Pt-based nanowire networks with enhanced oxygen-reduction activity
Authors:
Henning Galinski,
Thomas Ryll,
Yang Lin,
Barbara Scherrer,
Anna Evans,
Max Döbeli,
Ludwig J. Gauckler
Abstract:
Pt-Al and Pt-Y-Al thin film electrodes on yttria-stabilised zirconia electrolytes were prepared by dealloying of co-sputtered Pt-Al or Pt-Y-Al films. The selective dissolution of Al from the Pt-alloy compound causes the formation of a highly porous nanowire network with a mean branch thickness below 25 nm and a pore intercept length below 35 nm. The oxygen reduction capability of the resulting ele…
▽ More
Pt-Al and Pt-Y-Al thin film electrodes on yttria-stabilised zirconia electrolytes were prepared by dealloying of co-sputtered Pt-Al or Pt-Y-Al films. The selective dissolution of Al from the Pt-alloy compound causes the formation of a highly porous nanowire network with a mean branch thickness below 25 nm and a pore intercept length below 35 nm. The oxygen reduction capability of the resulting electrodes was analysed in a micro-solid oxide fuel cell setup at elevated temperatures (598-873 K). Here, we demonstrate that these nanoporous thin films excel "state-of-the-art" fuel cell electrodes in terms of catalytic activity and thermal stability. The nanoporous Pt electrodes exhibit exchange current densities that are up to 13 times higher than conventional Pt electrodes, measured at 648 K. It is shown that the enhanced catalytic activity of these Pt electrodes is achieved through the engineering of the materials d-bands due to the addition of yttrium as ternary constituent.
△ Less
Submitted 17 July, 2014; v1 submitted 18 March, 2014;
originally announced March 2014.
-
Temperature-dependent 2D-3D growth transition of ultra-thin Pt films deposited by PLD
Authors:
Henning Galinski,
Thomas Ryll,
Philipp Reibisch,
Lukas Schlagenhauf,
Iwan Schenker,
Ludwig J. Gauckler
Abstract:
During the growth of metal thin films on dielectric substrates at a given deposition temperature T, the film's morphology is conditioned by the magnitude and asymmetry of up- and downhill diffusion. Any severe change of this mechanism leads to a growth instability, which induces an alteration of the thin film morphology. In order to study this mechanism, ultra-thin Pt films were deposited via puls…
▽ More
During the growth of metal thin films on dielectric substrates at a given deposition temperature T, the film's morphology is conditioned by the magnitude and asymmetry of up- and downhill diffusion. Any severe change of this mechanism leads to a growth instability, which induces an alteration of the thin film morphology. In order to study this mechanism, ultra-thin Pt films were deposited via pulsed laser deposition (PLD) onto yttria-stabilized-zirconia single crystals at different deposition temperatures. The morphological evolution of Pt thin films has been investigated by means of scanning electron microscopy (SEM), atomic force microscopy (AFM) and standard image analysis techniques. The experimentally obtained morphologies are compared to simulated thin film structures resulting from a two-dimensional kinetic Monte Carlo (KMC) approach. Two main observations have been made: i) Thin Pt films deposited onto zirconia undergo a growth transition from two-dimensional to three-dimensional growth at T > 573 K. The growth transition and related morphological changes are a function of the deposition temperature. ii) A critical cluster size of i\ast = 4 in combination with an asymmetric Ehrlich-Schwoebel (ES) barrier favoring the uphill diffusion of atoms allows for a computational reproduction of the experimentally obtained film morphologies.
△ Less
Submitted 18 June, 2012;
originally announced June 2012.
