Towards engineering the perfect defect in high-performing permanent magnets
Authors:
S. Giron,
N. Polin,
E. Adabifiroozjaei,
Y. Yang,
A. Kovács,
T. P. Almeida,
D. Ohmer,
K. Üstüner,
A. Saxena,
M. Katter,
I. A. Radulov,
C. Freysoldt,
R. E. Dunin-Borkowski,
M. Farle,
K. Durst,
H. Zhang,
L. Alff,
K. Ollefs,
B. -X. Xu,
O. Gutfleisch,
L. Molina-Luna,
B. Gault,
K. P. Skokov
Abstract:
Permanent magnets draw their properties from a complex interplay, across multiple length scales, of the composition and distribution of their constituting phases, that act as building blocks, each with their associated intrinsic properties. Gaining a fundamental understanding of these interactions is hence key to decipher the origins of their magnetic performance and facilitate the engineering of…
▽ More
Permanent magnets draw their properties from a complex interplay, across multiple length scales, of the composition and distribution of their constituting phases, that act as building blocks, each with their associated intrinsic properties. Gaining a fundamental understanding of these interactions is hence key to decipher the origins of their magnetic performance and facilitate the engineering of better-performing magnets, through unlocking the design of the "perfect defects" for ultimate pinning of magnetic domains. Here, we deployed advanced multiscale microscopy and microanalysis on a bulk Sm2(CoFeCuZr)17 pinning-type high-performance magnet with outstanding thermal and chemical stability. Making use of regions with different chemical compositions, we showcase how both a change in the composition and distribution of copper, along with the atomic arrangements enforce the pinning of magnetic domains, as imaged by nanoscale magnetic induction mapping. Micromagnetic simulations bridge the scales to provide an understanding of how these peculiarities of micro- and nanostructure change the hard magnetic behaviour of Sm2(CoFeCuZr)17 magnets. Unveiling the origins of the reduced coercivity allows us to propose an atomic-scale defect and chemistry manipulation strategy to define ways toward future hard magnets.
△ Less
Submitted 4 June, 2023; v1 submitted 28 April, 2023;
originally announced April 2023.
-
Determining the First Order Character of La(Fe,Mn,Si)13
Authors:
Milan Bratko,
Edmund Lovell,
A. David Caplin,
Vittorio Basso,
Alexander Barcza,
Matthias Katter,
Lesley F. Cohen
Abstract:
Definitive determination of first order character of the magnetocaloric magnetic transition remains elusive. Here we use a microcalorimetry technique in two modes of operation to determine the contributions to entropy change from latent heat and heat capacity separately in an engineered set of La(Fe, Mn, Si)13 samples. We compare the properties extracted by this method with those determined using…
▽ More
Definitive determination of first order character of the magnetocaloric magnetic transition remains elusive. Here we use a microcalorimetry technique in two modes of operation to determine the contributions to entropy change from latent heat and heat capacity separately in an engineered set of La(Fe, Mn, Si)13 samples. We compare the properties extracted by this method with those determined using magnetometry and propose a model independent parameter that would allow the degree of first order character to be defined across different families of materials. The microcalorimetry method is sufficiently sensitive to allow observation of an additional peak feature in the low field heat capacity associated with the presence of Mn in these samples. The feature is of magnetic origin but is insensitive to magnetic field, explicable in terms of inhomogeneous occupancy of Mn within the lattice resulting in antiferromagnetic ordered Mn clusters.
△ Less
Submitted 3 October, 2016;
originally announced October 2016.
-
Magnetocaloric properties of LaFe$_{13-x-y}$Co$_x$Si$_y$ and commercial grade Gd
Authors:
R. Bjørk,
C. R. H. Bahl,
M. Katter
Abstract:
The magnetocaloric properties of three samples of LaFe$_{13-x-y}$Co$_x$Si$_y$ have been measured and compared to measurements of commercial grade Gd. The samples have (x=0.86, y=1.08), (x=0.94, y=1.01) and (x=0.97, y=1.07) yielding Curie temperatures in the range 276-288 K. The magnetization, specific heat capacity and adiabatic temperature change have been measured over a broad temperature interv…
▽ More
The magnetocaloric properties of three samples of LaFe$_{13-x-y}$Co$_x$Si$_y$ have been measured and compared to measurements of commercial grade Gd. The samples have (x=0.86, y=1.08), (x=0.94, y=1.01) and (x=0.97, y=1.07) yielding Curie temperatures in the range 276-288 K. The magnetization, specific heat capacity and adiabatic temperature change have been measured over a broad temperature interval. Importantly, all measurements were corrected for demagnetization, allowing the data to be directly compared. In an internal field of 1 T the maximum specific entropy changes were 6.2, 5.1 and 5.0 J/kg K, the specific heat capacities were 910, 840 and 835 J/kg K and the adiabatic temperature changes were 2.3, 2.1 and 2.1 K for the three LaFeCoSi samples respectively. For Gd in an internal field of 1 T the maximum specific entropy change was 3.1 J/kg K, the specific heat capacity was 340 J/kg K and the adiabatic temperature change was 3.3 K. The adiabatic temperature change was also calculated from the measured values of the specific heat capacity and specific magnetization and compared to the directly measured values. In general an excellent agreement was seen.
△ Less