Showing 1–28 of 28 results for author: Levin, G A

AC Losses of Copper Stabilized Multifilament YBCO Coated Conductors

Authors: G. A. Levin, J. Murphy, T. J. Haugan, J. Šouc, J. Kováč, P. Kováč

Abstract: We report the data on magnetization losses and critical current of multifilament copper stabilized coated conductors. Eight centimeters long samples of copper stabilized YBa2Cu3O7-x (YBCO) coated conductors manufactured commercially were subdivided into superconducting filaments by near-IR laser micromachining. The width of the superconducting stripes was varied from 0.2 mm to 0.04 mm. Some of the… ▽ More We report the data on magnetization losses and critical current of multifilament copper stabilized coated conductors. Eight centimeters long samples of copper stabilized YBa2Cu3O7-x (YBCO) coated conductors manufactured commercially were subdivided into superconducting filaments by near-IR laser micromachining. The width of the superconducting stripes was varied from 0.2 mm to 0.04 mm. Some of the samples were striated leaving superconducting bridges for current sharing between the filaments. The AC losses were measured at different sweep rates of the magnetic field up to 14 T/s. We will present the results for the hysteresis and coupling losses and discuss the means to reduce the coupling loss by changing the processing parameters of micromachining and by post-ablation treatment. △ Less

Submitted 17 December, 2012; v1 submitted 3 December, 2012; originally announced December 2012.

Comments: In the first version of this preprint the value of copper resistivity used for calculating eddy current losses was ten times lower than the actual value. Please don't ask how that could have happened. Correspondingly, the conclusions described in the first column on page 4 were wrong and are now corrected

Heat exchange mediated by a quantum system

Authors: George Y. Panasyuk, George A. Levin, Kirk L. Yerkes

Abstract: We consider heat transfer between two thermal reservoirs mediated by a quantum system using the generalized quantum Langevin equation. The thermal reservoirs are treated as ensembles of oscillators within the framework of the Drude-Ullersma model. General expressions for the heat current and thermal conductance are obtained for arbitrary coupling strength between the reservoirs and the mediator an… ▽ More We consider heat transfer between two thermal reservoirs mediated by a quantum system using the generalized quantum Langevin equation. The thermal reservoirs are treated as ensembles of oscillators within the framework of the Drude-Ullersma model. General expressions for the heat current and thermal conductance are obtained for arbitrary coupling strength between the reservoirs and the mediator and for different temperature regimes. As an application of these results we discuss the origin of Fourier's law in a chain of large, but finite subsystems coupled to each other by the quantum mediators. We also address a question of anomalously large heat current between the STM tip and substrate found in a recent experiment. The question of minimum thermal conductivity is revisited in the framework of scaling theory as a potential application of the developed approach. △ Less

Submitted 7 August, 2012; originally announced August 2012.

Comments: 16 pages, 6 figures

Anisotropic magnetoresistance of bulk carbon nanotube sheets

Authors: E. Cimpoiasu, G. A. Levin, B. White, D. Lashmore

Abstract: We have measured the magnetoresistance of stretched sheets of carbon nanotubes in temperatures ranging from 2 K to 300 K and in magnetic fields up to 9 T, oriented either perpendicular or parallel to the plane of the sheets. The samples have been partially aligned by post-fabrication stretching, such that the direction of stretching was either parallel or perpendicular to the direction of applied… ▽ More We have measured the magnetoresistance of stretched sheets of carbon nanotubes in temperatures ranging from 2 K to 300 K and in magnetic fields up to 9 T, oriented either perpendicular or parallel to the plane of the sheets. The samples have been partially aligned by post-fabrication stretching, such that the direction of stretching was either parallel or perpendicular to the direction of applied electric current. We have observed large differences between the magnetoresistance measured under the two field orientations, most pronounced at the lowest temperatures, highest fields, and for the laterally-aligned sample. Treatment of the sheets with nitric acid affects this anisotropy. We analyzed the results within the theoretical framework of weak and strong localization and concluded that the anisotropy bears the mark of a more unusual phenomenon, possibly magnetically-induced mechanical strain. △ Less

Submitted 19 June, 2012; originally announced June 2012.

