Thermal-fluctuation mechanism of long-term corrosion of glass caused by internal stress: processes of depolymerization, impurity migration and fracturing on an atomic scale
Authors:
Irina F. Kadikova,
Tatyana V. Yuryeva,
Ekaterina A. Morozova,
Irina A. Grigorieva,
Ilya B. Afanasyev,
Vladimir Y. Karpenko,
Vladimir A. Yuryev
Abstract:
Long-term corrosion of glass is studied using polarising light microscopy, FTIR and SEM including EDX and elemental mapping. Early 19th century beads made of lead-potassium glass are the object of the study. Non-uniformly distributed internal stresses were introduced into the studied glass during bead manufacturing. Corrosion of 19th century bead glass has been shown to comprise several mutually c…
▽ More
Long-term corrosion of glass is studied using polarising light microscopy, FTIR and SEM including EDX and elemental mapping. Early 19th century beads made of lead-potassium glass are the object of the study. Non-uniformly distributed internal stresses were introduced into the studied glass during bead manufacturing. Corrosion of 19th century bead glass has been shown to comprise several mutually connected processes developing in parallel and intensifying one another. These processes are the depolymerization of glass, the directed migration of alkali-metal impurities and local glass leaching, and the nucleation of micro discontinuities followed by the formation of micro cracks and their gradual growth. In course of time, their cumulative and apparently synergistic effect results in glass fracturing terminated with bead crumbling into tiny discoloured particles. All these phenomena are controlled by the internal stress originated from the bead production process. Thus, the phenomenon of stressed bead glass corrosion is the process of the internal stress relaxation in glass through the nucleation and growth of cracks, which lasts for many decades at room temperature. It is dramatically accelerated when beads are heat treated. Annealing at 300°C for 15 min. is sufficient for artificial ageing of initially intact beads. The corrosion has been observed to occur in glass even if beads are kept in well-controlled museum environment. The local thermal-fluctuation mechanism is proposed to account for the corrosion phenomenon on an atomic scale. The approach based on the thermal-fluctuation mechanism is applicable to describe degradation and destruction processes in various solid substances and composite materials under stress; this approach enables understanding the phenomena of formation and degradation of nanostructures, e. g., heterostructures with quantum wells or quantum dots.
△ Less
Submitted 2 February, 2023; v1 submitted 3 January, 2022;
originally announced January 2022.
-
Crystals in the 19th century glass beads
Authors:
Irina F. Kadikova,
Tatyana V. Yuryeva,
Ekaterina A. Morozova,
Irina A. Grigorieva,
Maria V. Lukashova,
Ilya B. Afanasyev,
Andrey A. Kudryavtsev,
Vladimir A. Yuryev
Abstract:
Glass seed beads probably are the most numerous group of art historical glass. From the ancient times to the modern era, glass beads played an essential role in culture, as they were used, e.g., to decorate clothing, religious objects and functional tools, and served as an important good for global trade. The conservation state of items made of glass beads is an actual issue for curators and conse…
▽ More
Glass seed beads probably are the most numerous group of art historical glass. From the ancient times to the modern era, glass beads played an essential role in culture, as they were used, e.g., to decorate clothing, religious objects and functional tools, and served as an important good for global trade. The conservation state of items made of glass beads is an actual issue for curators and conservators. Glass, as well known, is often unstable material, so a number of internal and external factors are responsible for chemical and physical processes in glass and on the glass surface. It was noticed that some types of historical 19th century glass beads are subjected to more intense destruction than others. The samples of glass beads of different colours and conservation states were examined by means of SEM-EDX, EBSD, Raman and FTIR microspectroscopy. Research showed that some types of beads are characterized by the presence of nano- and microcrystals in glass, which could be one of the causes of glass destruction. The elemental composition of crystals is different in each case and depends on raw materials and technical components used for glass manufacturing. The structure of crystals was identified by means of EBSD analysis.
△ Less
Submitted 30 April, 2021; v1 submitted 28 April, 2021;
originally announced April 2021.
-
Identification of CaCuSi$_4$O$_{10}$ (Egyptian blue) in the "Birch. Spring" painting by Robert Falk (1907) using photoluminescence
Authors:
Svetlana A. Pisareva,
Irina N. Shibanova,
Irina F. Kadikova,
Ekaterina A. Morozova,
Tatyana V. Yuryeva,
Ilya B. Afanasyev,
Vladimir A. Yuryev
Abstract:
We have detected Egyptian blue pigment in the paint layer of the "Birch. Spring" painting by Robert Falk (1907); we have also found this pigment in the paints of the sketch drawn on the canvas back side. This is probably the first discovery of Egyptian blue in a 20th century work of art.
