Domain wall patterning and giant response functions in ferrimagnetic spinels
Authors:
L. L. Kish,
A. Thaler,
M. Lee,
A. V. Zakrzewski,
D. Reig-i-Plessis,
B. Wolin,
X. Wang,
K. C. Littrell,
R. Budakian,
H. D. Zhou,
V. S. Zapf,
A. A. Aczel,
L. DeBeer-Schmitt,
G. J. MacDougall
Abstract:
The manipulation of mesoscale domain wall phenomena has emerged as a powerful strategy for designing ferroelectric responses in functional devices, but its full potential has not yet been realized in the field of magnetism. We show that mechanically strained samples of Mn$_3$O$_4$ and MnV$_2$O$_4$ exhibit a stripe-like patterning of the bulk magnetization below known magnetostructural transitions,…
▽ More
The manipulation of mesoscale domain wall phenomena has emerged as a powerful strategy for designing ferroelectric responses in functional devices, but its full potential has not yet been realized in the field of magnetism. We show that mechanically strained samples of Mn$_3$O$_4$ and MnV$_2$O$_4$ exhibit a stripe-like patterning of the bulk magnetization below known magnetostructural transitions, similar to the structural domains reported in ferroelectric materials. Building off our previous magnetic force microscopy data, we use small angle neutron scattering to show that these patterns extend to the bulk, and demonstrate an ability to manipulate the domain walls via applied magnetic field and mechanical stress. We then connect these domains back to the anomalously large magnetoelastic and magnetodielectric response functions reported in these materials, directly correlating local and macroscopic measurements on the same crystals.
△ Less
Submitted 30 November, 2020;
originally announced November 2020.
-
FeS: Structure and Composition Relations to Superconductivity and Magnetism
Authors:
S. J. Kuhn,
M. K. Kidder,
W. M. Chance,
C. dela Cruz,
M. A. McGuire,
D. S. Parker,
L. Li,
L. Debeer-Schmitt,
J. Ermentrout,
K. Littrell,
M. R. Eskildsen,
A. S. Sefat
Abstract:
Structure and composition of iron chalcogenides have a delicate relationship with magnetism and superconductivity. In this report we investigate the iron sulfide layered tetragonal phase (t-FeS), and compare with three-dimensional hexagonal phase (h-FeS). X-ray diffraction reveals the absence of structural transitions for both t- and h-FeS below room temperature, and gives phase compositions of Fe…
▽ More
Structure and composition of iron chalcogenides have a delicate relationship with magnetism and superconductivity. In this report we investigate the iron sulfide layered tetragonal phase (t-FeS), and compare with three-dimensional hexagonal phase (h-FeS). X-ray diffraction reveals the absence of structural transitions for both t- and h-FeS below room temperature, and gives phase compositions of Fe0.93(1)S and Fe0.84(1)S, respectively, for the samples studied here. The a lattice parameter of bigger than 3.68 A is significant for causing bulk superconductivity in iron sulfide, which is controlled by composition and structural details such as iron stoichiometry and concentration of vacancy. While h-FeS with a = 3.4436(1) A has magnetic ordering well above room temperature, our t-FeS with a =3.6779(8)A shows filamentary superconductivity below Tc = 4 K with less than 15% superconducting volume fraction. Also for t-FeS, the magnetic susceptibility shows an anomaly at ~ 15 K, and neutron diffraction reveals a commensurate antiferromagnetic ordering below TN = 116 K, with wave vector km= (0.25,0.25,0) and 0.46(2)uB/Fe. Although two synthesis routes are used here to stabilize t vs h crystal structures (hydrothermal vs solid-state methods), both FeS compounds order on two length-scales of ~1000 nm sheets or blocks and ~ 20 nm smaller particles, shown by neutron scattering. First principles calculations reveal a high sensitivity to the structure for the electronic and magnetic properties in t-FeS, predicting marginal antiferromagnetic instability for our compound (sulfur height of zS ~0.252) with an ordering energy of ~11 meV/Fe, while h-FeS is magnetically stable.
△ Less
Submitted 4 March, 2016;
originally announced March 2016.