Comments: 34 pages, 10 figures

Energy Transport in Closed Quantum Systems

Authors: G. A. Levin, W. A. Jones, K. Walczak, K. L. Yerkes

Abstract: We examine energy transport in an ensemble of closed quantum systems driven by stochastic perturbations. One can show that the probability and energy fluxes can be described in terms of quantum advection modes (QAM) associated with the off-diagonal elements of the density matrix. These QAM play the role of Landauer channels in a system with discrete energy spectrum and the eigenfunctions that cann… ▽ More We examine energy transport in an ensemble of closed quantum systems driven by stochastic perturbations. One can show that the probability and energy fluxes can be described in terms of quantum advection modes (QAM) associated with the off-diagonal elements of the density matrix. These QAM play the role of Landauer channels in a system with discrete energy spectrum and the eigenfunctions that cannot be described as plane waves. In order to determine the type of correlations that exist between the direction and magnitudes of each QAM and the average direction of energy and probability fluxes we have numerically solved the time-dependent Schrödinger equation describing a single particle trapped in a parabolic potential well which is perturbed by stochastic 'ripples'. The ripples serve as a localized energy source and are offset to one side of the potential well. As the result a non-zero net energy flux flows from one part of the potential well to another across the symmetry center of the potential. We find that some modes exhibit positive correlation with the direction of the energy flow. Other modes, that carry a smaller energy per unit of the probability flux, anticorrelate with the energy flow and thus provide a backflow of the probability. The overall picture of energy transport that emerges from our results is very different from the conventional one based on a system with continuous energy spectrum. △ Less

Submitted 22 February, 2012; originally announced February 2012.

Comments: 12 pages, 6 figures and one table. To be published in Phys. Rev. E

The effects of superconductor-stabilizer interfacial resistance on quench of a pancake coil made out of coated conductor

Authors: G. A. Levin, W. A. Jones, K. A. Novak, P. N. Barnes

Abstract: We present the results of numerical analysis of normal zone propagation in a stack of $YBa_2Cu_3O_{7-x}$ coated conductors which imitates a pancake coil. Our main purpose is to determine whether the quench protection quality of such coils can be substantially improved by increased contact resistance between the superconducting film and the stabilizer. We show that with increased contact resistance… ▽ More We present the results of numerical analysis of normal zone propagation in a stack of $YBa_2Cu_3O_{7-x}$ coated conductors which imitates a pancake coil. Our main purpose is to determine whether the quench protection quality of such coils can be substantially improved by increased contact resistance between the superconducting film and the stabilizer. We show that with increased contact resistance the speed of normal zone propagation increases, the detection of a normal zone inside the coil becomes possible earlier, when the peak temperature inside the normal zone is lower, and stability margins shrink. Thus, increasing contact resistance may become a viable option for improving the prospects of coated conductors for high $T_c$ magnets applications. △ Less

Submitted 28 July, 2010; v1 submitted 21 July, 2010; originally announced July 2010.

Comments: 9 pages, 4 figures

Use of 2G coated conductors for efficient shielding of DC magnetic fields

Authors: J. -F. Fagnard, M. Dirickx, G. A. Levin, P. N. Barnes, B. Vanderheyden, P. Vanderbemden

Abstract: This paper reports the results of an experimental investigation of the performance of two types of magnetic screens assembled from YBa2Cu3O7-d (YBCO) coated conductors. Since effective screening of the axial DC magnetic field requires the unimpeded flow of an azimuthal persistent current, we demonstrate a configuration of a screening shell made out of standard YBCO coated conductor capable to acco… ▽ More This paper reports the results of an experimental investigation of the performance of two types of magnetic screens assembled from YBa2Cu3O7-d (YBCO) coated conductors. Since effective screening of the axial DC magnetic field requires the unimpeded flow of an azimuthal persistent current, we demonstrate a configuration of a screening shell made out of standard YBCO coated conductor capable to accomplish that. The screen allows the persistent current to flow in the predominantly azimuthal direction at a temperature of 77 K. The persistent screen, incorporating a single layer of superconducting film, can attenuate an external magnetic field of up to 5 mT by more than an order of magnitude. For comparison purposes, another type of screen which incorporates low critical temperature quasi-persistent joints was also built. The shielding technique we describe here appears to be especially promising for the realization of large scale high-Tc superconducting screens. △ Less

Submitted 17 June, 2010; originally announced June 2010.

Comments: 8 pages, 3 figures

The effects of superconductor-stabilizer interfacial resistance on quench of current-carrying coated conductor

Authors: G. A. Levin, P. N. Barnes, K. A. Novak

Abstract: We present the results of numerical analysis of a model of normal zone propagation in coated conductors. The main emphasis is on the effects of increased contact resistance between the superconducting film and the stabilizer on the speed of normal zone propagation, the maximum temperature rise inside the normal zone, and the stability margins. We show that with increasing contact resistance the… ▽ More We present the results of numerical analysis of a model of normal zone propagation in coated conductors. The main emphasis is on the effects of increased contact resistance between the superconducting film and the stabilizer on the speed of normal zone propagation, the maximum temperature rise inside the normal zone, and the stability margins. We show that with increasing contact resistance the speed of normal zone propagation increases, the maximum temperature inside the normal zone decreases, and stability margins shrink. This may have an overall beneficial effect on quench protection quality of coated conductors. We also briefly discuss the propagation of solitons and development of the temperature modulation along the wire. △ Less

Submitted 28 September, 2009; originally announced September 2009.