We have analyzed a modern commercial Egyptian blue pigment (Kremer) and found it to be suitable as a standard…
▽ More
We have detected Egyptian blue pigment in the paint layer of the "Birch. Spring" painting by Robert Falk (1907); we have also found this pigment in the paints of the sketch drawn on the canvas back side. This is probably the first discovery of Egyptian blue in a 20th century work of art.
We have analyzed a modern commercial Egyptian blue pigment (Kremer) and found it to be suitable as a standard for photoluminescence spectral analysis. The characteristic photoluminescence band of CaCuSi$_4$O$_{10}$ reaches maximum at the wavelength of about 910 nm. The luminescence is efficiently excited by incoherent green or blue light.
The study demonstrates that the photoluminescence spectral micro analysis using excitation by incoherent light can be efficiently used for the identification of luminescent pigments in paint layers of artworks.
△ Less
Submitted 11 June, 2021; v1 submitted 7 July, 2020;
originally announced July 2020.
-
Cathodoluminescence of CdZnSSe crystals synthesized in 19th century bead glass
Authors:
Tatyana V. Yuryeva,
Sergey A. Malykhin,
Andrey A. Kudryavtsev,
Ilya B. Afanasyev,
Irina F. Kadikova,
Vladimir A. Yuryev
Abstract:
The article presents an experimental investigation of band-edge cathodoluminescence of CdZnSSe crystals that nucleated and grew in silicate glass melt during its production. We have studied Zn-rich red glass made for manufacture of seed beads in the 19th century and found it to contain CdZnSSe crystals. Due to colloidal staining using the CdZnSSe crystallites embedded in glass, glass makers were e…
▽ More
The article presents an experimental investigation of band-edge cathodoluminescence of CdZnSSe crystals that nucleated and grew in silicate glass melt during its production. We have studied Zn-rich red glass made for manufacture of seed beads in the 19th century and found it to contain CdZnSSe crystals. Due to colloidal staining using the CdZnSSe crystallites embedded in glass, glass makers were enabled to produce lustrous red glass that, as we presently know, manifests bright luminescence. The CdZnSSe crystallites exhibit intense band-edge cathodoluminescence both at room temperature and at liquid nitrogen temperature. We have found the band-edge cathodoluminescence of these crystals to peak in the range from 2.00 to 2.03 eV at 300 K and from 2.02 to 2.06 eV at 80 K. We have also estimated the value of the band gap derivative d$E_g$/d$T$ in the interval from 80 to 300 K and found it to lie in the range from $-2.5 \times 10^{-4}$ to 0 eV/K. CdZnSSe crystals in glass demonstrate high temperature and temporal stability. The glass-crystal composite on their basis is resistant to the electron-beam irradiation and long-term weathering. Possible applications of this composite in modern technologies, and processes and components that might be used for making glass stained with CdZnSSe in the past are also discussed.
△ Less
Submitted 29 November, 2019; v1 submitted 30 January, 2019;
originally announced January 2019.
-
Study of deteriorating semiopaque turquoise lead-potassium glass beads at different stages of corrosion using micro-FTIR spectroscopy
Authors:
Irina F. Kadikova,
Ekaterina A. Morozova,
Tatyana V. Yuryeva,
Irina A. Grigorieva,
Vladimir A. Yuryev
Abstract:
Nowadays, a problem of historical beadworks conservation in museum collections is actual more than ever because of fatal corrosion of the 19th century glass beads. Vibrational spectroscopy is a powerful method for investigation of glass, namely, of correlation of the structure-chemical composition. Therefore, Fourier-transform infrared spectroscopy was used for examination of degradation processes…
▽ More
Nowadays, a problem of historical beadworks conservation in museum collections is actual more than ever because of fatal corrosion of the 19th century glass beads. Vibrational spectroscopy is a powerful method for investigation of glass, namely, of correlation of the structure-chemical composition. Therefore, Fourier-transform infrared spectroscopy was used for examination of degradation processes in cloudy turquoise glass beads, which in contrast to other color ones deteriorate especially strongly. Micro-X-ray fluorescence spectrometry of samples has shown that lead-potassium glass PbO-K$_2$O-SiO$_2$ with small amount of Cu and Sb was used for manufacture of cloudy turquoise beads. Fourier-transform infrared spectroscopy study of the beads at different stages of glass corrosion was carried out in the range from 200 to 4000 cm$^{-1}$ in the attenuated total reflection mode. In all the spectra, we have observed shifts of two major absorption bands to low-frequency range (~1000 and ~775 cm$^{-1}$) compared to ones typical for amorphous SiO2 (~1100 and 800 cm$^{-1}$, respectively). Such an effect is connected with Pb$^{2+}$ and K$^+$ appending to the glass network. The presence of a weak band at ~1630 cm$^{-1}$ in all the spectra is attributed to the adsorption of H$_2$O. After annealing of the beads, the band disappeared completely in less deteriorated samples and became significantly weaker in more destroyed ones. Based on that we conclude that there is adsorbed molecular water on the beads. However, products of corrosion (e.g., alkali in the form of white crystals or droplets of liquid alkali) were not observed on the glass surface. We have also observed glass depolymerisation in the strongly degraded beads, which is exhibited in domination of the band peaked at ~1000 cm$^{-1}$.
