Rapid Electron Backscatter Diffraction Mapping: Painting by Numbers
Authors:
Vivian S Tong,
Alexander J Knowles,
David Dye,
T Ben Britton
Abstract:
Microstructure characterisation has been greatly enhanced through the use of electron backscatter diffraction (EBSD), where rich maps are generated through analysis of the crystal phase and orientation in the scanning electron microscope (SEM). Conventional EBSD analysis involves raster scanning of the electron beam and the serial analysis of each diffraction pattern in turn. For grain shape, crys…
▽ More
Microstructure characterisation has been greatly enhanced through the use of electron backscatter diffraction (EBSD), where rich maps are generated through analysis of the crystal phase and orientation in the scanning electron microscope (SEM). Conventional EBSD analysis involves raster scanning of the electron beam and the serial analysis of each diffraction pattern in turn. For grain shape, crystallographic texture, and microstructure analysis this can be inefficient. In this work, we present Rapid EBSD, a data fusion approach combining forescatter electron (FSE) imaging with static sparse sampling of EBSD patterns. We segment the FSE image into regions of similar colour (i.e. phase and crystal orientation) and then collect representative EBSD data for each segmented region. This enables microstructural assessment to be performed at the spatial resolution of the (fast) FSE imaging whilst including orientation and phase information from EBSD analysis of representative points. We demonstrate the Rapid EBSD technique on samples of a cobalt based superalloy and a strained dual phase titanium alloy, comparing the results with conventional analysis. Rapid EBSD is advantageous for assessing grain size distributions in time-limited experiments.
△ Less
Submitted 13 November, 2018; v1 submitted 19 September, 2018;
originally announced September 2018.
The Kinetics of Primary Alpha Plate Growth in Titanium Alloys
Authors:
Abigail K Ackerman,
Alexander J. Knowles,
Hazel M. Gardner,
Andre A N Nemeth,
Ioannis Bantounas,
Anna Radecka,
Michael P. Moody,
Paul A. J. Bagot,
Roger C. Reed,
David Rugg,
David Dye
Abstract:
The kinetics of primary alpha-Ti colony/Widmanstatten plate growth from the beta are examined, comparing model to experiment. The plate growth velocity depends sensitively both on the diffusivity D(T) of the rate-limiting species and on the supersaturation around the growing plate. These result in a maxima in growth velocity around 40 K below the transus, once sufficient supersaturation is availab…
▽ More
The kinetics of primary alpha-Ti colony/Widmanstatten plate growth from the beta are examined, comparing model to experiment. The plate growth velocity depends sensitively both on the diffusivity D(T) of the rate-limiting species and on the supersaturation around the growing plate. These result in a maxima in growth velocity around 40 K below the transus, once sufficient supersaturation is available to drive plate growth. In Ti-6246, the plate growth velocity was found to be around 0.32 um min-1 at 850 oC, which was in good agreement with the model prediction of 0.36 um min-1 . The solute field around the growing plates, and the plate thickness, was found to be quite variable, due to the intergrowth of plates and soft impingement. This solute field was found to extend to up to 30 nm, and the interface concentration in the beta was found to be around 6.4 at.% Mo. It was found that increasing O content will have minimal effect on the plate lengths expected during continuous cooling; in contrast, Mo approximately doubles the plate lengths obtained for every 2 wt.% Mo reduction. Alloys using V as the beta stabiliser instead of Mo are expected to have much faster plate growth kinetics at nominally equivalent V contents. These findings will provide a useful tool for the integrated design of alloys and process routes to achieve tailored microstructures.
△ Less
Submitted 31 July, 2019; v1 submitted 24 May, 2018;