RF Surface Resistance of a HIPped MgB2 Sample at 21 GHz
Authors:
T. Tajima,
F. L. Krawczyk,
J. Liu,
D. C. Nguyen,
D. L. Schrage,
A. Serquis,
A. H. Shapiro,
V. F. Nesterenko,
Y. Gu
Abstract:
Magnesium diboride (MgB2) is attractive for RF cavity application for particle accelerators because it might not show an increase of RF surface losses at high magnetic surface fields, a phenomenon that has prevented high-Tc superconducting materials such as YBCO from being used for this application. We have measured the RF surface resistance (Rs) at 21 GHz of a MgB2 sample fabricated using Hot I…
▽ More
Magnesium diboride (MgB2) is attractive for RF cavity application for particle accelerators because it might not show an increase of RF surface losses at high magnetic surface fields, a phenomenon that has prevented high-Tc superconducting materials such as YBCO from being used for this application. We have measured the RF surface resistance (Rs) at 21 GHz of a MgB2 sample fabricated using Hot Isostatic Press (HIP) at 200 MPa and 1000 C. The results show that polishing with 0.1-micron diamond lapping film followed by a 1500-psi DI water rinse in a clean room reduced the Rs by a factor of 6.2 at 15 K and it is the lowest compared to other published data. The Rs data near the lowest temperature (~13 K) scatter between 0.6 and 1.3 mOhm. The penetration depth and energy gap were estimated to be 263 nm and 1.9-2.7, respectively, for the polished surface.
△ Less
Submitted 9 October, 2003;
originally announced October 2003.