Comments: To be published in Superconductor Science and Technology. This preprint contains one animated figure (Fig. 6(a)). when asked whether you want to play the content, click "Play". Acrobat Reader (Windows and Mac, but not Linux) will play embedded flash movies. In the printed copy Fig. 6(b) will show the temperature profile at gamma t=150

Emergence of dissipative structures in current-carrying superconducting wires

Authors: G. A. Levin, P. N. Barnes, J. P. Rodriguez, J. A. Connors, J. S. Bulmer

Abstract: We discuss the emergence of a spontaneous temperature and critical current spatial modulation in current-carrying high temperature superconducting wire. The modulation of the critical current along the wire on a scale of 3 - 10 mm forces a fraction of the transport current to crisscross the resistive interface between the superconducting film and normal metal stabilizer attached to it. This gene… ▽ More We discuss the emergence of a spontaneous temperature and critical current spatial modulation in current-carrying high temperature superconducting wire. The modulation of the critical current along the wire on a scale of 3 - 10 mm forces a fraction of the transport current to crisscross the resistive interface between the superconducting film and normal metal stabilizer attached to it. This generates additional heat that allows such a structure to be self sustainable. Stability and the conditions for experimental observation of this phenomenon are also discussed. △ Less

Submitted 22 April, 2009; originally announced April 2009.

Comments: To be published in Phys. Rev. E (in section Chaos and Pattern Formation)

Stability and normal zone propagation speed in YBCO coated conductors with increased interfacial resistance

Authors: George A. Levin, Paul N. Barnes, Jose P. Rodriguez, Jake A. Connors, John S. Bulmer

Abstract: We will discuss how stability and speed of normal zone propagation in YBCO-coated conductors is affected by interfacial resistance between the superconducting film and the stabilizer. Our numerical simulation has shown that the increased interfacial resistance substantially increases speed of normal zone propagation and decreases the stability margins. Optimization of the value of the resistance… ▽ More We will discuss how stability and speed of normal zone propagation in YBCO-coated conductors is affected by interfacial resistance between the superconducting film and the stabilizer. Our numerical simulation has shown that the increased interfacial resistance substantially increases speed of normal zone propagation and decreases the stability margins. Optimization of the value of the resistance may lead to a better compromise between stability and quench protection requirements than what is found in currently manufactured coated conductors. △ Less

Submitted 4 November, 2008; v1 submitted 25 August, 2008; originally announced August 2008.

Comments: To be published in IEEE Transactions on Applied Superconductivity. A typo in eq. (3)is corrected and Fig. 1 is modified. Typo in Eq. (5) is corrected

Normal zone in $YBa_2Cu_3O_{6+x}$-coated conductors

Authors: George A. Levin, Paul N. Barnes

Abstract: We consider the distribution of an electric field in YBCO-coated conductors for a situation in which the DC transport current is forced into the copper stabilizer due to a weak link -- a section of the superconducting film with a critical current less than the transport current. The electric field in the metal substrate is also discussed. The results are compared with recent experiments on norma… ▽ More We consider the distribution of an electric field in YBCO-coated conductors for a situation in which the DC transport current is forced into the copper stabilizer due to a weak link -- a section of the superconducting film with a critical current less than the transport current. The electric field in the metal substrate is also discussed. The results are compared with recent experiments on normal zone propagation in coated conductors for which the substrate and stabilizer are insulated from each other. The potential difference between the substrate and stabilizer, and the electric field in the substrate outside the normal zone can be accounted for by a large screening length in the substrate, comparable to the length of the sample. During a quench, the electric field inside the interface between YBCO and stabilizer, as well as in the buffer layer, can be several orders of magnitude greater than the longitudinal macroscopic electric field inside the normal zone. We speculate on the possibility of using possible microscopic electric discharges caused by this large ($\sim $kV/cm) electric field as a means to detect a quench. △ Less

Submitted 27 June, 2007; originally announced June 2007.

Comments: 8 pages, 4 figures

Current sharing between superconducting film and normal metal

Authors: George A. Levin, Paul N. Barnes, John S. Bulmer

Abstract: A two-dimensional model is introduced that describes current sharing between the superconducting and normal metal layers in configuration typical of YBCO-coated conductors. The model is used to compare the effectiveness of surround stabilizer and more conventional one-sided stabilizer. When the resistance of the interface between the superconductor and stabilizer is low enough, the surround stab… ▽ More A two-dimensional model is introduced that describes current sharing between the superconducting and normal metal layers in configuration typical of YBCO-coated conductors. The model is used to compare the effectiveness of surround stabilizer and more conventional one-sided stabilizer. When the resistance of the interface between the superconductor and stabilizer is low enough, the surround stabilizer is less effective than the one-sided stabilizer in stabilizing a hairline crack in the superconducting film. △ Less

Submitted 7 March, 2007; originally announced March 2007.

