A flux free single crystal study
Authors:
P. K. Maheshwari,
Bhasker Gahtori,
Anurag Gupta,
V. P. S. Awana
Abstract:
We report synthesis of Co substitution at Fe site in Fe1-xCoxSe0.5Te0.5 (x=0.0 to 0.10) single crystals via vacuum shield solid state reaction route using flux free method. Single crystal XRD results showed that these crystals grow in (00l) plane i.e., orientation in c-direction. All the crystals possess tetragonal structure having P4/nmm space group. Detailed scanning electron microscopy (SEM) im…
▽ More
We report synthesis of Co substitution at Fe site in Fe1-xCoxSe0.5Te0.5 (x=0.0 to 0.10) single crystals via vacuum shield solid state reaction route using flux free method. Single crystal XRD results showed that these crystals grow in (00l) plane i.e., orientation in c-direction. All the crystals possess tetragonal structure having P4/nmm space group. Detailed scanning electron microscopy (SEM) images show that the crystals are grown in slab-like morphology. The EDAX results revealed the final elemental composition to be near stoichiometric. Powder X-Ray diffraction (PXRD) Rietveld analysis results show that (00l) peaks are shifted towards higher angle with increasing Co concentration. Both a and c lattice parameters decrease with increasing Co concentration in Fe1-xCoxSe0.5Te0.5 (x=0.0 to 0.10) single crystals. Low temperature transport and magnetic measurements show that the superconducting transition temperature (Tc), decreases from around 12K to 10K and 4K for x=0.03 and x=0.05 respectively. For x=0.10 crystal superconductivity is not observed down to 2K.
△ Less
Submitted 23 January, 2017; v1 submitted 25 October, 2016;
originally announced October 2016.
-
Flux free growth of superconducting FeSe single crystals
Authors:
P. K. Maheshwari,
L. M. Joshi,
Bhasker Gahtori,
A. K. Srivastava,
Anurag Gupta,
S. P. Patnaik,
V. P. S. Awana
Abstract:
We report flux free growth of superconducting FeSe single crystals by an easy and versatile high temperature melt and slow cooling method for first time. The room temperature XRD on the surface of the piece of such obtained crystals showed single 101 plane of Beta-FeSe tetragonal phase. The bulk powder XRD, being obtained by crushing the part of crystal chunk showed majority tetragonal and minorit…
▽ More
We report flux free growth of superconducting FeSe single crystals by an easy and versatile high temperature melt and slow cooling method for first time. The room temperature XRD on the surface of the piece of such obtained crystals showed single 101 plane of Beta-FeSe tetragonal phase. The bulk powder XRD, being obtained by crushing the part of crystal chunk showed majority tetragonal and minority FeSe hexagonal crystalline phases. Detailed HRTEM images along with SAED (selected area electron diffraction) showed the abundance of both majority and minority FeSe phases. Both transport (RT) and magnetization (MT) exhibited superconductivity at below around 10K. Interestingly, the magnetization signal of these crystals is dominated by the magnetism of minority magnetic phase, and hence the isothermal magnetization (MH) at 4K was seen to be ferromagnetic (FM) like. Transport (R-T) measurements under magnetic field showed superconductivity onset at below 12K, and R = 0 (Tc) at 9K. Superconducting transition temperature (Tc) decreases with applied field to around 6K at 7Tesla, with dTc/dH of 0.4K/Tesla, giving rise to an Hc2 value of around 50 Tesla, 30 Tesla and 20 Tesla for Rn = 90, 50 and 10 percent respectively. FeSe single crystal activation energy is calculated from Thermally Activated Flux Flow (TAFF) model which is found to decreases with field.
△ Less
Submitted 23 January, 2017; v1 submitted 27 June, 2016;
originally announced June 2016.
-
Fast suppression of superconductivity with Fe site Ni substitution in Fe1-xNixSe0.5Te0.5 (x=0.0, 0.01, 0.03, 0.05, 0.07, 0.10 and 0.20) single crystals
Authors:
P. K. Maheshwari,
Bhasker Gahtori,
V. P. S. Awana
Abstract:
We report the effect of Ni doping on superconductivity of FeSe0.5Te0.5. The single crystal samples of series Fe1-xNixSe0.5Te0.5 (x=0.0, 0.01, 0.03, 0.05, 0.07, 0.10 and 0.20) are synthesized via vacuum shield solid state reaction route and high temperature heating followed by slow cooling. All the crystals of Fe1-xNixSe0.5Te0.5 series with x up to 0.20, i.e., 20% substitution of Ni at Fe site are…
▽ More
We report the effect of Ni doping on superconductivity of FeSe0.5Te0.5. The single crystal samples of series Fe1-xNixSe0.5Te0.5 (x=0.0, 0.01, 0.03, 0.05, 0.07, 0.10 and 0.20) are synthesized via vacuum shield solid state reaction route and high temperature heating followed by slow cooling. All the crystals of Fe1-xNixSe0.5Te0.5 series with x up to 0.20, i.e., 20% substitution of Ni at Fe site are crystallized in single phase tetragonal structure with space group P4/nmm. The electrical resistivity measurements revealed that Tc decreases fast with increase of Ni concentration in Fe1-xNixSe0.5Te0.5. Namely the superconducting transition temperature (Tc) being defined as resistivity =0 decrease from 12K to around 4K and 2K for x=0.01 and 0.03 samples respectively. For x=0.05 (5at% Ni at Fe site) though Tconset is observed in resistivity measurements but \r{ho}=0 is not seen down to 2K. For x more than 0.07, neither the Tconset nor Tc\r{ho}=0 is seen down 2K in R-T measurements. It is demonstrated that Ni doping at Fe site in FeSe0.5Te0.5 superconductor suppresses superconductivity fast. The rate of Tc depression is albeit non monotonic. Summarily, a systematic study on suppression of superconductivity with Fe site Ni doping in flux free gown FeSe0.5Te0.5 single crystals is presented in the current communication.