-
Vortex lattice structure in BaFe2(As0.67P0.33)2 by the small-angle neutron scattering technique
Authors:
R. Morisaki-Ishii,
H. Kawano-Furukawa,
A. S. Cameron,
L. Lemberger,
E. Blackburn,
A. T. Holmes,
E. M. Forgan,
L. M. DeBeer-Schmitt,
K. Littrell,
M. Nakajima,
K. Kihou,
C. H. Lee,
A. Iyo,
H. Eisaki,
S. Uchida,
J. S. White,
C. D. Dewhurst,
J. L. Gavilano,
M. Zolliker
Abstract:
We have observed a magnetic vortex lattice (VL) in BaFe2(As_{0.67}P_{0.33})2 (BFAP) single crystals by small-angle neutron scattering (SANS). With the field along the c-axis, a nearly isotropic hexagonal VL was formed in the field range from 1 to 16 T, which is a record for this technique in the pnictides, and no symmetry changes in the VL were observed. The temperature-dependence of the VL signal…
▽ More
We have observed a magnetic vortex lattice (VL) in BaFe2(As_{0.67}P_{0.33})2 (BFAP) single crystals by small-angle neutron scattering (SANS). With the field along the c-axis, a nearly isotropic hexagonal VL was formed in the field range from 1 to 16 T, which is a record for this technique in the pnictides, and no symmetry changes in the VL were observed. The temperature-dependence of the VL signal was measured and confirms the presence of (non d-wave) nodes in the superconducting gap structure for measurements at 5 T and below. The nodal effects were suppressed at high fields. At low fields, a VL reorientation transition was observed between 1 T and 3 T, with the VL orientation changing by 45°. Below 1 T, the VL structure was strongly affected by pinning and the diffraction pattern had a fourfold symmetry. We suggest that this (and possibly also the VL reorientation) is due to pinning to defects aligned with the crystal structure, rather than being intrinsic.
△ Less
Submitted 29 May, 2014;
originally announced May 2014.
-
Field Dependence of the Superconducting Basal Plane Anisotropy of TmNi2B2C
Authors:
P. Das,
J. M. Densmore,
C. Rastovski,
K. J. Schlesinger,
M. Laver,
C. D. Dewhurst,
K. Littrell,
S. L. Bud'ko,
P. C. Canfield,
M. R. Eskildsen
Abstract:
The superconductor TmNi2B2C possesses a significant four-fold basal plane anisotropy, leading to a square Vortex Lattice (VL) at intermediate fields. However, unlike other members of the borocarbide superconductors, the anisotropy in TmNi2B2C appears to decrease with increasing field, evident by a reentrance of the square VL phase. We have used Small Angle Neutron Scattering measurements of the VL…
▽ More
The superconductor TmNi2B2C possesses a significant four-fold basal plane anisotropy, leading to a square Vortex Lattice (VL) at intermediate fields. However, unlike other members of the borocarbide superconductors, the anisotropy in TmNi2B2C appears to decrease with increasing field, evident by a reentrance of the square VL phase. We have used Small Angle Neutron Scattering measurements of the VL to study the field dependence of the anisotropy. Our results provide a direct, quantitative measurement of the decreasing anisotropy. We attribute this reduction of the basal plane anisotropy to the strong Pauli paramagnetic effects observed in TmNi2B2C and the resulting expansion of vortex cores near Hc2.
△ Less
Submitted 24 September, 2012;
originally announced September 2012.
-
Kondo behavior, ferromagnetic correlations, and crystal fields in the heavy Fermion compounds Ce3X (X=In, Sn)
Authors:
C. H. Wang,
J. M. Lawrence,
A. D. Christianson,
E. A. Goremychkin,
V. R. Fanelli,
K. Gofryk,
E. D. Bauer,
F. Ronning,
J. D. Thompson,
N. R. de Souza,
A. I. Kolesnikov,
K. C. Littrell
Abstract:
We report measurements of inelastic neutron scattering, magnetic susceptibility, magnetization, and the magnetic field dependence of the specific heat for the heavy Fermion compounds Ce$_3$In and Ce$_3$Sn. The neutron scattering results show that the excited crystal field levels have energies $E_1$ = 13.2 meV, $E_2$ = 44.8 meV for Ce$_3$In and $E_1$ = 18.5 meV, $E_2$ = 36.1 meV for Ce$_3$Sn. The K…
▽ More
We report measurements of inelastic neutron scattering, magnetic susceptibility, magnetization, and the magnetic field dependence of the specific heat for the heavy Fermion compounds Ce$_3$In and Ce$_3$Sn. The neutron scattering results show that the excited crystal field levels have energies $E_1$ = 13.2 meV, $E_2$ = 44.8 meV for Ce$_3$In and $E_1$ = 18.5 meV, $E_2$ = 36.1 meV for Ce$_3$Sn. The Kondo temperature deduced from the quasielastic linewidth is 17 K for Ce$_3$In and 40 K for Ce$_3$Sn. The low temperature behavior of the specific heat, magnetization, and susceptibility can not be well-described by J=1/2 Kondo physics alone, but require calculations that include contributions from the Kondo effect, broadened crystal fields, and ferromagnetic correlations, all of which are known to be important in these compounds. We find that in Ce$_3$In the ferromagnetic fluctuation makes a 10-15 % contribution to the ground state doublet entropy and magnetization. The large specific heat coefficient $γ$ in this heavy fermion system thus arises more from the ferromagnetic correlations than from the Kondo behavior.
△ Less
Submitted 17 March, 2010;
originally announced March 2010.