Spin-current mediated exchange coupling in MgO-based magnetic tunnel junctions
Authors:
L. Gladczuk,
L. Gladczuk,
P. Dluzewski,
K. Lasek,
P. Aleshkevych,
D. M. Burn,
G. van der Laan,
T. Hesjedal
Abstract:
Heterostructures composed of ferromagnetic layers that are mutually interacting through a nonmagnetic spacer are at the core of magnetic sensor and memory devices. In the present study, layer-resolved ferromagnetic resonance was used to investigate the coupling between the magnetic layers of a Co/MgO/Permalloy magnetic tunnel junction. Two magnetic resonance peaks were observed for both magnetic l…
▽ More
Heterostructures composed of ferromagnetic layers that are mutually interacting through a nonmagnetic spacer are at the core of magnetic sensor and memory devices. In the present study, layer-resolved ferromagnetic resonance was used to investigate the coupling between the magnetic layers of a Co/MgO/Permalloy magnetic tunnel junction. Two magnetic resonance peaks were observed for both magnetic layers, as probed at the Co and Ni L3 x-ray absorption edges, showing a strong interlayer interaction through the insulating MgO barrier. A theoretical model based on the Landau-Lifshitz-Gilbert-Slonczewski equation was developed, including exchange coupling and spin pumping between the magnetic layers. Fits to the experimental data were carried out, both with and without a spin pumping term, and the goodness of the fit was compared using a likelihood ratio test. This rigorous statistical approach provides an unambiguous proof of the existence of interlayer coupling mediated by spin pumping.
△ Less
Submitted 20 January, 2021;
originally announced January 2021.
-
Impact of organic capping layer on the magnetic anisotropy of ultrathin Co films
Authors:
Leszek Gladczuk,
Kinga Lasek,
Roman Puzniak,
Maciej Sawicki,
Pavlo Aleshkevych,
Wojciech Paszkowicz,
Roman Minikayev,
Iraida N. Demchenko,
Yevgen Syryanyy,
Piotr Przyslupski
Abstract:
Using combined magnetometry and ferromagnetic resonance studies, it is shown that introduction of a hydrocarbon cover layer leads to an increase of the contribution of the surface anisotropy to the effective magnetic anisotropy energy of hexagonal close-packed 0001 cobalt films, largely enhancing the perpendicular anisotropy. Due to a weak electronic interaction of the organic molecules with the C…
▽ More
Using combined magnetometry and ferromagnetic resonance studies, it is shown that introduction of a hydrocarbon cover layer leads to an increase of the contribution of the surface anisotropy to the effective magnetic anisotropy energy of hexagonal close-packed 0001 cobalt films, largely enhancing the perpendicular anisotropy. Due to a weak electronic interaction of the organic molecules with the Co atoms, an increase of surface anisotropy could be explained by the presence of an electric field at the organic-material/Co interface and by modification of surface atoms charge configuration.
△ Less
Submitted 10 November, 2017;
originally announced November 2017.
-
MgO thickness-induced spin reorientation transition in Co0.9Fe0.1/MgO/Co0.9Fe0.1 structure
Authors:
Kinga Lasek,
Leszek Gladczuk,
Maciej Sawicki,
Pavlo Aleshkevych,
Piotr Przyslupski
Abstract:
The magnetic anisotropy (MA) of Mo/Au/Co0.9Fe0.1/Au/MgO(0.7 - 3 nm)/Au/Co0.9Fe0.1/Au heterostructure has been investigated at room temperature as a function of MgO layer thickness (tMgO). Our studies show that while the MA of the top layer does not change its character upon variation of tMgO, the uniaxial out-of-plane MA of the bottom one undergoes a spin reorientation transition at tMgO of about…
▽ More
The magnetic anisotropy (MA) of Mo/Au/Co0.9Fe0.1/Au/MgO(0.7 - 3 nm)/Au/Co0.9Fe0.1/Au heterostructure has been investigated at room temperature as a function of MgO layer thickness (tMgO). Our studies show that while the MA of the top layer does not change its character upon variation of tMgO, the uniaxial out-of-plane MA of the bottom one undergoes a spin reorientation transition at tMgO of about 0.8 nm, switching to the regime where the coexistence of in- and out-of-plane magnetization alignments is observed. The magnitudes of the magnetic anisotropy constants have been determined from ferromagnetic resonance and dc-magnetometry measurements. The origin of MA evolution has been attributed to a presence of an interlayer exchange coupling (IEC) between Co0.9Fe0.1 layers through the thin MgO film.
△ Less
Submitted 24 August, 2017;
originally announced August 2017.
-
The structure and stability of beta-Ta thin films
Authors:
Aiqin Jiang,
Trevor A. Tyson,
Lisa Axe,
Leszek Gladczuk,
Marek Sosnowski,
Paul Cote
Abstract:
Ta films with tetragonal crystalline structure (beta-phase), deposited by magnetron sputtering on different substrates (steel, silicon and silicon dioxide), have been studied. In all cases, very highly preferred (001) orientation was observed in x-ray diffraction (XRD) measurements. All diffraction data revealed two weak reflections corresponding to d-spacing of 0.5272 and 0.1777 nm. The presenc…
▽ More
Ta films with tetragonal crystalline structure (beta-phase), deposited by magnetron sputtering on different substrates (steel, silicon and silicon dioxide), have been studied. In all cases, very highly preferred (001) orientation was observed in x-ray diffraction (XRD) measurements. All diffraction data revealed two weak reflections corresponding to d-spacing of 0.5272 and 0.1777 nm. The presence of the two peaks, attributed to (001) and (003) reflections, indicates that beta-Ta films exhibit a high preference for the space group of P-421m over P42/mnm, previously proposed for beta-Ta. Differences in relative intensities of (00l) reflections, calculated for single crystal beta-Ta sigma-type Frank-Kasper structure and those measured in the films, are attributed to defects in the films. Molecular dynamics simulations performed on tantalum clusters with six different initial configurations using the embedded-atom-method (EAM) potential revealed the stability of beta-Ta, which might explain its growth on many substrates under various deposition conditions.
△ Less
Submitted 7 July, 2004;
originally announced July 2004.