Showing 1–2 of 2 results for author: Lepienski, C M
-
Nanosized precipitates in H13 tool steel low temperature plasma nitriding
Authors:
L. F. Zagonel,
J. Bettini,
R. L. O. Basso,
P. Paredez,
H. Pinto,
C. M. Lepienski,
F. Alvarez
Abstract:
A comprehensive study of pulsed nitriding in AISI H13 tool steel at low temperature (400°C) is reported for several durations. X-ray diffraction results reveal that a nitrogen enriched compound (Epsilon-Fe2-3N, iron nitride) builds up on the surface within the first process hour despite the low process temperature. Beneath the surface, X-ray Wavelength Dispersive Spectroscopy (WDS) in a Scanning E…
▽ More
A comprehensive study of pulsed nitriding in AISI H13 tool steel at low temperature (400°C) is reported for several durations. X-ray diffraction results reveal that a nitrogen enriched compound (Epsilon-Fe2-3N, iron nitride) builds up on the surface within the first process hour despite the low process temperature. Beneath the surface, X-ray Wavelength Dispersive Spectroscopy (WDS) in a Scanning Electron Microscope (SEM) indicates relatively higher nitrogen concentrations (up to 12 at.%) within the diffusion layer while microscopic nitrides are not formed and existing carbides are not dissolved. Moreover, in the diffusion layer, nitrogen is found to be dispersed in the matrix and forming nanosized precipitates. The small coherent precipitates are observed by High-Resolution Transmission Electron Microscopy (HR-TEM) while the presence of nitrogen is confirmed by electron energy loss spectroscopy (EELS). Hardness tests show that the material hardness increases linearly with the nitrogen concentration, reaching up to 14.5 GPa in the surface while the Young Modulus remains essentially unaffected. Indeed, the original steel microstructure is well preserved even in the nitrogen diffusion layer. Nitrogen profiles show a case depth of about ~43 microns after nine hours of nitriding process. These results indicate that pulsed plasma nitriding is highly efficient even at such low temperatures and that at this process temperature it is possible to form thick and hard nitrided layers with satisfactory mechanical properties. This process can be particularly interesting to enhance the surface hardness of tool steels without exposing the workpiece to high temperatures and altering its bulk microstructure.
△ Less
Submitted 28 August, 2012;
originally announced August 2012.
-
Depth-Sensing Indentation on REBa2Cu3O(7-δ) Single Crystals obtained from Xenotime Mineral
Authors:
Francisco Carlos Serbena,
Carlos Eugênio Foerster,
Alcione Roberto Jurelo,
Alexandre Mikowski,
Pedro Rodrigues Júnior,
Célia Regina Carubelli,
Carlos Maurício Lepienski
Abstract:
A natural mixture of heavy rare earths oxides extracted from xenotime mineral have been used to prepare large single crystals of high-temperature REBa2Cu3O(7-δ) superconductor grown using the CuO-BaO self-flux method. Its mechanical properties along the ab-plane were characterized using instrumented indentation. Hardness and elastic modulus were obtained by the Oliver and Pharr method and correspo…
▽ More
A natural mixture of heavy rare earths oxides extracted from xenotime mineral have been used to prepare large single crystals of high-temperature REBa2Cu3O(7-δ) superconductor grown using the CuO-BaO self-flux method. Its mechanical properties along the ab-plane were characterized using instrumented indentation. Hardness and elastic modulus were obtained by the Oliver and Pharr method and corresponds to 7.4 \pm 0.2 GPa and in range 135-175 GPa at small depths, respectively. Increasing the load promotes the nucleation of lateral cracks that causes a decrease in hardness and the measured elastic modulus by instrumented indentation at higher loads. The indentation fracture toughness was estimated by measuring the radial crack length from cube-corner indentations at various loads and was 0.8 \pm 0.2 MPa.m1/2. The observed slip systems of REBa2Cu3O(7-δ) single crystals were [100](001) and [010](001), the same as for YBa2Cu3O(7-δ) single crystals. The initial stages of deformation and fracture in the indentation process were investigated. The hardness and elastic modulus were not strongly modified by the crystallographic orientation in the ab-plane. This was interpreted in terms of the resolved shear stresses in the active slip systems. Evidence of cracking along the {100} and {110} planes on the ab-plane was observed. As a conclusion, the mechanical properties of REBa2Cu3O(7-δ) single crystals prepared from xenotime are equivalent to those of YBa2Cu3O(7-δ) single crystals produced by conventional rare earths oxides.
△ Less
Submitted 30 May, 2012;
originally announced May 2012.