Structure, magnetic and transport properties of Ti-substituted La0.7Sr0.3MnO3
Authors:
M. S. Kim,
J. B. Yang,
Q. Cai,
X. D. Zhou,
W. J. James,
W. B. Yelon,
P. E. Parris,
D. Buddhikot,
S. K. Malik
Abstract:
Ti-substituted perovskites, La0.7Sr0.3Mn1-xTixO3, with x between 0 to 0.20, were investigated by neutron diffraction, magnetization, electric resistivity, and magnetoresistance (MR) measurements. All samples show a rhombohedral structure (space group R3c) from 10 K to room temperature. At room temperature, the cell parameters a, c and the unit cell volume increase with increasing Ti content. How…
▽ More
Ti-substituted perovskites, La0.7Sr0.3Mn1-xTixO3, with x between 0 to 0.20, were investigated by neutron diffraction, magnetization, electric resistivity, and magnetoresistance (MR) measurements. All samples show a rhombohedral structure (space group R3c) from 10 K to room temperature. At room temperature, the cell parameters a, c and the unit cell volume increase with increasing Ti content. However, at 10 K, the cell parameter a has a maximum value for x = 0.10, and decreases for x greater than 0.10, while the unit cell volume remains nearly constant for x greater than 0.10. The average (Mn,Ti)-O bond length increases up to x=0.15, and the (Mn,Ti)-O-(Mn,Ti) bond angle decreases with increasing Ti content to its minimum value at x=0.15 at room temperature. Below the Curie temperature T_C, the resistance exhibits metallic behavior for the x _ 0.05 samples. A metal (semiconductor) to insulator transition is observed for the x_ 0.10 samples. A peak in resistivity appears below T_C for all samples, and shifts to a lower temperature as x increases. The substitution of Mn by Ti decreases the 2p-3d hybridization between O and Mn ions, reduces the bandwidth W, and increases the electron-phonon coupling. Therefore, the TC shifts to a lower temperature and the resistivity increases with increasing Ti content. A field-induced shift of the resistivity maximum occurs at x less than or equal to 0.10. The maximum MR effect is about 70% for La0.7Sr0.3Mn0.8Ti0.2O3. The separation of TC and the resistivity maximum temperature Tmax enhances the MR effect in these compounds due to the weak coupling between the magnetic ordering and the resistivity as compared with La0.7Sr0.3MnO3.
△ Less
Submitted 9 February, 2005;
originally announced February 2005.
The effect of Cu-doping on the magnetic and transport properties of La0.7Sr0.3MnO3
Authors:
M. S. Kim,
J. B. Yang,
Q. Cai,
X. D. Zhou,
W. J. James,
W. B. Yelon,
P. E. Parris,
D. Buddhikot,
S. K. Malik
Abstract:
The effects of Cu-doping on the structural, magnetic, and transport properties of La0.7Sr0.3Mn1-xCuxO3 (0 < x < 0.20) have been studied using neutron diffraction, magnetization and magnetoresistance (MR) measurements. All samples show the rhombohedral structure with the R3c space-group from 10K to room temperature (RT). Neutron diffraction data suggest that some of the Cu ions have a Cu3+ state…
▽ More
The effects of Cu-doping on the structural, magnetic, and transport properties of La0.7Sr0.3Mn1-xCuxO3 (0 < x < 0.20) have been studied using neutron diffraction, magnetization and magnetoresistance (MR) measurements. All samples show the rhombohedral structure with the R3c space-group from 10K to room temperature (RT). Neutron diffraction data suggest that some of the Cu ions have a Cu3+ state in these compounds. The substitution of Mn by Cu affects the Mn-O bond length and Mn-O-Mn bond angle resulting from the minimization of the distortion of the MnO6 octahedron. Resistivity measurements show that a metal to insulator transition occurs for the x more than 0.15 samples. The x = 0.15 sample shows the highest MR(_80%), which might result from the co-existence of Cu3+/Cu2+ and the dilution effect of Cu-doping on the double exchange interaction.
△ Less
Submitted 9 February, 2005;
originally announced February 2005.
Growth and magnetic properties of MnO2−delta nanowire microspheres
Authors:
J. B. Yang,
X. D. Zhou,
W. J. James,
S. K. Malik,
C. S. Wang
Abstract:
We report the synthesis of MnO2−delta microspheres using hydrothermal and conventional chemical reaction methods. The microspheres of MnO2−delta consist of nanowires having a diameter of 20-50 nm and a length of 2-8 micro m. The value of the oxygen vacancy delta estimated from the x-ray photoelectron spectrum (XPS) is 0.3. The magnetization versus temperature curve indicates a magnet…
▽ More
We report the synthesis of MnO2−delta microspheres using hydrothermal and conventional chemical reaction methods. The microspheres of MnO2−delta consist of nanowires having a diameter of 20-50 nm and a length of 2-8 micro m. The value of the oxygen vacancy delta estimated from the x-ray photoelectron spectrum (XPS) is 0.3. The magnetization versus temperature curve indicates a magnetic transition at about 13 K. It is found that a parasitic ferromagnetic component is imposed on the antiferromagnetic structure of MnO2−delta, which might result from distortion of the lattice structure due to oxygen vacancies. The magnetic transition temperature TN is about 10 K lower than that of the bulk MnO2 single crystal.
△ Less
Submitted 14 September, 2004;
originally announced September 2004.