Comparative Study of Dense Bulk MgB$_2$ Materials Prepared by Different Methods
Authors:
V. N. Narozhnyi,
G. Fuchs,
A. Handstein,
A. Gümbel,
J. Eckert,
K. Nenkov,
D. Hinz,
O. Gutfleisch,
A. Wälte,
L. N. Bogacheva,
I. E. Kostyleva,
K. -H. Müller,
L. Schultz
Abstract:
We report on the results of a comparative investigation of highly dense bulk MgB$_2$ samples prepared by three methods: (i) hot deformation; (ii) high pressure sintering; and (iii) mechanical alloying of Mg and B powders with subsequent hot compaction. All types of samples were studied by ac-susceptibility, dc-magnetization and resistivity measurements in magnetic fields up to $μ_0H=160$ kOe. A…
▽ More
We report on the results of a comparative investigation of highly dense bulk MgB$_2$ samples prepared by three methods: (i) hot deformation; (ii) high pressure sintering; and (iii) mechanical alloying of Mg and B powders with subsequent hot compaction. All types of samples were studied by ac-susceptibility, dc-magnetization and resistivity measurements in magnetic fields up to $μ_0H=160$ kOe. A small but distinct anisotropy of the upper critical field $H_{c2}^{a,b}/H_{c2}^{c}\sim1.2$ connected with some texture of MgB$_2$ grains was found for the hot deformed samples. The samples prepared by high pressure sintering as well as by mechanical alloying show improved superconducting properties, including high upper critical fields $H_{c2}$ ($μ_0H_{c2}(0)\sim23$ T), irreversibility fields $H_{irr}$ which are strongly shifted towards higher values $H_{irr}(T)\sim0.8H_{c2}(T)$ and high critical current $J_c$ ($J_c=10^5$ A/cm$^2$ at 20 K and 1 T).
△ Less
Submitted 26 June, 2002;
originally announced June 2002.
Improved superconducting properties in nanocrystalline bulk MgB_2
Authors:
A. Gümbel,
J. Eckert,
G. Fuchs,
K. Nenkov,
K. -H. Müller,
L. Schultz
Abstract:
Highly dense nanocrystalline MgB_2 bulk superconductors with distinctly improved pinning were prepared by mechanical alloying of Mg and B powders and hot compaction at ambient temperatures. The nanocrystalline samples reveal high critical current densities of 105 A/cm2 at 20 K and 1 T together with a strongly shifted irreversibility line towards higher fields resulting in H_irr(T) ~ 0.8 H_c2(T),…
▽ More
Highly dense nanocrystalline MgB_2 bulk superconductors with distinctly improved pinning were prepared by mechanical alloying of Mg and B powders and hot compaction at ambient temperatures. The nanocrystalline samples reveal high critical current densities of 105 A/cm2 at 20 K and 1 T together with a strongly shifted irreversibility line towards higher fields resulting in H_irr(T) ~ 0.8 H_c2(T), whereas typically H_irr(T) ~ 0.5 H_c2(T) is observed for bulk untextured samples. These values exceed that of all other so far reported bulk samples and are in the range of the values of thin films. The improved pinning of this material which mainly consists of spherical grains of about 40-100 nm in size is attributed to the large number of grain boundaries.
△ Less
Submitted 30 November, 2001;
originally announced November 2001.