Micromechanical fatigue experiments for validation of microstructure-sensitive fatigue simulation models
Authors:
Ali Riza Durmaz,
Erik Natkowski,
Nikolai Arnaudov,
Petra Sonnweber-Ribic,
Stefan Weihe,
Sebastian Münstermann,
Chris Eberl,
Peter Gumbsch
Abstract:
Crack initiation governs high cycle fatigue life and is susceptible to microstructural details. While corresponding microstructure-sensitive models are available, their validation is difficult. We propose a validation framework where a fatigue test is mimicked in a sub-modeling simulation by embedding the measured microstructure into the specimen geometry and adopting the experimental boundary con…
▽ More
Crack initiation governs high cycle fatigue life and is susceptible to microstructural details. While corresponding microstructure-sensitive models are available, their validation is difficult. We propose a validation framework where a fatigue test is mimicked in a sub-modeling simulation by embedding the measured microstructure into the specimen geometry and adopting the experimental boundary conditions. Exemplary, a phenomenological crystal plasticity model was applied to predict deformation in ferritic steel (EN1.4003). Hotspots in commonly used fatigue indicator parameter maps are compared with damage segmented from micrographs. Along with the data, the framework is published for benchmarking future micromechanical fatigue models.
△ Less
Submitted 8 December, 2021;
originally announced December 2021.
-
On the effect of strain and triaxiality on void evolution in a heterogeneous microstructure -- A statistical and single void study of damage in DP800
Authors:
Carl F. Kusche,
Felix Pütz,
Sebastian Münstermann,
Talal Al-Samman,
Sandra Korte-Kerzel
Abstract:
In order to improve the understanding of damage evolution in mechanically heterogeneous microstructures, like the ones of dual-phase steels, the influence of the applied stress state is a key element. In this work, we studied the influence of the globally applied stress state on the evolution of damage in such a microstructure. Classical damage models allow predictions of damage during deformation…
▽ More
In order to improve the understanding of damage evolution in mechanically heterogeneous microstructures, like the ones of dual-phase steels, the influence of the applied stress state is a key element. In this work, we studied the influence of the globally applied stress state on the evolution of damage in such a microstructure. Classical damage models allow predictions of damage during deformation based on considerations of the material as an isotropic continuum. Here, we investigate their validity in a dual phase microstructure that is locally dominated by its microstructural morphological complexity based on a statistical ensemble of thousands of individual voids formed under different stress states. For this purpose, we combined a calibrated material model incorporating damage formation to assess the local stress state in samples with different notch geometries and high-resolution electron microscopy of large areas using a deep learning-based automated micrograph analysis to detect and classify microstructural voids according to their source of origin. This allowed us to obtain both the continuum stress state during deformation and statistically relevant data of individual void formation. We found that the applied plastic strain is the major influence on the overall number, and therefore the nucleation of new voids, while triaxiality correlates with the median void size, supporting its proposed influence on void growth. In contrast, coalescence of voids leading to failure appears related to local instabilities in the form of shear band formation and is therefore only indirectly determined by the global stress state in that it determines the global distribution, density and size of voids.
△ Less
Submitted 4 June, 2020;
originally announced June 2020.
-
The differences of damage initiation and accumulation of DP steels: a numerical and experimental analysis
Authors:
Felix Pütz,
Fuhui Shen,
Markus Könemann,
Sebastian Münstermann
Abstract:
Many studies have examined the damage behaviour of dual-phase steels already. It is a topic of high interest, since understanding the mechanisms of damage during forming processes enables the production of steels with improved properties and damage tolerance. However, the focus was rarely on the comparison between representatives of this steel class, and the numerical simulation for the quantifica…
▽ More
Many studies have examined the damage behaviour of dual-phase steels already. It is a topic of high interest, since understanding the mechanisms of damage during forming processes enables the production of steels with improved properties and damage tolerance. However, the focus was rarely on the comparison between representatives of this steel class, and the numerical simulation for the quantification of damage states was not thoroughly used. Therefore, this study compares the damage initiation and accumulation of two dual-phase steels (DP800 and DP1000), which are used in the automotive industry. Additionally, parameter sets of a phenomenological damage mechanics model with coupled damage evolution are calibrated for each material. The combined analysis reveals an earlier initiation of damage for the DP800, where the damage accumulation phase is prolonged. For DP1000 the damage nucleates only shortly before material failure. The material model is able to correctly predict the behaviour, while experimental analysis confirms the prediction via light optical and SEM metallography.
△ Less
Submitted 27 April, 2020;
originally announced April 2020.