Comments: 9 pages, 4 figures

AC-Tolerant Multifilament Coated Conductors

Authors: G. A. Levin, P. N. Barnes, N. Amemiya

Abstract: We report the magnetization losses in an experimental multifilament coated conductor. A 4 mm wide and 10 cm long YBCO coated conductor was subdivided into eight 0.5 mm wide filaments by laser ablation and subjected to post-ablation treatment. As the result, the hysteresis loss was reduced, as expected, in proportion to the width of the filaments. However, the coupling loss was reduced dramatical… ▽ More We report the magnetization losses in an experimental multifilament coated conductor. A 4 mm wide and 10 cm long YBCO coated conductor was subdivided into eight 0.5 mm wide filaments by laser ablation and subjected to post-ablation treatment. As the result, the hysteresis loss was reduced, as expected, in proportion to the width of the filaments. However, the coupling loss was reduced dramatically, and became practically negligible, in the range of a sweep rate up to 20 T/s. This represents a drastic improvement on previous multifilament conductors in which often the coupling losses became equal to the hysteresis loss at a sweep rate as low as 3-4 T/s. These results demonstrate that there is an effective and practical way to suppress coupling losses in coated multifilament conductors. △ Less

Submitted 19 September, 2006; originally announced September 2006.

Comments: This paper is based on a talk given at 2006 Applied Superconductivity Conference in Seattle, WA (August 27-September 1, 2006). To be published in IEEE Trans. Appl. Superconductivity

Multifilament YBa2Cu3O6+x -coated conductors with minimized coupling losses

Authors: G. A. Levin, P. N. Barnes, J. W. Kell, N. Amemiya, Z. Jiang, K. Yoda, F. Kimura

Abstract: We report an experimental approach to making multifilament coated conductors with low losses in applied time-varying magnetic field. Previously, the multifilament conductors obtained for that purpose by laser ablation suffered from high coupling losses. Here we report how this problem can be solved. When the substrate metal in the grooves segregating the filaments is exposed to oxygen, it forms… ▽ More We report an experimental approach to making multifilament coated conductors with low losses in applied time-varying magnetic field. Previously, the multifilament conductors obtained for that purpose by laser ablation suffered from high coupling losses. Here we report how this problem can be solved. When the substrate metal in the grooves segregating the filaments is exposed to oxygen, it forms high resistivity oxides that electrically insulate the stripes from each other and from the substrate. As the result, the coupling loss has become negligible over the entire range of tested parameters (magnetic field amplitudes B and frequencies f) available to us. △ Less

Submitted 11 May, 2006; originally announced May 2006.

Comments: Submitted to Appl. Phys. Lett. 10 pages, 3 figures

Coupling losses and transverse resistivity of multifilament YBCO coated superconductors

Authors: M. Polak, L. Krempasky, E. Usak, L. Jansak, E. Demencik, G. A. Levin, P. N. Barnes, D. Wehler, B. Moenter

Abstract: We studied the magnetization losses of four different types of filamentary YBCO coated conductors. A 10 mm wide YBCO coated conductor was subdivided into 20 filaments by laser cutting. The separation of coupling loss from the total is possible because the energy loss per cycle in samples with electrically insulated filaments has a very small frequency dependence. We measured the frequency depend… ▽ More We studied the magnetization losses of four different types of filamentary YBCO coated conductors. A 10 mm wide YBCO coated conductor was subdivided into 20 filaments by laser cutting. The separation of coupling loss from the total is possible because the energy loss per cycle in samples with electrically insulated filaments has a very small frequency dependence. We measured the frequency dependence of the total losses in the frequency range between 0.1 Hz and 500 Hz. The coupling loss was obtained from the total by subtracting the hysteresis loss. The latter was measured at low frequencies since only hysteresis loss is non-negligible at frequencies below 1 Hz. The transverse resistivity was determined from the coupling losses; it was assumed that the sample length is equal to half of the twist pitch. The values of transverse resistivity deduced from the loss data were compared with those obtained by the four-point measurements with current flowing perpendicular to the filaments. Preliminary results indicate that the current method of laser ablation creates electrical contacts between the superconducting filaments and the substrate. This was also confirmed by the Hall probe mapping of the magnetic field in the vicinity of the tape. The measured transverse resistivity was close to the resistivity of the substrate (Hastelloy). △ Less

Submitted 17 February, 2006; originally announced February 2006.

