Charge ordering in charge-compensated $Na_{0.41}CoO_2$ by oxonium ions
Authors:
C. H. Wang,
H. T. Zhang,
X. X. Lu,
G. Wu,
J. Q. Li,
X. H. Chen
Abstract:
Charge ordering behavior is observed in the crystal prepared through the immersion of the $Na_{0.41}CoO_2$ crystal in distilled water. Discovery of the charge ordering in the crystal with Na content less than 0.5 indicates that the immersion in water brings about the reduction of the
$Na_{0.41}CoO_2$. The formal valence of Co changes from +3.59 estimated from the
Na content to +3.5, the same a…
▽ More
Charge ordering behavior is observed in the crystal prepared through the immersion of the $Na_{0.41}CoO_2$ crystal in distilled water. Discovery of the charge ordering in the crystal with Na content less than 0.5 indicates that the immersion in water brings about the reduction of the
$Na_{0.41}CoO_2$. The formal valence of Co changes from +3.59 estimated from the
Na content to +3.5, the same as that in $Na_{0.5}CoO_2$. The charge compensation is confirmed to arise from the intercalation of the oxonium ions as occurred in the superconducting sodium cobalt oxide bilayer-hydrate.\cite{takada1}
The charge ordering is the same as that observed in $Na_{0.5}CoO_2$. It suggests that the Co valence of +3.5 is necessary for the charge ordering.
△ Less
Submitted 20 December, 2005; v1 submitted 9 January, 2005;
originally announced January 2005.
-
Effect of oxygen content on the transport properties and magnetoresistance in [Ca$_{2}$CoO$_{3-δ}$]$_{0.62}$[CoO$_{2}$] single crystals
Authors:
X. G. Luo,
X. H. Chen,
G. Y. Wang,
C. H. Wang,
Y. M. Xiong,
H. B. Song,
H. Li,
X. X. Lu
Abstract:
Transport property is investigated in [Ca$_{2}$CoO$_{3-δ}$]$_{0.62}$[CoO$_{2}$] single crystals obtained by varying annealing conditions. The $ρ_{ab}(T)$ exhibits a resistivity minimum, and the temperature corresponding to this minimum increases with the loss of oxygen content, indicative of the enhancement of spin density wave (SDW). Large negative magnetoresistance (MR) was observed in all sin…
▽ More
Transport property is investigated in [Ca$_{2}$CoO$_{3-δ}$]$_{0.62}$[CoO$_{2}$] single crystals obtained by varying annealing conditions. The $ρ_{ab}(T)$ exhibits a resistivity minimum, and the temperature corresponding to this minimum increases with the loss of oxygen content, indicative of the enhancement of spin density wave (SDW). Large negative magnetoresistance (MR) was observed in all single crystals [Ca$_{2}$CoO$_{3-δ}$]$_{0.62}$[CoO$_{2}$], while a magnetic-field-driven insulator-to-metal (IM) transition in oxygen annealed samples. These results suggest a ferromagnetic correlation in system enhanced by oxygen content. In addition, a low temperature thermal activation resistivity induced by fields was observed in single crystals annealed in oxygen atmosphere.
△ Less
Submitted 11 December, 2004;
originally announced December 2004.
-
Dimensional crossover and anomalous magnetoresistivity in single crystals $Na_xCoO_2$
Authors:
C. H. Wang,
X. H. Chen,
J. L. Luo,
G. T. Liu,
X. X. Lu,
H. T. Zhang,
G. Y. Wang,
X. G. Luo,
N. L. Wang
Abstract:
The in-plane ($ρ_{ab}$) and c-axis ($ρ_c$) resistivities, and the magnetoresistivity of single crystals $Na_xCoO_2$ with x = 0.7, 0.5 and 0.3 were studied systematically. $ρ_{ab}(T)$ shows similar temperature dependence between $Na_{0.3}CoO_2$ and $Na_{0.7}CoO_2$, while $ρ_c(T)$ is quite different. A dimensional crossover from two to three occurs with decreasing Na concentration from 0.7 to 0.3.…
▽ More
The in-plane ($ρ_{ab}$) and c-axis ($ρ_c$) resistivities, and the magnetoresistivity of single crystals $Na_xCoO_2$ with x = 0.7, 0.5 and 0.3 were studied systematically. $ρ_{ab}(T)$ shows similar temperature dependence between $Na_{0.3}CoO_2$ and $Na_{0.7}CoO_2$, while $ρ_c(T)$ is quite different. A dimensional crossover from two to three occurs with decreasing Na concentration from 0.7 to 0.3. The angular dependence of in-plane magnetoresistivity for 0.5 sample shows a \emph{"d-wave-like"} symmetry at 2K, while the \emph{"p-wave-like"} symmetry at 20 K. These results give an evidence for existence of a \emph{spin ordering orientation} below 20 K turned by external field, like the stripes in cuprates.
△ Less
Submitted 2 November, 2004;
originally announced November 2004.