-
High temperature oxygen NEXAFS valence band spectra and conductivity of LaFe3/4Ni1/4O3 from 300 K to 773 K
Authors:
Artur Braun,
Selma Erat,
Ahmad K. Ariffin,
Recardo Manzke,
Hiroki Wadati,
Thomas Graule,
Ludwig J. Gauckler
Abstract:
LaFe3/4Ni1/4O3 was subjected to oxygen near edge x-ray absorption fine structure (NEXAFS) spectroscopy for 300 K < T < 773 K. The spectra show in the pre-edge a small hole doped peak originating from Ni substitution. The relative spectral weight of this transition to the weight of the hybridized O(2p) - Fe(3d) transitions scales with T and has a maximum at around 600 K. The characteristic energies…
▽ More
LaFe3/4Ni1/4O3 was subjected to oxygen near edge x-ray absorption fine structure (NEXAFS) spectroscopy for 300 K < T < 773 K. The spectra show in the pre-edge a small hole doped peak originating from Ni substitution. The relative spectral weight of this transition to the weight of the hybridized O(2p) - Fe(3d) transitions scales with T and has a maximum at around 600 K. The characteristic energies of the thermal activated spectral intensity and conductivity suggest that the concentration of charge transferred electrons from O(2p) to Ni(3d) increases and that the pre-edges account in part for the polaron activated transport.
△ Less
Submitted 26 November, 2011;
originally announced November 2011.
-
Hillock formation of Pt thin films on Yttria stabilized Zirconia single crystals
Authors:
Henning Galinski,
Thomas Ryll,
Lukas Schlagenhauf,
Patrick Stender,
Guido Schmitz,
Ludwig J. Gauckler
Abstract:
The stability of a metal thin films on a dielectric substrate is conditioned by the magnitude of the interactive forces at the interface. In the case of a non-reactive interface and weak adhesion, the minimization of free surface energy gives rise to an instability of the thin film. In order to study these effects, Pt thin films with a thickness of 50 nm were deposited via ion-beam sputtering on y…
▽ More
The stability of a metal thin films on a dielectric substrate is conditioned by the magnitude of the interactive forces at the interface. In the case of a non-reactive interface and weak adhesion, the minimization of free surface energy gives rise to an instability of the thin film. In order to study these effects, Pt thin films with a thickness of 50 nm were deposited via ion-beam sputtering on yttria stabilized zirconia single crystals. All Pt films were subjected to heat treatments up to 973 K for 2 h. The morphological evolution of Pt thin films has been investigated by means of scanning electron microscopy (SEM), atomic force microscopy (AFM) and standard image analysis techniques. Three main observations have been made: i) the deposition method has a direct impact on the morphological evolution of the film during annealing. Instead of hole formation, that is typically observed as response to a thermal treatment, anisotropic pyramidal shaped hillocks are formed on top of the film. ii) It is shown by comparing the hillocks' aspect ratio with finite element method (FEM) simulations that the hillock formation can be assigned to a stress relaxation process inside the thin film. iii) By measuring the equilibrium shapes and the shape fluctuations of the formed Pt hillocks the anisotropy of the step free energy and its stiffness have been derived in addition to the anisotropic kink energy of the hillock's edges.
△ Less
Submitted 4 October, 2011;
originally announced October 2011.
-
Dealloying of Platinum-Aluminum Thin Films Part II. Electrode Performance
Authors:
Thomas Ryll,
Henning Galinski,
Lukas Schlagenhauf,
Felix Rechberger,
Ying Sun,
Ludwig J. Gauckler,
Flavio C. F. Mornaghini,
Yasmina Ries,
Ralph Spolenak,
Max Doebeli
Abstract:
Highly porous Pt/Al thin film electrodes on yttria stabilized zirconia electrolytes were prepared by dealloying of co-sputtered Pt/Al films. The oxygen reduction capability of the resulting electrodes was analyzed in a solid oxide fuel cell setup at elevated temperatures. During initial heating to 523 K exceptionally high performances compared to conventional Pt thin film electrodes were measured.…
▽ More
Highly porous Pt/Al thin film electrodes on yttria stabilized zirconia electrolytes were prepared by dealloying of co-sputtered Pt/Al films. The oxygen reduction capability of the resulting electrodes was analyzed in a solid oxide fuel cell setup at elevated temperatures. During initial heating to 523 K exceptionally high performances compared to conventional Pt thin film electrodes were measured. This results from the high internal surface area and large three phase boundary length obtained by the dealloying process. Exposure to elevated temperatures of 673 K or 873 K gave rise to degradation of the electrode performance, which was primarily attributed to the oxidation of remaining Al in the thin films.