Comments: This paper was presented at 2005 EUCAS Conference

Magnetization Losses in Multiply Connected YBa2Cu3O6+x Coated Conductors

Authors: G. A. Levin, P. N. Barnes, Naoyuki Amemiya, Satoshi Kasai, Keiji Yoda, Zhenan Jiang, A. Polyanskii

Abstract: We report the results of a magnetization losses study in experimental multifilament, multiply connected coated superconductors exposed to time-varying magnetic field. In these samples, the superconducting layer is divided into parallel stripes segregated by non-superconducting grooves. In order to facilitate the current sharing between the stripes and thus increase the reliability of the striate… ▽ More We report the results of a magnetization losses study in experimental multifilament, multiply connected coated superconductors exposed to time-varying magnetic field. In these samples, the superconducting layer is divided into parallel stripes segregated by non-superconducting grooves. In order to facilitate the current sharing between the stripes and thus increase the reliability of the striated conductors, a sparse network of superconducting bridges is superimposed on the striated film. We find that the presence of the bridges does not substantially increase the magnetization losses, both hysteresis and coupling, as long as the number of bridges per length of the sample is not large. These results indicate that it is possible to find a reasonable compromise between the competing requirements of connectivity and loss reduction in an ac-tolerant version of the high temperature coated conductors specifically designed for ac power applications. △ Less

Submitted 21 October, 2005; originally announced October 2005.

Comments: 19 pages, 12 figures to be published in J. Appl. Phys

The Integration of YBCO Coated Conductors into Magnets and Rotating Machinery

Authors: G. A. Levin, P. N. Barnes

Abstract: The implementation of the 2nd generation high-Tc superconductors in power applications, such as electrical transformers, motors and generators requires superconducting wires that are superior to copper Litz wires at cryogenic temperatures in terms of losses in time-varying magnetic field, as well as in engineering current density. Another problem is to find a way to make practical coils and arma… ▽ More The implementation of the 2nd generation high-Tc superconductors in power applications, such as electrical transformers, motors and generators requires superconducting wires that are superior to copper Litz wires at cryogenic temperatures in terms of losses in time-varying magnetic field, as well as in engineering current density. Another problem is to find a way to make practical coils and armatures out of flat tape-like conductors with low bending strain tolerance. We discuss several novel approaches to the construction of coils and armatures based specifically on the properties of coated conductors manufactured today. △ Less

Submitted 13 September, 2005; originally announced September 2005.

Concept of Multiply Connected Superconducting Tapes

Authors: G. A. Levin, P. N. Barnes

Abstract: The possibility of a substantial reduction of weight and size of electrical generators is the main incentive behind the effort to develop superconducting armature windings based on coated conductors in the form of wide tapes with large aspect ratio. The main obstacle to the application of coated superconductors in stator windings is the large losses incurred due to the ac magnetic field produced… ▽ More The possibility of a substantial reduction of weight and size of electrical generators is the main incentive behind the effort to develop superconducting armature windings based on coated conductors in the form of wide tapes with large aspect ratio. The main obstacle to the application of coated superconductors in stator windings is the large losses incurred due to the ac magnetic field produced by the rotor's dc coils of the field windings. In the range of frequencies typical for aircraft generators, the hysteretic losses in wide tapes are unacceptably high. They can be reduced by dividing the superconducting layer into multiple filaments separated by non-superconducting barriers. However, the lack of current sharing between the filaments makes the conductor vulnerable to the localized defects, so that a single blockage can impede the flow of transport current through the whole length of a given filament. We present estimates of reliability as well as the magnetization losses in multiply connected superconductors. In this type of superconducting tape, a sparse network of superconducting bridges, which allows for current sharing, connects the filaments. The trade-off between the different types of losses and the connectivity requirement imposes restrictions on the number of filaments and properties of the network of bridges. △ Less

Submitted 16 November, 2004; originally announced November 2004.

Comments: 4 pages, 3 figures

Magnetization Losses in Multifilament Coated Superconductors

Authors: G. A. Levin, P. N. Barnes, N. Amemiya, S. Kasai, K. Yoda, Z. Jiang

Abstract: We report the results of a study of the magnetization losses in experimental multifilament, as well as control (uniform), coated superconductors exposed to time-varying magnetic field of various frequencies. Both the hysteresis loss, proportional to the sweep rate of the applied magnetic field, and the coupling loss, proportional to the square of the sweep rate, have been observed. A scaling is… ▽ More We report the results of a study of the magnetization losses in experimental multifilament, as well as control (uniform), coated superconductors exposed to time-varying magnetic field of various frequencies. Both the hysteresis loss, proportional to the sweep rate of the applied magnetic field, and the coupling loss, proportional to the square of the sweep rate, have been observed. A scaling is found that allows us to quantify each of these contributions and extrapolate the results of the experiment beyond the envelope of accessible field amplitude and frequency. The combined loss in the multifilament conductor is reduced by about 90% in comparison with the uniform conductor at full field penetration at sweep rate as high as 3T/s. △ Less

Submitted 9 September, 2004; originally announced September 2004.

