Pressure-induced structural disordering and anomalous pressure-volume behaviour in high-entropy zirconates
Authors:
Yogendar Singh,
Xinghua Su,
Vivek Kumar,
H. K. Poswal,
K. K. Pandey,
Pawan Kumar Kulriya
Abstract:
The ambient-temperature high-pressure behaviour of (La0.2Nd0.2Sm0.2Gd0.2Yb0.2)2Zr2O7 zirconate (HEZ) nanopowders with three different average particle sizes (~25nm, ~45 nm and ~ 68nm) were studied using synchrotron X-ray diffraction (SR-XRD) measurements up to ~30 GPa. Smaller particle-size HEZ nanopowder (~25 nm), synthesized at the lower sintering temperature, exhibits pure defect-fluorite (DF)…
▽ More
The ambient-temperature high-pressure behaviour of (La0.2Nd0.2Sm0.2Gd0.2Yb0.2)2Zr2O7 zirconate (HEZ) nanopowders with three different average particle sizes (~25nm, ~45 nm and ~ 68nm) were studied using synchrotron X-ray diffraction (SR-XRD) measurements up to ~30 GPa. Smaller particle-size HEZ nanopowder (~25 nm), synthesized at the lower sintering temperature, exhibits pure defect-fluorite (DF) phase, whereas larger particle-size HEZ nanopowders (~45nm and ~68nm), synthesized at the higher sintering temperature, exhibit mixture of DF and pyrochlore phase (PY). The phase fraction of the PY phase increases with sintering temperature and hence with the particle size. All the HEZ nanopowders exhibit stability of initial structures (DF and PY) up to ~ 30 GPa, though phase fraction of PY phase in larger particle-size HEZ nanopowders successively reduces with pressure which is concomitant with significant variation in ox48f fractional coordinate in PY phase. Both the phases in all the studied samples exhibit anomalous pressure-volume (P-V) behaviour between ~7 to 15 GPa. The anomaly decreases with increasing particle size of HEZ nanopowders. The variation of bond lengths and polyhedron volume with pressure suggests that the anomalous P-V behaviour and structural changes at high pressures are primarily due to the distortion of the polyhedrons in DF and PY structures in HEZ nanopowders.
△ Less
Submitted 2 June, 2025;
originally announced June 2025.
-
Investigation of charge carrier dynamics in Ti3C2Tx MXene for ultrafast photonics applications
Authors:
Ankita Rawat,
Nitesh K. Chourasia,
Saurabh K. Saini,
Gaurav Rajput,
Aditya Yadav,
Ritesh Kumar Chourasia,
Govind Gupta,
P. K. Kulriya
Abstract:
The rapid advancement of nanomaterials has paved the way for various technological breakthroughs, and MXenes, in particular, have gained substantial attention due to their unique properties such as high conductivity, broad-spectrum absorption strength, and tunable band gap. This article presents the impact of the process parameters on the structural and optical properties of Ti3C2Tx MXene for appl…
▽ More
The rapid advancement of nanomaterials has paved the way for various technological breakthroughs, and MXenes, in particular, have gained substantial attention due to their unique properties such as high conductivity, broad-spectrum absorption strength, and tunable band gap. This article presents the impact of the process parameters on the structural and optical properties of Ti3C2Tx MXene for application in ultrafast dynamics. XRD along with Raman spectroscopy studies, confirmed the synthesis of a single phase from their MAX phase Ti3AlC2. The complete etching of Al and increase in the interplanar distance is also observed on centrifugation at very high speed. The ultrafast transient absorption spectroscopy used to understand the effect of centrifuge speed on the charge carrier dynamics and ultrafast spectrum of MXene displayed that the carrier lifetime is critically influenced by rotation per minute (rpm) e.g. faster decay lifetime at 10k rpm than 7k rpm. The electronic relaxation probed using the time-resolved photoluminescence (TRPL) technique exhibits an average decay time of 5.13 ns and 5.35 ns at the 7k and 10k rpm, respectively, which confirms that the optical properties of the MXene are strongly affected by the centrifuge speed. The synthesized MXene at 10k rpm typically suggests that radiative processes due to longer decay lifetime and experiences fewer nonradiative losses, resulting in enhanced luminescence properties.
△ Less
Submitted 16 August, 2023;
originally announced August 2023.
