Hydrogenation via a low energy mechanochemical approach: the MgB$_2$ case
Authors:
Claudio Pistidda,
Archa Santhosh,
Paul Jerabek,
Yuanyuan Shang,
Alessandro Girella,
Chiara Milanese,
Maria Dore,
Sebastiano Garroni,
Simone Bordignon,
Michele R. Chierotti,
Thomas Klassen,
Martin Dornheim
Abstract:
This work aims at investigating the effect that the energy transferred during powder-to-wall collisions in a milling process without grinding media entails on solid-gas reactions. For this purpose, the synthesis of Mg(BH$_4$)$_2$ from MgB$_2$ in a pressurized hydrogen atmosphere was chosen as a model reaction. MgB$_2$ was milled under a broad set of milling parameters (i.e. milling times and rota…
▽ More
This work aims at investigating the effect that the energy transferred during powder-to-wall collisions in a milling process without grinding media entails on solid-gas reactions. For this purpose, the synthesis of Mg(BH$_4$)$_2$ from MgB$_2$ in a pressurized hydrogen atmosphere was chosen as a model reaction. MgB$_2$ was milled under a broad set of milling parameters (i.e. milling times and rotation regimes) and the obtained product thoroughly characterized. By proving the partial formation of Mg(BH$_4$)$_2$, the results of this investigation indicate that the energy transferred to the powder bed by the powder particles colliding with the chamber wall during milling is not negligible, in particular when the milling process is protracted for a long period.
△ Less
Submitted 18 February, 2021;
originally announced February 2021.
Sodium catalytic effect in the NaxLi6-xC60 hydrogen storage process
Authors:
Mattia Gaboardi,
Chiara Milanese,
Giacomo Magnani,
Alessandro Girella,
Daniele Pontiroli,
Mauro Ricco
Abstract:
We report on the hydrogen sorption investigation of the mixed alkali cluster intercalated fulleride series NaxLi6-xC60. These compounds are isostructural to Na6C60 and Li6C60 while the cubic lattice parameter is linearly dependent on x. The H2 absorption/desorption was studied by means of charge/discharge kinetic and coupled calorimetric - manometric measurements. By varying the stoichiometry, we…
▽ More
We report on the hydrogen sorption investigation of the mixed alkali cluster intercalated fulleride series NaxLi6-xC60. These compounds are isostructural to Na6C60 and Li6C60 while the cubic lattice parameter is linearly dependent on x. The H2 absorption/desorption was studied by means of charge/discharge kinetic and coupled calorimetric - manometric measurements. By varying the stoichiometry, we found the best compromise between absorption rate, temperature and amount of hydrogen in Na1Li5C60. This system is able to reversibly absorb up to 4.3 wt% H2 at 280 °C, which is 70 °C lower in temperature than its parent compound Li6C60. Furthermore, the kinetics is improved of 67% with respect Li6C60 and the dehydrogenation enthalpy is 13 kJ/mol H2 lower.
△ Less