Phenomenology of Conduction in Incoherent Layered Crystals

Authors: George A. Levin

Abstract: A novel phenomenological approach to the analysis of the conductivities of incoherent layered crystals is presented. It is based on the fundamental relationship between the resistive anisotropy $σ_{ab}/σ_c$ and the ratio of the phase coherence lengths in the respective directions. We explore the model-independent consequences of a general assumption that the out-of-plane phase coherence length o… ▽ More A novel phenomenological approach to the analysis of the conductivities of incoherent layered crystals is presented. It is based on the fundamental relationship between the resistive anisotropy $σ_{ab}/σ_c$ and the ratio of the phase coherence lengths in the respective directions. We explore the model-independent consequences of a general assumption that the out-of-plane phase coherence length of single electrons is a short fixed distance of the order of interlayer spacing. Several topics are discussed: application of the scaling theory, magnetoresistivity, the effects of substitutions and the intermediate regime of conduction when both coherence lengths change with temperature, but at different rate. △ Less

Submitted 10 August, 2004; originally announced August 2004.

Comments: Scheduled to appear in August 1, 2004 issue of Phys. Rev. B

Laser Micromachining of Coated YBa2Cu3O6+x Superconducting Thin Films

Authors: Kenneth E. Hix, Matthew C. Rendina, James L. Blackshire, George A. Levin

Abstract: Over the last decade advances in high temperature superconducting (HTS) materials have generated a renewed optimism in the use of this technology in future high-power applications including motors, generators, and power transmission. The most promising superconducting material, YBa2Cu3O6+x (YBCO), has demonstrated current density capacity as high as 106 A/cm2 and is typically deposited epitaxial… ▽ More Over the last decade advances in high temperature superconducting (HTS) materials have generated a renewed optimism in the use of this technology in future high-power applications including motors, generators, and power transmission. The most promising superconducting material, YBa2Cu3O6+x (YBCO), has demonstrated current density capacity as high as 106 A/cm2 and is typically deposited epitaxially as a thin film on a buffered metallic substrate. The coated conductor architecture Ag/YBCO/Buffer/Ni-based substrate, as does other heteromaterials, introduces unique challenges to the laser micromachining process. In the present study, optimization of the laser micromachining process for machining grooves extending through the YBCO into the buffer layer is considered. A frequency tripled diode-pumped solid-state Nd:YVO4 laser at 355 nm is used in conjunction with both fixed and scanning optical systems. The dependence of cut quality, dimension, and local damage to the YBCO layer on the laser processing parameters including focal spot size, pulse overlap, and fluence will be discussed. Preliminary experimental results indicate that laser micromachining may be used as a reliable process for patterning of superconducting tapes. △ Less

Submitted 14 June, 2004; originally announced June 2004.

Comments: Paper submitted to the Great Lakes Photonics Symposium, Cleveland, Ohio (June 7-11, 2004)

Magnetotransport Mechanisms in Strongly Underdoped YBa_2Cu_3O_x Single Crystals

Authors: E. Cimpoiasu, G. A. Levin, C. C. Almasan, A. P. Paulikas, B. W. Veal

Abstract: We report magnetoresistivity measurements on strongly underdoped YBa_2Cu_3O_x (x=6.25, 6.36) single crystals in applied magnetic fields H || c-axis. We identify two different contributions to both in-plane and out-of-plane magnetoresistivities. The first contribution has the same sign as the temperature coefficient of the resistivity \partial ln(ρ_i)/\partial T (i={c,ab}). This contribution refl… ▽ More We report magnetoresistivity measurements on strongly underdoped YBa_2Cu_3O_x (x=6.25, 6.36) single crystals in applied magnetic fields H || c-axis. We identify two different contributions to both in-plane and out-of-plane magnetoresistivities. The first contribution has the same sign as the temperature coefficient of the resistivity \partial ln(ρ_i)/\partial T (i={c,ab}). This contribution reflects the incoherent nature of the out-of-plane transport. The second contribution is positive, quadratic in field, with an onset temperature that correlates to the antiferromagnetic ordering. △ Less

Submitted 26 September, 2001; originally announced September 2001.

Comments: 4 pages, 3 figures

Journal ref: Phys. Rev. B 64, 104514 (2001)

Magnetoconductivity due to Quantum Interference in Strongly Underdoped YBa_2Cu_3O_x

Authors: E. Cimpoiasu, G. A. Levin, C. C. Almasan, Hong Zheng, B. W. Veal

Abstract: We report magnetoconductivity measurements on YBa_2Cu_3O_x (x=6.25 and 6.36) single crystals. Our main result is that both the in-plane Delta_sigma_ab and out-of-plane Delta_sigma_c magnetoconductivities exhibit the field dependence characteristic of "two-dimensional" quantum interference in applied magnetic fields H parallel to the c-axis. Namely, Delta_sigma_c,ab are proportional to ln(H/H_0),… ▽ More We report magnetoconductivity measurements on YBa_2Cu_3O_x (x=6.25 and 6.36) single crystals. Our main result is that both the in-plane Delta_sigma_ab and out-of-plane Delta_sigma_c magnetoconductivities exhibit the field dependence characteristic of "two-dimensional" quantum interference in applied magnetic fields H parallel to the c-axis. Namely, Delta_sigma_c,ab are proportional to ln(H/H_0), with Delta_sigma_c/sigma_c substantially greater than Delta_sigma_ab/sigma_ab. We interpret this result as evidence of interlayer incoherence in these crystals, so that the phase-coherent trajectories are mostly confined to one bilayer. △ Less

Submitted 3 April, 2001; originally announced April 2001.