△ Less
Submitted 8 May, 2019; v1 submitted 23 May, 2017;
originally announced May 2017.
-
Crystallites in Color Glass Beads of the 19th Century and Their Influence on Fatal Deterioration of Glass
Authors:
E. A. Morozova,
I. F. Kadikova,
T. V. Yuryeva,
V. A. Yuryev
Abstract:
Glass corrosion is a crucial problem in keeping and conservation of beadworks in museums. All kinds of glass beads undergo deterioration but blue-green lead-potassium glass beads of the 19th century are subjected to the destruction to the greatest extent. Blue-green lead-potassium glass beads of the 19th century obtained from exhibits kept in Russian museums were studied with the purpose to determ…
▽ More
Glass corrosion is a crucial problem in keeping and conservation of beadworks in museums. All kinds of glass beads undergo deterioration but blue-green lead-potassium glass beads of the 19th century are subjected to the destruction to the greatest extent. Blue-green lead-potassium glass beads of the 19th century obtained from exhibits kept in Russian museums were studied with the purpose to determine the causes of the observed phenomenon. For the comparison, yellow lead beads of the 19th century were also explored. Both kinds of beads contain Sb but yellow ones are stable. Using scanning electron microscopy, energy dispersive X-ray microspectrometry, electron backscatter diffraction, transmission electron microscopy and X-ray powder analysis, we have registered the presence of crystallites of orthorhombic KSbOSiO$_4$ and cubic Pb$_2$Sb$_{1.5}$Fe$_{0.5}$O$_{6.5}$ in glass matrix of blue-green and yellow beads, respectively. Both compounds form at rather high temperatures obviously during glass melting and/or melt cooling. We suppose that the crystallites generate internal tensile strain in glass during its cooling which causes formation of multiple microcracks in inner domains of blue-green beads. We suggest that the deterioration degree depends on quantity of the precipitates, their sizes and their temperature coefficients of linear expansion. In blue-green beads, the crystallites are distributed in their sizes from $\sim\,$200 nm to several tens of $μ$m and tend to gather in large colonies. The sizes of crystallites in yellow beads are several hundreds of nm and their clusters contain few crystallites. This explains the difference in corrosion of these kinds of beads containing crystals of Sb compounds.
△ Less
Submitted 23 May, 2017;
originally announced May 2017.
-
KSbOSiO$_4$ microcrystallites as a source of corrosion of blue-green lead-potassium glass beads of the 19th century
Authors:
T. V. Yuryeva,
I. B. Afanasyev,
E. A. Morozova,
I. F. Kadikova,
V. S. Popov,
V. A. Yuryev
Abstract:
Presently, deterioration of glass beads is a significant problem in conservation and restoration of beaded exhibits in museums. Glass corrosion affects nearly all kinds of beads but cloudy blue-green ones are more than others subjected to disastrous destruction. However, physical and chemical mechanisms of this phenomenon have not been understood thus far. This article presents results of a study…
▽ More
Presently, deterioration of glass beads is a significant problem in conservation and restoration of beaded exhibits in museums. Glass corrosion affects nearly all kinds of beads but cloudy blue-green ones are more than others subjected to disastrous destruction. However, physical and chemical mechanisms of this phenomenon have not been understood thus far. This article presents results of a study of elemental and phase composition of glass of the blue-green beads of the 19th century obtained from exhibits kept in Russian museums. Using scanning electron microscopy, X-ray microanalysis and X-ray powder analysis we have detected and investigated Sb-rich microinclusions in the glass matrix of these beads and found them to be micro crystallites of KSbSiO$_5$. These crystallites were not detected in other kinds of beads which are much less subjected to corrosion than the blue-green ones and deteriorate in a different way. We belive that individual precipitates of KSbSiO$_5$ and especially their clusters play a major role in the blue-green bead deterioration giving rise to slow internal corrosion of the bead glass.
△ Less
Submitted 30 December, 2016; v1 submitted 7 September, 2016;
originally announced September 2016.