△ Less
Submitted 30 October, 2011; v1 submitted 25 August, 2011;
originally announced August 2011.
-
Fe-resonant valence band photoemission and oxygen NEXAFS study on La1-xSrxFe0.75Ni0.25O3-δ
Authors:
Selma Erat,
Hiroki Wadati,
Funda Aksoy,
Zhi Liu,
Thomas Graule,
Ludwig J. Gauckler,
Artur Braun
Abstract:
Iron resonant valance band photoemission spectra of Sr substituted LaFe0.75Ni0.25 O3-δ have been recorded across the Fe 2p - 3d absorption threshold to obtain Fe specific spectral information on the 3d projected partial density of states. Comparison with La1-xSrxFeO3 resonant VB PES literature data suggests that substitution of Fe by Ni forms electron holes which are mainly O 2p character. Substit…
▽ More
Iron resonant valance band photoemission spectra of Sr substituted LaFe0.75Ni0.25 O3-δ have been recorded across the Fe 2p - 3d absorption threshold to obtain Fe specific spectral information on the 3d projected partial density of states. Comparison with La1-xSrxFeO3 resonant VB PES literature data suggests that substitution of Fe by Ni forms electron holes which are mainly O 2p character. Substitution of La by Sr increases the hole concentration to an extent that the eg structure vanishes. The variation of the eg and t2g structures is paralleled by the changes in the electrical conductivity.
△ Less
Submitted 6 June, 2011;
originally announced June 2011.
-
Correlation of conductivity and angle integrated valence band photoemission characteristics in single crystal iron perovskites for 300 K < T < 800 K: Comparison of surface and bulk sensitive methods
Authors:
A. Braun,
B. S. Mun,
Y. Sun,
Z. Liu,
R. Mäder,
S. Erat,
X. Zhang,
S. S. Mao,
E. Pomjakushina,
K. Conder,
L. J. Gauckler,
T. Graule
Abstract:
A single crystal monolith of La0.9Sr0.1FeO3 and thin pulsed laser deposited film of La0.8Sr0.2Fe0.8Ni0.2O3 were subject to angle integrated valence band photoemission spectroscopy in ultra high vacuum and conductivity experiments in ambient air at temperatures from 300 K to 800 K. Except for several sputtering and annealing cycles, the specimen were not prepared in-situ.. Peculiar changes in the t…
▽ More
A single crystal monolith of La0.9Sr0.1FeO3 and thin pulsed laser deposited film of La0.8Sr0.2Fe0.8Ni0.2O3 were subject to angle integrated valence band photoemission spectroscopy in ultra high vacuum and conductivity experiments in ambient air at temperatures from 300 K to 800 K. Except for several sputtering and annealing cycles, the specimen were not prepared in-situ.. Peculiar changes in the temperature dependent, bulk representative conductivity profile as a result of reversible phase transitions, and irreversible chemical changes are semi-quantitatively reflected by the intensity variation in the more surface representative valence band spectra near the Fermi energy. X-ray photoelectron diffraction images reflect the symmetry as expected from bulk iron perovskites. The correlation of spectral details in the valence band photoemission spectra (VB PES) and details of the conductivity during temperature variation suggest that valuable information on electronic structure and transport properties of complex materials may be obtained without in-situ preparation.
△ Less
Submitted 6 June, 2011;
originally announced June 2011.