Comments: 9 pages, 5 figures

Journal ref: PRB 63, 104515 (2001)

New Software for Measurements of the Anisotropic Resistivity by Multiterminal Technique

Authors: G. A. Levin, D. A. Chernikov

Abstract: We present an overview of the capabilities of a new software developed for use with multiterminal measurements. The program supports two configurations of current and voltage contacts known in the parlance of the field as "flux transformer" and " I$\|$c" geometries. The problem of instability of the results obtained by the multiterminal method and the ways to overcome it is also discussed. We present an overview of the capabilities of a new software developed for use with multiterminal measurements. The program supports two configurations of current and voltage contacts known in the parlance of the field as "flux transformer" and " I$\|$c" geometries. The problem of instability of the results obtained by the multiterminal method and the ways to overcome it is also discussed. △ Less

Submitted 29 February, 2000; originally announced February 2000.

Comments: 2 pages; more information on http://www.virtinst.com

Dynamics of Flux Creep in Underdoped Single Crystals of Y_1-xPr_xBa_2Cu_3O_7-d

Authors: T. Stein, G. A. Levin, C. C. Almasan, D. A. Gajewski, M. B. Maple

Abstract: Transport as well as magnetic relaxation properties of the mixed state were studied on strongly underdoped Y_1-xPr_xBa_2Cu_3O_7-d crystals. We observed two correlated phenomena - a coupling transition and a transition to quantum creep. The distribution of transport current below the coupling transition is highly nonuniform, which facilitates quantum creep. We speculate that in the mixed state be… ▽ More Transport as well as magnetic relaxation properties of the mixed state were studied on strongly underdoped Y_1-xPr_xBa_2Cu_3O_7-d crystals. We observed two correlated phenomena - a coupling transition and a transition to quantum creep. The distribution of transport current below the coupling transition is highly nonuniform, which facilitates quantum creep. We speculate that in the mixed state below the coupling transition, where dissipation is nonohmic, the current distribution may be unstable with respect to self-channeling resulting in the formation of very thin current-carrying layers. △ Less

Submitted 12 October, 1999; originally announced October 1999.

Comments: 11 pages, 9 figures, Submitted to Phys. Rev. B

Relationship Between Conductivity and Phase Coherence Length in Cuprates

Authors: C. C. Almasan, G. A. Levin, E. Cimpoiasu, T. Stein, C. L. Zhang, M. C. Deandrade, M. B. Maple, Hong Zheng, A. P. Paulikas, B. W. Veal

Abstract: The large ($10^2 - 10^5$) and strongly temperature dependent resistive anisotropy $η= (σ_{ab}/σ_c)^{1/2}$ of cuprates perhaps holds the key to understanding their normal state in-plane $σ_{ab}$ and out-of-plane $σ_{c}$ conductivities. It can be shown that $η$ is determined by the ratio of the phase coherence lengths $\ell_i$ in the respective directions: $σ_{ab}/σ_c = \ell_{ab}^2/\ell_{c}^2$. In… ▽ More The large ($10^2 - 10^5$) and strongly temperature dependent resistive anisotropy $η= (σ_{ab}/σ_c)^{1/2}$ of cuprates perhaps holds the key to understanding their normal state in-plane $σ_{ab}$ and out-of-plane $σ_{c}$ conductivities. It can be shown that $η$ is determined by the ratio of the phase coherence lengths $\ell_i$ in the respective directions: $σ_{ab}/σ_c = \ell_{ab}^2/\ell_{c}^2$. In layered crystals in which the out-of-plane transport is incoherent, $\ell_{c}$ is fixed, equal to the interlayer spacing. As a result, the T-dependence of $η$ is determined by that of $\ell_{ab}$, and vice versa, the in-plane phase coherence length can be obtained directly by measuring the resistive anisotropy. We present data for hole-doped $YBa_2Cu_3O_y$ ($6.3 < y < 6.9$) and $Y_{1-x}Pr_xBa_2Cu_3O_{7-δ}$ ($0 < x \leq 0.55$) and show that $σ_{ab}$ of crystals with different doping levels can be well described by a two parameter universal function of the in-plane phase coherence length. In the electron-doped $Nd_{2-x}Ce_{x}CuO_{4-y}$, the dependence $σ_{ab}(η)$ indicates a crossover from incoherent to coherent transport in the c-direction. △ Less

Submitted 1 October, 1999; originally announced October 1999.

