Showing 1–4 of 4 results for author: Dai, S Y

Preparation of YBCO superconducting thick films On MgO substrates by modified melt growth process

Authors: Y. B. Zhu, J. W. Xiong, S. F. Wang, Y. L. Zhou, Q. Zhang, S. Y. Dai, Z. H. Chen, H. B. Lu, G. Z. Yang

Abstract: Superconducting thick films (200$μ$m-300$μ$m) of YBCO have been fabricated successfully on MgO substrates by a new approach. The precursor powders (YBa2Cu3O7-$δ$(Y123)+0.1molY2BaCuO5(Y211)) are placed between two MgO (10mm x 10mm) slices to form sandwich structure. The YBCO thick films have been obtained from the precursors by modified melt growth process. Resistance measurements of YBCO thick f… ▽ More Superconducting thick films (200$μ$m-300$μ$m) of YBCO have been fabricated successfully on MgO substrates by a new approach. The precursor powders (YBa2Cu3O7-$δ$(Y123)+0.1molY2BaCuO5(Y211)) are placed between two MgO (10mm x 10mm) slices to form sandwich structure. The YBCO thick films have been obtained from the precursors by modified melt growth process. Resistance measurements of YBCO thick films show Tcon of 87.3K and $Δ$T of 4.5K. Estimates using hysteresis loops and the Bean model give a value of 2.78 x 10$^{3}$ A/cm2 (77K, 0T) for the critical current density. The observations of scanning electron microscopy (SEM) and x-ray diffraction patterns (XRD) show the supercoducting Y123 phase matrix containing discrete Y211 inclusions. Keywords: superconducting thick films, YBCO, Y211 phase, peritectic temperature △ Less

Submitted 23 January, 2003; originally announced January 2003.

Comments: 12 pages, 4 figure

Structure, Magnetic Properties and Spin-glass Behavior in La$sub{0.9}Tesub{0.1}MnOsub{3}$

Authors: Guotai Tan, P. Duan, S. Y. Dai, Y. L. Zhou, H. B. Lu, Z. H. Chen

Abstract: In this study we report the structure, magnetic and electrical transport properties of pervoskite oxide La$sub{0.9}Tesub{0.1}MnOsub{3}$. This is a novel material with the space group R-3c, which shows the spin-glass-like feature at low temperature and has a good colossal magnetoresistance behavior. The magnetoresistance ratio is about 51% at 200 K in a field of 4 T. The XPS measurement suggests… ▽ More In this study we report the structure, magnetic and electrical transport properties of pervoskite oxide La$sub{0.9}Tesub{0.1}MnOsub{3}$. This is a novel material with the space group R-3c, which shows the spin-glass-like feature at low temperature and has a good colossal magnetoresistance behavior. The magnetoresistance ratio is about 51% at 200 K in a field of 4 T. The XPS measurement suggests that Te ions are in the Te$up{4+}$ state, while Mn ions may be in the 2+ and 3+ valence state. △ Less

Submitted 21 January, 2003; originally announced January 2003.

Comments: 9 pages, 4figures. submitted to J. Appl. Phys

Irreversibility line of the MgB$_{2}$ superconductor

Authors: Y. Z. Zhang, R. Deltour, H. H. Wen, J. F. de Marneffe, H. Chen, S. F. Wang, S. Y. Dai, Y. L. Zhou, Q. Li, A. G. M. Jansen, P. Wyder, Z. X. Zhao

Abstract: Magneto-resistivity of a c-axis oriented MgB$_{2}$ thin film was studied in perpendicular and parallel magnetic fields up to $\sim $23 T with temperatures down to 0.38 K. Resistive critical magnetic fields were determined. Large separations between irreversibility lines and upper critical magnetic fields are observed. An effective quantum parameter as a function of temperature is proposed to exp… ▽ More Magneto-resistivity of a c-axis oriented MgB$_{2}$ thin film was studied in perpendicular and parallel magnetic fields up to $\sim $23 T with temperatures down to 0.38 K. Resistive critical magnetic fields were determined. Large separations between irreversibility lines and upper critical magnetic fields are observed. An effective quantum parameter as a function of temperature is proposed to explain the separations under the theoretical framework of quantum fluctuations, in good agreement with our experimental and previously published experimental data. △ Less

Submitted 4 March, 2002; v1 submitted 16 October, 2001; originally announced October 2001.

Comments: : 11 pages, revtex4, 4 figs embedded

Superconducting MgB2 Thin Films with Tc of about 39K Grown by Pulsed Laser Deposition

Authors: S. F. Wang, S. Y. Dai, Y. L. Zhou, Z. H. Chen, D. F. Cui, J. D. Yu, M. He, H. B. Lu, G. Z. Yang

Abstract: Superconducting MgB2 thin films were fabricated on Al2O3(0001) substrates under an ex-situ processing conditions. Boron thin films were deposited by pulsed laser deposition followed by a post-annealing process. Resistance measurements of the deposited MgB2 films show Tc of about 39K, while scanning electron microscopy and x-ray diffraction analysis indicate that the films consist of well-crystal… ▽ More Superconducting MgB2 thin films were fabricated on Al2O3(0001) substrates under an ex-situ processing conditions. Boron thin films were deposited by pulsed laser deposition followed by a post-annealing process. Resistance measurements of the deposited MgB2 films show Tc of about 39K, while scanning electron microscopy and x-ray diffraction analysis indicate that the films consist of well-crystallized grains with a highly c-axis-oriented structure. △ Less

Submitted 27 April, 2001; originally announced April 2001.

Comments: 7 Pages, 3 figures