-
Entanglement of charge transfer, hole doping, exchange interaction and octahedron tilting angle and their influence on the conductivity of La1-xSrxFe0.75Ni0.25O3-δ: A combination of x-ray spectroscopy and diffraction
Authors:
Selma Erat,
Artur Braun,
Cinthia Piamonteze,
Zhi Liu,
Alejandro Ovalle,
Hansjürgen Schindler,
Thomas Graule,
Ludwig J. Gauckler
Abstract:
Substitution of La by Sr in the 25% Ni doped charge transfer insulator LaFeO3 creates structural changes that inflect the electrical conductivity caused by small polaron hopping via exchange interactions and charge transfer. The substitution forms electron holes and a structural crossover from orthorhombic to rhombohedral symmetry, and then to cubic symmetry. The structural crossover is accompanie…
▽ More
Substitution of La by Sr in the 25% Ni doped charge transfer insulator LaFeO3 creates structural changes that inflect the electrical conductivity caused by small polaron hopping via exchange interactions and charge transfer. The substitution forms electron holes and a structural crossover from orthorhombic to rhombohedral symmetry, and then to cubic symmetry. The structural crossover is accompanied by a crossover from Fe3+-O2--Fe3+ superexchange interaction to Fe3+-O2--Fe4+ double exchange interaction, as evidenced by a considerable increase of conductivity. These interactions and charge transfer mechanism depend on superexchange angle, which approaches 180° upon increasing Sr concentration, leading an increased overlap between the O (2p) and Fe/Ni (3d) orbitals.
△ Less
Submitted 6 June, 2011;
originally announced June 2011.
-
An electron hole doping and soft x-ray spectroscopy study on La1-xSrxFe0.75Ni0.25O3-δ
Authors:
Selma Erat,
Artur Braun,
Alejandro Ovalle,
Cinthia Piamonteze,
Zhi Liu,
Thomas Graule,
Ludwig J. Gauckler
Abstract:
The conductivity of the electron hole and polaron conductor La1-xSrxFe0.75Ni0.25O3-δ, a potential cathode material for intermediate temperature solid oxide fuel cells, was studied for 0 <x < 1 and for temperatures 300 K <T < 1250 K. In LaSrFe-oxide, an ABO3 type perovskite, A-site substitu-tion of the trivalent La3+ by the divalent Sr2+ causes oxidation of Fe3+ towards Fe4+, which forms conducting…
▽ More
The conductivity of the electron hole and polaron conductor La1-xSrxFe0.75Ni0.25O3-δ, a potential cathode material for intermediate temperature solid oxide fuel cells, was studied for 0 <x < 1 and for temperatures 300 K <T < 1250 K. In LaSrFe-oxide, an ABO3 type perovskite, A-site substitu-tion of the trivalent La3+ by the divalent Sr2+ causes oxidation of Fe3+ towards Fe4+, which forms conducting electron holes. Here we have in addition a B-site substitution by Ni. The compound for x = 0.5 is identified as the one with the highest conductivity (σ ~ 678 S/cm) and lowest activation energy for polaron conductivity (Ep = 39 meV). The evolution of the electronic structure was monitored by soft x-ray Fe and oxygen K-edge spectroscopy. Homogeneous trend for the oxida-tion state of the Fe was observed. The variation of the ambient temperature conductivity and activation energy with relative Sr content (x) shows a correlation with the ratio of (eg/eg+t2g) in Fe L3 edge up to x=0.5. The hole doping process is reflected by an almost linear trend by the variation of the pre-peaks of the oxygen K-edge soft x-ray absorption spectra.
△ Less
Submitted 6 June, 2011;
originally announced June 2011.