Comments: 5 pages, 2 figures

Is There a Unified Description of Conductivity of Layered Cuprates ?

Authors: C. C. Almasan, E. Cimpoiasu, G. A. Levin, H. Zheng, A. P. Paulikas, B. W. Veal

Abstract: We present a novel approach to the analysis of the normal state in-plane $σ_{ab}$ and out-of-plane $σ_{c}$ conductivities of anisotropic layered crystals such as oxygen deficient $YBa_{2}Cu_{3}O_{x}$. It can be shown that the resistive anisotropy is determined by the ratio of the phase coherence lengths in the respective directions; i.e., $σ_{ab}/σ_c=\ell_{ab}^2/\ell_c^2$. From the idea that at… ▽ More We present a novel approach to the analysis of the normal state in-plane $σ_{ab}$ and out-of-plane $σ_{c}$ conductivities of anisotropic layered crystals such as oxygen deficient $YBa_{2}Cu_{3}O_{x}$. It can be shown that the resistive anisotropy is determined by the ratio of the phase coherence lengths in the respective directions; i.e., $σ_{ab}/σ_c=\ell_{ab}^2/\ell_c^2$. From the idea that at all doping levels and temperatures $T$ the out-of-plane transport in these crystals is incoherent, follows that $\ell_c$ is T-independent, equal to the spacing $\ell_0$ between the neighboring bilayers. Thus, the T-dependence of $\ell_{ab}$ is given by the measured anisotropy, and $σ_{ab}(\ell_{ab})$ dependence is obtained by plotting $σ_{ab}$ vs $\ell=(σ_{ab}/σ_c)^{1/2}\ell_0$. The analysis of several single crystals of $YBa_{2}Cu_{3}O_{x}$ ($6.35<x<6.93$) shows that for all of them $σ_{ab}(\ell)$ is described by a universal dependence $σ_{ab}/\barσ=f(\ell/\bar\ell)$ with doping dependent parameters $\barσ$ and $\bar\ell$. △ Less

Submitted 23 August, 1999; v1 submitted 16 August, 1999; originally announced August 1999.

Comments: 5 pages, 2 figures. To be published in J. Low Temp. Phys. Proceedings of MOS-99, Stockholm. Prompted by inquiries from readers, several clarifications are introduced: Temperature range over which data were taken is indicated; a misleading typo in the sentence at the bottom of page 3 is corrected; a few minor grammatical changes have been made

Conductivity of Layered Crystals

Authors: G. A. Levin, C. C. Almasan

Abstract: We show that the resistive anisotropy of an anisotropic medium is determined by the ratio of the phase coherence lengths. In layered crystals in which the interlayer transport is incoherent, the out-of-plane phase coherence length is fixed and temperature independent. This leads to a temperature dependent resistive anisotropy and to the coexistence of metallic in-plane and non-metallic out-of-pl… ▽ More We show that the resistive anisotropy of an anisotropic medium is determined by the ratio of the phase coherence lengths. In layered crystals in which the interlayer transport is incoherent, the out-of-plane phase coherence length is fixed and temperature independent. This leads to a temperature dependent resistive anisotropy and to the coexistence of metallic in-plane and non-metallic out-of-plane conductivities. Our approach provides a description of the c-axis conductivity in the highly nonclassical regime, characteristic of layered cuprates. △ Less

Submitted 20 July, 1999; originally announced July 1999.

Comments: 5 pages and 1 figure

Quantum Creep in Y_{1-x}Pr_{x}Ba_{2}Cu_{3}O_{7}$ Crystals: Magnetic Relaxation and Transport

Authors: T. Stein, G. A. Levin, C. C. Almasan, D. A. Gajewski, M. B. Maple

Abstract: We report transport and magnetic relaxation measurements in the mixed state of strongly underdoped Y_{1-x}Pr_{x}Ba_{2}Cu_{3}O_{7} crystals. A transition from thermally activated flux creep to temperature independent quantum flux creep is observed in both transport and magnetic relaxation at temperatures T * 5 K. Flux transformer measurements indicate that the crossover to quantum creep is preced… ▽ More We report transport and magnetic relaxation measurements in the mixed state of strongly underdoped Y_{1-x}Pr_{x}Ba_{2}Cu_{3}O_{7} crystals. A transition from thermally activated flux creep to temperature independent quantum flux creep is observed in both transport and magnetic relaxation at temperatures T * 5 K. Flux transformer measurements indicate that the crossover to quantum creep is preceded by a coupling transition. Based on these observations we argue that below the coupling transition the current is confined within a very narrow layer beneath the current contacts. △ Less

Submitted 9 February, 1999; v1 submitted 4 February, 1999; originally announced February 1999.

Comments: 5 Pages, 3 figures