Complex magnetic interactions and critical behavior analysis in quaternary CoFeV$_{0.8}$Mn$_{0.2}$Si Heusler alloy
Authors:
Guru Dutt Gupt,
P. D. Babu,
R. S. Dhaka
Abstract:
We investigate the magnetic behavior and critical exponents of quaternary CoFeV$_{0.8}$Mn$_{0.2}$Si Heusler alloy to understand the interactions across the Curie temperature ($T_{\rm C}$). The Rietveld refinement of the x-ray diffraction pattern with the space group F$\bar{4}$3m confirms a single-phase cubic Y-type crystal structure. The magnetic susceptibility $χ(T)$ data show a ferromagnetic nat…
▽ More
We investigate the magnetic behavior and critical exponents of quaternary CoFeV$_{0.8}$Mn$_{0.2}$Si Heusler alloy to understand the interactions across the Curie temperature ($T_{\rm C}$). The Rietveld refinement of the x-ray diffraction pattern with the space group F$\bar{4}$3m confirms a single-phase cubic Y-type crystal structure. The magnetic susceptibility $χ(T)$ data show a ferromagnetic nature with a second-order phase transition from paramagnetic to ferromagnetic at $446\pm1$~K. The saturation magnetization at 5~K is determined to be 2.2~$μ_B$/f.u., which found to be close to the Slater--Pauling rule and indicates its half-metallic nature. The values of asymptotic critical exponents ($β$, $γ$, and $δ$) and the $T_{\rm C}$ are extracted through detailed analytical analysis including the Modified Arrott plot, the Kouvel-Fisher (K--F) method, and the Widom scaling relation. Interestingly, the estimated values of $β$ = 0.369 and $γ$ = 1.445 closely approximate the theoretical values of the 3D Heisenberg model and second-order thermodynamic phase transition across the $T_{\rm C}$. The obtained exponents lead to the collapse of renormalized isotherms, represented by the relationship between the magnetization (m) and the applied magnetic field (h), into two distinct branches above and below the $T_{\rm C}$, which validates the reliability of the analysis. Furthermore, these exponents suggest that the spin interaction follows a decay pattern of $J(r) \sim r^{-4.99}$, indicating a short-range magnetic ordering, akin to the itinerant-electron 3D Heisenberg model.
△ Less
Submitted 3 October, 2023;
originally announced October 2023.
-
Unveiling the magnetic structure and phase transition of Cr$_2$CoAl using neutron diffraction
Authors:
Guru Dutt Gupt,
Yousef Kareri,
James Hester,
Clemens Ulrich,
R. S. Dhaka
Abstract:
We report the detailed analysis of temperature dependent neutron diffraction pattern of the Cr$_2$CoAl inverse Heusler alloy and unveil the magnetic structure up to the phase transition as well as its fully compensated ferrimagnetic nature. The Rietveld refinement of the diffraction pattern using the space group I$\bar4${\it m}2 confirm the inverse tetragonal structure over the large temperature r…
▽ More
We report the detailed analysis of temperature dependent neutron diffraction pattern of the Cr$_2$CoAl inverse Heusler alloy and unveil the magnetic structure up to the phase transition as well as its fully compensated ferrimagnetic nature. The Rietveld refinement of the diffraction pattern using the space group I$\bar4${\it m}2 confirm the inverse tetragonal structure over the large temperature range from 100~K to 900~K. The refinement of the magnetic phase considering the wave vector $k=$ (0, 0, 0) reveals the ferrimagnetic nature of the sample below 730$\pm$5~K. This transition temperature is obtained from empirical power law fitting of the variation in the ordered net magnetic moment and intensity of (110) peak as a function of temperature. The spin configuration of the microscopic magnetic structure suggests the nearly fully compensated ferrimagnetic behavior where the magnetic moments of Cr2 are antiparallel with respect to the Cr1, and Co moments. Moreover, the observed anomaly in the thermal expansion and lattice parameters at 730$\pm$5~K suggest that the distortion in crystal structure may play an important role in the magnetic phase transition.
△ Less
Submitted 21 March, 2023;
originally announced March 2023.