-
Electron hole - phonon interaction and structural changes in La0.9Sr0.1FeO3 by temperature dependent conductivity and valence band photoemission spectros-copy
Authors:
A. Braun,
J. Richter,
A. S. Harvey,
A. Infortuna,
A. Frei,
E. Pomjakushina,
Bongjin S. Mun,
P. Holtappels,
U. Vogt,
K. Conder,
L. J. Gauckler,
T. Graule
Abstract:
Electric conductivity and structural details of the hole-doped polaron conductor La0.9Sr0.1FeO3 (LSF10) are reported. The conductivity of a single crystal shows an exponential increase with temperature with a maxi-mum of 100 S/cm at 700 K and with activation energy of about 375 meV, and a decrease for higher temperatures that follows a power law. The exponential increase of the electric conductivi…
▽ More
Electric conductivity and structural details of the hole-doped polaron conductor La0.9Sr0.1FeO3 (LSF10) are reported. The conductivity of a single crystal shows an exponential increase with temperature with a maxi-mum of 100 S/cm at 700 K and with activation energy of about 375 meV, and a decrease for higher temperatures that follows a power law. The exponential increase of the electric conductivity for 300 K {\leg} T {\leg} 700 is accompanied by a shift of spectral weight in the photoemission valence band towards the Fermi level, indicative of a strong electron-phonon interaction. The subsequent decrease of the conductivity for T > 700 K is accompanied by a reversible phase transformation from orthorhombic to rhombohedral symmetry. The decreasing conductivity for T > 700 K is likely due to the reduction of the iron due to oxygen loss causing a decreasing hole concentration, as evidenced by a substantial chemical shift in the Fe K-shell x-ray absorption spectra. Two additional fine structures in the conductivity data at 357 K, this is, a small temperature reversible jump in the conductivity, and at 573 K, a slight reversible increase of the polaron activation energy, are correlated with an exceptionally strong decrease in spectral valence band intensity near the Fermi level, and with the onset of a corresponding structural transition.
△ Less
Submitted 6 June, 2011;
originally announced June 2011.
-
Direct evidence for electron hole depletion in La0.5Sr0.5FeO3-d upon B-site cation doping
Authors:
Artur Braun,
Defne Bayraktar,
Ashley S. Harvey,
Daniel Beckel,
John A. Purton,
Peter Holtappels,
Ludwig J. Gauckler,
Thomas Graule
Abstract:
Partial substitution of Fe by Ta in the hole-doped La0.5Sr0.5FeO3 decreases the electric conductivity by up to three orders of magnitude. This decrease is in immediate correlation with a decrease of the electron hole concentration and a shift of the spectral weight within the O(1s)-Fe(3d) mixed states from eg bands near the Fermi energy to t2g bands. Corresponding differences in the Fe(2p) and O(1…
▽ More
Partial substitution of Fe by Ta in the hole-doped La0.5Sr0.5FeO3 decreases the electric conductivity by up to three orders of magnitude. This decrease is in immediate correlation with a decrease of the electron hole concentration and a shift of the spectral weight within the O(1s)-Fe(3d) mixed states from eg bands near the Fermi energy to t2g bands. Corresponding differences in the Fe(2p) and O(1s) X-ray absorption spectra reveals formation of states with increased covalency in the initial state and states which contain O(2p) character, and that hole states are responsible for transport changes in the material. The intensity ratio of eg and t2g bands appears to be a spectral indicator for hole formation.
△ Less
Submitted 6 June, 2011;
originally announced June 2011.
-
Dealloying of Platinum-Aluminum Thin Films Part I. Dynamics of Pattern Formation
Authors:
Henning Galinski,
Thomas Ryll,
Lukas Schlagenhauf,
Felix Rechberger,
Sun Ying,
Flavio C. F. Mornaghini,
Yasmina Ries,
Max Döbeli,
Ralph Spolenak,
Ludwig J. Gauckler
Abstract:
Applying focused ion beam (FIB) nanotomography and Rutherford backscattering spectroscopy (RBS) to dealloyed platinum-aluminum thin films an in-depth analysis of the dominating physical mechanisms of porosity formation during the dealloying process is performed. The dynamical porosity formation due to the dissolution of the less noble aluminum in the alloy is treated as result of a reaction-diffus…
▽ More
Applying focused ion beam (FIB) nanotomography and Rutherford backscattering spectroscopy (RBS) to dealloyed platinum-aluminum thin films an in-depth analysis of the dominating physical mechanisms of porosity formation during the dealloying process is performed. The dynamical porosity formation due to the dissolution of the less noble aluminum in the alloy is treated as result of a reaction-diffusion system. The RBS analysis yields that the porosity formation is mainly caused by a linearly propagating diffusion front, i.e. the liquid/solid interface, with a uniform speed of 42(3) nm/s when using a 4M aqueous NaOH solution at room temperature. The experimentally observed front evolution is captured by the normal diffusive Fisher-Kolmogorov-Petrovskii-Piskounov (FKPP) equation and can be interpreted as a branching random walk phenomenon. The etching front produces a gradual porosity with an enhanced porosity in the surface-near regions of the thin film due to prolonged exposure of the alloy to the alkaline solution.