△ Less
Submitted 23 January, 2017; v1 submitted 26 May, 2016;
originally announced May 2016.
-
Effect of impurity substitution on band structure and mass renormalization of the correlated FeTe$_{0.5}$Se$_{0.5}$ superconductor
Authors:
S. Thirupathaiah,
J. Fink,
P. K. Maheshwari,
V. V. Ravi Kishore,
Z. -H. Liu,
E. D. L. Rienks,
B. Büchner,
V. P. S. Awana,
D. D. Sarma
Abstract:
Using angle-resolved photoemission spectroscopy (ARPES), we studied the effect of the impurity potential on the electronic structure of FeTe$_{0.5}$Se$_{0.5}$ superconductor by substituting 10\% of Ni for Fe which leads to an electron doping of the system. We could resolve three hole pockets near the zone center and an electron pocket near the zone corner in the case of FeTe$_{0.5}$Se$_{0.5}$, whe…
▽ More
Using angle-resolved photoemission spectroscopy (ARPES), we studied the effect of the impurity potential on the electronic structure of FeTe$_{0.5}$Se$_{0.5}$ superconductor by substituting 10\% of Ni for Fe which leads to an electron doping of the system. We could resolve three hole pockets near the zone center and an electron pocket near the zone corner in the case of FeTe$_{0.5}$Se$_{0.5}$, whereas only two hole pockets near the zone center and an electron pocket near the zone corner are resolved in the case of Fe$_{0.9}$Ni$_{0.1}$Te$_{0.5}$Se$_{0.5}$, suggesting that the hole pocket having predominantly the $xy$ orbital character is very sensitive to the impurity scattering. Upon electron doping, the size of the hole pockets decrease and the size of the electron pockets increase as compared to the host compound. However, the observed changes in the size of the electron and hole pockets are not consistent with the rigid-band model. Moreover, the effective mass of the hole pockets is reduced near the zone center and of the electron pockets is increased near the zone corner in the doped Fe$_{0.9}$Ni$_{0.1}$Te$_{0.5}$Se$_{0.5}$ as compared to FeTe$_{0.5}$Se$_{0.5}$. We refer these observations to the changes of the spectral function due to the effect of the impurity potential of the dopants.
△ Less
Submitted 24 May, 2016;
originally announced May 2016.
-
Structural and Transport Studies of Under Doped FeTe1-xSex(x=0.0, 0.01, 0.03, 0.05) Single Crystals
Authors:
P. K. Maheshwari,
Rajveer Jha,
Bhasker Gahtori,
V. P. S. Awana
Abstract:
We report synthesis of under doped non-superconducting parent compound of iron chalcogenide, i.e FeTe1-xSex (x=0.0, 0.01, 0.03, 0.05) single crystals by flux free method. These FeTe1-xSex (x=0.0, 0.01, 0.03, 0.05) single crystals are crystallized in the tetragonal structure with space group P4/nmm at room temperature. Detailed scanning electron microscopy (SEM) results showed that the crystals are…
▽ More
We report synthesis of under doped non-superconducting parent compound of iron chalcogenide, i.e FeTe1-xSex (x=0.0, 0.01, 0.03, 0.05) single crystals by flux free method. These FeTe1-xSex (x=0.0, 0.01, 0.03, 0.05) single crystals are crystallized in the tetragonal structure with space group P4/nmm at room temperature. Detailed scanning electron microscopy (SEM) results showed that the crystals are formed in slab-like morphology structure. Powder X-Ray diffraction (XRD) results show that (0 0 l) peaks are shifted towards higher angel with increasing Se concentration. Coupled magnetic and structural phase transition temperature, being seen as a step in resistivity, decreases from around 67K for x = 0.0 to 55K for x = 0.05 crystal. Further, the step in resistivity is seen to be hysteric (ΔT) in nature, i.e., different step temperatures in cooling and warming cycles. Interestingly, the hysteric (ΔT) becomes narrower from around 5.8K for x =0.0 to 0.95K for x =0.05 crystal.