-
High temperature dielectric and impedance spectroscopy study of LaCo$_{0.7}$Nb$_{0.3}$O$_3$
Authors:
Vikas N. Thakur,
Ajay Kumar,
Aakash Kaushik,
Guru Dutt Gupt,
Rajendra S. Dhaka
Abstract:
We report the high temperature dielectric and {\it ac} impedance spectroscopy investigation of Nb substituted LaCo$_{0.7}$Nb$_{0.3}$O$_3$ polycrystalline sample. The maximum dielectric constant value was observed $\approx$1400 at around 400~K where the peak value shows a decreasing trend at higher temperatures and frequency. Similar variation was reflected in the dielectric loss (tan$δ$) behavior…
▽ More
We report the high temperature dielectric and {\it ac} impedance spectroscopy investigation of Nb substituted LaCo$_{0.7}$Nb$_{0.3}$O$_3$ polycrystalline sample. The maximum dielectric constant value was observed $\approx$1400 at around 400~K where the peak value shows a decreasing trend at higher temperatures and frequency. Similar variation was reflected in the dielectric loss (tan$δ$) behavior with temperature, which shows the thermal activation of the charge carriers in the material. The analysis of high temperature impedance spectroscopy data shows the grain and grain boundary contributions by fitting the Nyquist plots to the equivalent circuit. From the analysis of the impedance and modulus spectra, it was possible to discern between the effects of overlapping grains, grain boundaries, and electrode interfaces. The relaxation time decreases with an increase in the temperature and the activation energy changes from 0.44~eV to 0.56~eV at around 400~K, which is due to involvement of thermal activation in the conduction of charge carriers. The conductivity is found to be increased with temperature for a given frequency, which again shows the semiconducting behavior. Whereas the conductivity increases with increase in frequency at lower temperatures. Also, the conductivity almost saturates with frequency at high temperatures.
△ Less
Submitted 16 August, 2022;
originally announced August 2022.
-
Structural, magnetic and transport properties of Co$_2$CrAl epitaxial thin films
Authors:
Guru Dutt Gupt,
Rajendra S. Dhaka
Abstract:
We report the physical properties of Co$_2$CrAl Heusler alloy epitaxial thin films grown on single crystalline MgO(001) substrate using pulsed laser deposition technique. The x-ray diffraction pattern in $θ$-2$θ$ mode showed the film growth in single phase B2-type ordered cubic structure with the presence of (002) and (004) peaks, and the film oriented along the MgO(001) direction. The $φ$~scan al…
▽ More
We report the physical properties of Co$_2$CrAl Heusler alloy epitaxial thin films grown on single crystalline MgO(001) substrate using pulsed laser deposition technique. The x-ray diffraction pattern in $θ$-2$θ$ mode showed the film growth in single phase B2-type ordered cubic structure with the presence of (002) and (004) peaks, and the film oriented along the MgO(001) direction. The $φ$~scan along the (220) plane confirms the four-fold symmetry and the epitaxial growth relation found to be Co$_2$CrAl(001)[100]$\vert$$\vert$MgO(001)[110]. The thickness of about 12~nm is extracted through the analysis of x-ray reflectivity data. The isothermal magnetization (M--H) curves confirm the ferromagnetic (FM) nature of the thin film having significant hysteresis at 5 and 300~K. From the in-plane M--H curves, the saturation magnetization values are determined to be 2.1~$μ$$_{\rm B}$/f.u.~at 5~K and 1.6~$μ$$_{\rm B}$/f.u. at 300~K, which suggests the soft FM behavior in the film having the coercive field $\approx$ 522~Oe at 5~K. The thermo-magnetization measurements at 500~Oe magnetic field show the bifurcation between field-cooled and zero-field-cooled curves below about 100~K. The normalized field-cooled magnetization curve follows the T$^2$ dependency, and the analysis reveal the Curie temperature around 335$\pm$11~K. Moreover, the low-temperature resistivity indicates semiconducting behavior with the temperature, and we find a negative temperature coefficient of resistivity (5.2 $\times$ 10$^{-4}$ /K).
△ Less
Submitted 9 August, 2022;
originally announced August 2022.