△ Less
Submitted 26 April, 2011;
originally announced April 2011.
-
The Influence of the Degree of Heterogeneity on the Elastic Properties of Random Sphere Packings
Authors:
Iwan Schenker,
Frank T. Filser,
Markus Hütter,
Ludwig J. Gauckler
Abstract:
The macroscopic mechanical properties of colloidal particle gels strongly depend on the local arrangement of the powder particles. Experiments have shown that more heterogeneous microstructures exhibit up to one order of magnitude higher elastic properties than their more homogeneous counterparts at equal volume fraction. In this paper, packings of spherical particles are used as model structures…
▽ More
The macroscopic mechanical properties of colloidal particle gels strongly depend on the local arrangement of the powder particles. Experiments have shown that more heterogeneous microstructures exhibit up to one order of magnitude higher elastic properties than their more homogeneous counterparts at equal volume fraction. In this paper, packings of spherical particles are used as model structures to computationally investigate the elastic properties of coagulated particle gels as a function of their degree of heterogeneity. The discrete element model comprises a linear elastic contact law, particle bonding and damping. The simulation parameters were calibrated using a homogeneous and a heterogeneous microstructure originating from earlier Brownian dynamics simulations. A systematic study of the elastic properties as a function of the degree of heterogeneity was performed using two sets of microstructures obtained from Brownian dynamics simulation and from the void expansion method. Both sets cover a broad and to a large extent overlapping range of degrees of heterogeneity. The simulations have shown that the elastic properties as a function of the degree of heterogeneity are independent of the structure generation algorithm and that the relation between the shear modulus and the degree of heterogeneity can be well described by a power law. This suggests the presence of a critical degree of heterogeneity and, therefore, a phase transition between a phase with finite and one with zero elastic properties.
△ Less
Submitted 13 February, 2012; v1 submitted 7 November, 2010;
originally announced November 2010.
-
Stochastic Generation of Particle Structures with Controlled Degree of Heterogeneity
Authors:
Iwan Schenker,
Frank T. Filser,
Ludwig J. Gauckler
Abstract:
The recently developed void expansion method (VEM) allows for an efficient generation of porous packings of spherical particles over a wide range of volume fractions. The method is based on a random placement of the structural particles under addition of much smaller "void-particles" whose radii are repeatedly increased during the void expansion. Thereby, they rearrange the structural particles un…
▽ More
The recently developed void expansion method (VEM) allows for an efficient generation of porous packings of spherical particles over a wide range of volume fractions. The method is based on a random placement of the structural particles under addition of much smaller "void-particles" whose radii are repeatedly increased during the void expansion. Thereby, they rearrange the structural particles until formation of a dense particle packing and introduce local heterogeneities in the structure. In this paper, microstructures with volume fractions between 0.4 and 0.6 produced by VEM are analyzed with respect to their degree of heterogeneity (DOH). In particular, the influence of the void- to structural particle number ratio, which constitutes a principal VEM-parameter, on the DOH is studied. The DOH is quantified using the pore size distribution, the Voronoi volume distribution and the density-fluctuation method in conjunction with fit functions or integral measures. This analysis has revealed that for volume fractions between 0.4 and 0.55 the void-particle number allows for a quasi-continuous adjustment of the DOH. Additionally, the DOH-range of VEM-generated microstructures with a volume fraction of 0.4 is compared to the range covered by microstructures generated using previous Brownian dynamics simulations, which represent the structure of coagulated colloidal suspensions. Both sets of microstructures cover similarly broad and overlapping DOH-ranges, which allows concluding that VEM is an efficient method to stochastically reproduce colloidal microstructures with varying DOH.
△ Less
Submitted 25 July, 2010; v1 submitted 17 February, 2010;
originally announced February 2010.