-
Grain boundary and defects assisted thermal conductivity of nano-crystalline Gd2Ti2O7 Pyrochlore
Authors:
Yogendar Singh,
Vivek Kumar,
Saurabh Kumar Sharma,
Pawan Kumar Kulriya
Abstract:
The thermal conductivity study on the pyrochlore structured ceramics is important for utilization of these materials as an inert matrix fuel, electrolytes for oxide fuel cell and thermal barrier coating. The impact of porosity, structural defects and boundary scattering on thermal properties of the nanocrystalline Gd2Ti2O7 fabricated by spark plasma sintering followed by high energy ball milling h…
▽ More
The thermal conductivity study on the pyrochlore structured ceramics is important for utilization of these materials as an inert matrix fuel, electrolytes for oxide fuel cell and thermal barrier coating. The impact of porosity, structural defects and boundary scattering on thermal properties of the nanocrystalline Gd2Ti2O7 fabricated by spark plasma sintering followed by high energy ball milling has been investigated. The thermal conductivity has been measured in the temperature range from room temperature to 900 C using laser flash apparatus (LFA), and results were discussed by including several phenomena contributing to the thermal transmission in nc-pyrochlore in support of the scattering mechanism. A systematic decrease in thermal conductivity with reducing grain size can be understood by the phonon-pore scattering phenomenon. Furthermore, dominate of the boundary scattering on the thermal transmission with the increasing temperature is also observed. The experimentally determined values of thermal conductivity are compatible with the thermal insulation requirements for thermal barrier coating (TBC) applications
△ Less
Submitted 30 October, 2022;
originally announced October 2022.
-
Enhanced radiation tolerance of YSZ at high temperature against swift heavy ions: key role of interplay between material microstructure and irradiation temperature
Authors:
Parswajit Kalita,
Santanu Ghosh,
Udai B. Singh,
Pawan K. Kulriya,
Vinita Grover,
Rakesh Shukla,
A. K. Tyagi,
Gael Sattonnay,
Devesh K. Avasthi
Abstract:
Yttria stabilized Zirconia (YSZ) pellets with different crystallite sizes were irradiated with 80 MeV Ag$^{6+}$ ions at room temperature and 1000 K to understand the role of crystallite size/material microstructure and irradiation temperature on the radiation tolerance against high electronic energy loss (S$_e$). X-ray diffraction and Raman spectroscopy measurements reveal that, irrespective of th…
▽ More
Yttria stabilized Zirconia (YSZ) pellets with different crystallite sizes were irradiated with 80 MeV Ag$^{6+}$ ions at room temperature and 1000 K to understand the role of crystallite size/material microstructure and irradiation temperature on the radiation tolerance against high electronic energy loss (S$_e$). X-ray diffraction and Raman spectroscopy measurements reveal that, irrespective of the irradiation temperature, the nano-crystalline samples suffered more damage as compared to the bulk-like sample. A reduction in the irradiation damage i.e. improvement in the radiation tolerance, was observed for all the samples irradiated at 1000 K. The reduction in the damage, however, was remarkably higher for the two nano-crystalline samples compared to the bulk-like sample, and hence the difference in the damage between the bulk-like and nano-crystalline samples was also significantly lower at 1000 K than that at room temperature. The irradiation damage, against S$_e$, was thus found to be critically dependent on the interplay between the irradiation temperature and crystallite size. These results are explained with the help of detailed theoretical calculations/simulations based on the 'in-elastic thermal spike' model by taking into consideration the combined effect of crystallite size and environmental (irradiation) temperature on the electron-phonon coupling factor and lattice thermal conductivity (and hence on the resulting thermal spike). Our results are crucial from the fundamental perspective of comprehending the size and temperature dependent radiation damage against S$_e$ ; and also for a number of applications, in various radiation environments, where nano-materials are being envisioned for use.
△ Less
Submitted 27 July, 2018; v1 submitted 26 June, 2018;
originally announced June 2018.
-
Swift heavy ion irradiation induced structural phase transitions in BaTiO3: An in-situ x-ray diffraction study
Authors:
Ravindra Singh Solanki,
Jay Prakash Patel,
Chandana Rath,
Pawan Kumar Kulriya,
Devesh Kumar Avasthi,
Dhananjai Pandey
Abstract:
There is considerable controversy about swift heavy ion (SHI) irradiation induced displacive phase transitions in thermally insulating oxides. We present here unambiguous evidence for tetragonal to monoclinic and rhombohedral to monoclinic phase transitions in BaTiO3 under swift heavy ion irradiation (120MeV 108Ag+9 ions) using in-situ x-ray powder diffraction (XRPD) studies. The anomalous splitti…
▽ More
There is considerable controversy about swift heavy ion (SHI) irradiation induced displacive phase transitions in thermally insulating oxides. We present here unambiguous evidence for tetragonal to monoclinic and rhombohedral to monoclinic phase transitions in BaTiO3 under swift heavy ion irradiation (120MeV 108Ag+9 ions) using in-situ x-ray powder diffraction (XRPD) studies. The anomalous splitting/broadening of 111/222pc, 200pc and 220pc pseudocubic peaks for fluences greater than 3*1012 ions/cm2 reveal structural changes before amorphization at higher fluences. Lebail analysis of XRPD profiles confirm that the monoclinic phase is of MA type in the Cm space group. Shear stress for the structural phase transition is estimated to be ~ 430MPa, which we believe is generated as a result of stopping of the SHI.
△ Less
Submitted 7 March, 2017;
originally announced March 2017.