Phase transition at 350 K in the Ti$_3$C$_2$T$_x$ MXene: possible sliding (moiré) ferroelectricity
Authors:
Francesco Cordero,
Hanna Pazniak,
Thierry Ouisse,
Jesus Gonzalez-Julian,
Aldo Di Carlo,
Viktor Soprunyuk,
Wilfried Schranz
Abstract:
A phase transition is found in Ti$_3$C$_2$T$_x$ MXene at 350 K, by measuring the complex Young's modulus of self-standing thick films. A step-like softening and increase of the mechanical losses is found below 350 K, indicative of a phase transition, where the square of the order parameter is coupled to strain. It is argued that it should be a ferroelectric transition, most likely of the sliding (…
▽ More
A phase transition is found in Ti$_3$C$_2$T$_x$ MXene at 350 K, by measuring the complex Young's modulus of self-standing thick films. A step-like softening and increase of the mechanical losses is found below 350 K, indicative of a phase transition, where the square of the order parameter is coupled to strain. It is argued that it should be a ferroelectric transition, most likely of the sliding (moiré) type, due to charge transfer between facing flakes sliding with respect to each other. If the transition will be confirmed to be ferroelectric, Ti$_3$C$_2$T$_x$ will be added to the class of metallic ferroelectrics and open new perspectives of applications, in addition to the numerous already studied.
△ Less
Submitted 24 October, 2023;
originally announced October 2023.
Mechanical Characterisation of the Protective Al$_2$O$_3$ Scale in Cr$_2$AlC MAX phases
Authors:
J. S. K. -L. Gibson,
J. Gonzalez-Julian,
S. Krishnan,
R. Vaßen,
S. Korte-Kerzel
Abstract:
MAX phases have great potential under demands of both high-temperature and high-stress performance, with their mixed atomic bonding producing the temperature and oxidation resistance of ceramics with the mechanical resilience of metals. Here, we measure the mechanical properties up to 980C by nanoindentation on highly dense and pure Cr$_2$AlC, as well as after oxidation with a burner rig at 1200C…
▽ More
MAX phases have great potential under demands of both high-temperature and high-stress performance, with their mixed atomic bonding producing the temperature and oxidation resistance of ceramics with the mechanical resilience of metals. Here, we measure the mechanical properties up to 980C by nanoindentation on highly dense and pure Cr$_2$AlC, as well as after oxidation with a burner rig at 1200C for more than 29 hours. Only modest reductions in both hardness and modulus up to 980C were observed, implying no change in deformation mechanism. Furthermore, micro-cantilever fracture tests were carried out at the Cr$_2$AlC/Cr$_7$C$_3$ and Cr$_7$C$_3$/Al$_2$O$_3$ interfaces after the oxidation of the Cr$_2$AlC substrates with said burner rig. The values are typical of ceramic-ceramic interfaces, below 4 MPa/m, leading to the hypothesis that the excellent macroscopic behaviour is due to a combination of low internal strain due to the match in thermal expansion coefficient as well as the convoluted interface.
△ Less
Submitted 29 July, 2019;
originally announced July 2019.