-
Microstructures and Mechanical Properties of Dense Particle Gels: Microstructural Characterization
Authors:
Iwan Schenker,
Frank T. Filser,
Tomaso Aste,
Ludwig J. Gauckler
Abstract:
The macroscopic mechanical properties of densely packed coagulated colloidal particle gels strongly depend on the local arrangement of the powder particles on length scales of a few particle diameters. Heterogeneous microstructures exhibit up to one order of magnitude higher elastic properties and yield strengths than their homogeneous counterparts. The microstructures of these gels are analyzed…
▽ More
The macroscopic mechanical properties of densely packed coagulated colloidal particle gels strongly depend on the local arrangement of the powder particles on length scales of a few particle diameters. Heterogeneous microstructures exhibit up to one order of magnitude higher elastic properties and yield strengths than their homogeneous counterparts. The microstructures of these gels are analyzed by the straight path method quantifying quasi-linear particle arrangements of particles. They show similar characteristics than force chains bearing the mechanical load in granular material. Applying this concept to gels revealed that heterogeneous colloidal microstructures show a significantly higher straight paths density and exhibit longer straight paths than their homogeneous counterparts.
△ Less
Submitted 6 November, 2009;
originally announced November 2009.
-
Quantification of the Heterogeneity of Particle Packings
Authors:
Iwan Schenker,
Frank T. Filser,
Tomaso Aste,
Hans J. Herrmann,
Ludwig J. Gauckler
Abstract:
The microstructure of coagulated colloidal particles, for which the inter-particle potential is described by the DLVO theory, is strongly influenced by the particles' surface potential. Depending on its value, the resulting microstructures are either more "homogeneous" or more "heterogeneous", at equal volume fractions. An adequate quantification of a structure's degree of heterogeneity (DOH) ho…
▽ More
The microstructure of coagulated colloidal particles, for which the inter-particle potential is described by the DLVO theory, is strongly influenced by the particles' surface potential. Depending on its value, the resulting microstructures are either more "homogeneous" or more "heterogeneous", at equal volume fractions. An adequate quantification of a structure's degree of heterogeneity (DOH) however does not yet exist. In this work, methods to quantify and thus classify the DOH of microstructures are investigated and compared. Three methods are evaluated using particle packings generated by Brownian dynamics simulations: (1) the pore size distribution, (2) the density fluctuation method and (3) the Voronoi volume distribution. Each method provides a scalar measure, either via a parameter in a fit function or an integral, which correlates with the heterogeneity of the microstructure and which thus allows for the first time to quantitatively capture the DOH of a granular material. An analysis of the differences in the density fluctuations between two structures additionally allows for a detailed determination of the length scale on which differences in heterogeneity are most pronounced.
△ Less
Submitted 6 November, 2009;
originally announced November 2009.
-
Generation of Porous Particle Structures using the Void Expansion Method
Authors:
Iwan Schenker,
Frank T. Filser,
Hans J. Herrmann,
Ludwig J. Gauckler
Abstract:
The newly developed "void expansion method" allows for an efficient generation of porous packings of spherical particles over a wide range of volume fractions using the discrete element method. Particles are randomly placed under addition of much smaller "void-particles". Then, the void-particle radius is increased repeatedly, thereby rearranging the structural particles until formation of a den…
▽ More
The newly developed "void expansion method" allows for an efficient generation of porous packings of spherical particles over a wide range of volume fractions using the discrete element method. Particles are randomly placed under addition of much smaller "void-particles". Then, the void-particle radius is increased repeatedly, thereby rearranging the structural particles until formation of a dense particle packing.
The structural particles' mean coordination number was used to characterize the evolving microstructures. At some void radius, a transition from an initially low to a higher mean coordination number is found, which was used to characterize the influence of the various simulation parameters. For structural and void-particle stiffnesses of the same order of magnitude, the transition is found at constant total volume fraction slightly below the random close packing limit. For decreasing void-particle stiffness the transition is shifted towards a smaller void-particle radius and becomes smoother.
△ Less
Submitted 6 November, 2009;
originally announced November 2009.