-
Structural and magnetic behavior of Cr$_2$Co$_{(1-x)}$Cr$_x$Al inverse Heusler alloys
Authors:
Manisha Srivastava,
Guru Dutt Gupt,
Priyanka Nehla,
Anita Dhaka,
R. S. Dhaka
Abstract:
We report the structural and magnetic behavior of single phase inverse Heusler alloys Cr$_2$Co$_{(1-x)}$Cr$_x$Al ($x = $ 0, 0.2, 0.4) using x-ray diffraction (XRD), Raman spectroscopy, isothermal magnetization, and magnetic susceptibility measurements. Interestingly, the Rietveld refinement of XRD data with the space group I$\bar{4}m2$ reveal a tetragonal distortion with c/a ratio around 1.38 in t…
▽ More
We report the structural and magnetic behavior of single phase inverse Heusler alloys Cr$_2$Co$_{(1-x)}$Cr$_x$Al ($x = $ 0, 0.2, 0.4) using x-ray diffraction (XRD), Raman spectroscopy, isothermal magnetization, and magnetic susceptibility measurements. Interestingly, the Rietveld refinement of XRD data with the space group I$\bar{4}m2$ reveal a tetragonal distortion with c/a ratio around 1.38 in these inverse Heusler structures. The bulk compositions have been confirmed by energy dispersive x-ray spectroscopy measurements. The active Raman mode F$_{2g}$ is observed at 320~cm$^{-1}$, which confirms the X-type Heusler structure as the A2 and B2 type structures are known to be not Raman active. The area of F$_{2g}$ mode decreases with Cr concentration, which indicate the origin of this mode due to Co vibrations. The isothermal magnetization data confirm the magnetic moment close to zero ($\le$0.02 $μ_B/f.u.$) at $\approx$70~kOe and negligible coercive field suggest the fully compensated ferrimagnetic nature of these samples. The susceptibility behavior indicates irreversibility between zero-field and field-cooled curves and complex magnetic interactions at low temperatures.
△ Less
Submitted 7 May, 2020;
originally announced May 2020.
-
Neutron diffraction and magnetic properties of Co$_2$Cr$_{1-x}$Ti$_x$Al Heusler alloys
Authors:
Priyanka Nehla,
Yousef Kareri,
Guru Dutt Gupt,
James Hester,
P. D. Babu,
Clemens Ulrich,
R. S. Dhaka
Abstract:
We report the structural, magnetic, and magnetocaloric properties of Co$_2$Cr$_{1-x}$Ti$_x$Al ($x=$ 0--0.5) Heusler alloys for spintronic and magnetic refrigerator applications. Room temperature X-ray diffraction and neutron diffraction patterns along with Rietveld refinements confirm that the samples are of single phase and possess a cubic structure. Interestingly, magnetic susceptibly measuremen…
▽ More
We report the structural, magnetic, and magnetocaloric properties of Co$_2$Cr$_{1-x}$Ti$_x$Al ($x=$ 0--0.5) Heusler alloys for spintronic and magnetic refrigerator applications. Room temperature X-ray diffraction and neutron diffraction patterns along with Rietveld refinements confirm that the samples are of single phase and possess a cubic structure. Interestingly, magnetic susceptibly measurements indicate a second order phase transition from paramagnetic to ferromagnetic where the Curie temperature (T$_{\rm C}$) of Co$_2$CrAl increases from 330~K to 445~K with Ti substitution. Neutron powder diffraction data of the $x=$ 0 sample across the magnetic phase transition taken in a large temperature range confirm the structural stability and exclude the possibility of antiferromagnetic ordering. The saturation magnetization of the $x=$ 0 sample is found to be 8000~emu/mol (1.45~$μ_{\rm B}$/{\it f.u.}) at 5~K, which is in good agreement with the value (1.35$\pm$0.05~$μ_{\rm B}$/{\it f.u.}) obtained from the Rietveld analysis of the neutron powder diffraction pattern measured at temperature of 4~K. By analysing the temperature dependence of the neutron data of the $x=$ 0 sample, we find that the change in the intensity of the most intense Bragg peak (220) is consistent with the magnetization behavior with temperature. Furthermore, an enhancement of change in the magnetic entropy and relative cooling power values has been observed for the $x=$ 0.25 sample. Interestingly, the critical behavior analysis across the second order magnetic phase transition and extracted exponents ($β\approx$ 0.496, $γ\approx$ 1.348, and $δ\approx$ 3.71 for the $x=$ 0.25 sample) suggest the presence of long-range ordering, which deviates towards 3D Heisenberg type interactions above T$_{\rm C}$, consistent with the interaction range value $σ$.
△ Less
Submitted 18 September, 2019;
originally announced September 2019.