△ Less
Submitted 19 January, 2016;
originally announced January 2016.
-
Structural, and Magnetic properties of flux free large FeTe Single crystal
Authors:
P. K Maheshwari,
Rajveer Jha,
Bhasker Gahtori,
V. P. S. Awana
Abstract:
We report synthesis of non superconducting parent compound of iron chalcogenide, i.e., FeTe single crystal by self flux method. The FeTe single crystal is crystallized in tetragonal structure with the P4/nmm space group. The detailed SEM (scanning electron microscopy) results showed that the crystals are formed in slab like morphology and are near (slight deficiency of Te) stoichiometric with homo…
▽ More
We report synthesis of non superconducting parent compound of iron chalcogenide, i.e., FeTe single crystal by self flux method. The FeTe single crystal is crystallized in tetragonal structure with the P4/nmm space group. The detailed SEM (scanning electron microscopy) results showed that the crystals are formed in slab like morphology and are near (slight deficiency of Te) stoichiometric with homogenous distribution of Fe and Te. The coupled structural and magnetic phase transition is seen at around 70K in both electrical resistivity and magnetization measurements, which is hysteric (deltaT = 5K) in nature with cooling and warming cycles. Magnetic susceptibility (chi-T) measurements showed the magnetic transition to be of antiferromagnetic nature, which is substantiated by isothermal magnetization (M-H) plots as well. The temperature dependent electrical resistivity measured in 10kOe field in both in plane and out of plane field directions showed that the hysteric width nearly becomes double to deltaT = 10K, and is maximum for the out of plane field direction for the studied FeTe single crystal. We also obtained a sharp spike like peak in heat capacity Cp(T) measurement due to the coupled structural and magnetic order phase transitions.
△ Less
Submitted 15 January, 2016; v1 submitted 13 July, 2015;
originally announced July 2015.
-
Flux free growth of large FeSe1/2Te1/2 superconducting single crystals by an easy high temperature melt and slow cooling method
Authors:
Rajveer Jha,
P. K. Maheshwari,
Bhasker Gahtori,
V. P. S. Awana
Abstract:
We report successful growth of flux free large single crystals of superconducting FeSe1/2Te1/2 with typical dimensions of up to few cm. The AC and DC magnetic measurements revealed the superconducting transition temperature (Tc) value of around 11.5K and the iso-thermal MH showed typical type-II superconducting behavior. The lower critical field being estimated by measuring the low field iso-therm…
▽ More
We report successful growth of flux free large single crystals of superconducting FeSe1/2Te1/2 with typical dimensions of up to few cm. The AC and DC magnetic measurements revealed the superconducting transition temperature (Tc) value of around 11.5K and the iso-thermal MH showed typical type-II superconducting behavior. The lower critical field being estimated by measuring the low field iso-thermal magnetization in superconducting regime is found to be above 200 Oe at 0K.
△ Less
Submitted 7 September, 2015; v1 submitted 6 February, 2015;
originally announced February 2015.
-
Effect of high temperature heat treatments on the quality factor of a large-grain superconducting radio-frequency niobium cavity
Authors:
P. Dhakal,
G. Ciovati,
G. R. Myneni,
K. E. Gray,
N. Groll,
P. Maheshwari,
D. M. McRae,
R. Pike,
T. Proslier,
F. Stevie,
R. P. Walsh,
Q. Yang,
J. Zasadzinzki
Abstract:
Large-grain Nb has become a viable alternative to fine-grain Nb for the fabrication of superconducting radio-frequency cavities. In this contribution we report the results from a heat treatment study of a large-grain 1.5 GHz single-cell cavity made of "medium purity" Nb. The baseline surface preparation prior to heat treatment consisted of standard buffered chemical polishing. The heat treatment i…
▽ More
Large-grain Nb has become a viable alternative to fine-grain Nb for the fabrication of superconducting radio-frequency cavities. In this contribution we report the results from a heat treatment study of a large-grain 1.5 GHz single-cell cavity made of "medium purity" Nb. The baseline surface preparation prior to heat treatment consisted of standard buffered chemical polishing. The heat treatment in the range 800 - 1400 C was done in a newly designed vacuum induction furnace. Q0 values of the order of 2x1010 at 2.0 K and peak surface magnetic field (Bp) of 90 mT were achieved reproducibly. A Q0-value of (5+-1)1010 at 2.0 K and Bp = 90 mT was obtained after heat treatment at 1400 C. This is the highest value ever reported at this temperature, frequency and field. Samples heat treated with the cavity at 1400 C were analyzed by secondary ion mass spectrometry, secondary electron microscopy, energy dispersive X-ray, point contact tunneling and X-ray diffraction and revealed a complex surface composition which includes titanium oxide, increased carbon and nitrogen content but reduced hydrogen concentration compared to a non heat-treated sample.
△ Less
Submitted 25 March, 2013; v1 submitted 25 October, 2012;
originally announced October 2012.