The effect of externally applied pressure on the magnetic behavior of Cu2Te2O5(BrxCl{1-x})2
Authors:
S. J. Crowe,
M. R. Lees,
D. McK. Paul,
R. I. Bewley,
J. W. Taylor,
G. McIntyre,
O. Zaharko,
H. Berger
Abstract:
The effect of externally applied pressure on the magnetic behavior of Cu2Te2O5(BrxCl{1-x})2 with x = 0, 0.73 and 1, is investigated by a combination of magnetic susceptibility, neutron diffraction and neutron inelastic scattering measurements. The magnetic transition temperatures of the x = 0 and 0.73 compositions are observed to increase linearly with increasing pressure at a rate of 0.23(2) K/…
▽ More
The effect of externally applied pressure on the magnetic behavior of Cu2Te2O5(BrxCl{1-x})2 with x = 0, 0.73 and 1, is investigated by a combination of magnetic susceptibility, neutron diffraction and neutron inelastic scattering measurements. The magnetic transition temperatures of the x = 0 and 0.73 compositions are observed to increase linearly with increasing pressure at a rate of 0.23(2) K/kbar and 0.04(1) K/kbar respectively. However, the bromide shows contrasting behavior with a large suppression of the transition temperature under pressure, at a rate of -0.95(9) K/kbar. In neutron inelastic scattering measurements of Cu2Te2O5Br2 under pressure only a small change to the ambient pressure magnetic excitations were observed. A peak in the density of states was seen to shift from ~5 meV in ambient pressure to ~6 meV under an applied pressure of 11.3 kbar, which was associated with an increase in the overall magnetic coupling strength.
△ Less
Submitted 2 January, 2006;
originally announced January 2006.
-
Incommensurate magnetic ordering in Cu2Te2O5X2 (X=Cl, Br) studied by single crystal neutron diffraction
Authors:
O. Zaharko,
H. Ronnow,
J. Mesot,
S. J. Crowe,
D. M^cK. Paul,
P. J. Brown,
A. Daoud-Aladine,
A. Meents,
A. Wagner,
M. Prester,
H. Berger
Abstract:
Polarized and unpolarized neutron diffraction studies have been carried out on single crystals of the coupled spin tetrahedra systems Cu2Te2O5X2 (X=Cl, Br). A model of the magnetic structure associated with the propagation vectors k'Cl ~ -0.150,0.422,1/2 and k'Br ~ -0.172,0.356,1/2 and stable below TN=18 K for X=Cl and TN=11 K for X=Br is proposed. A feature of the model, common to both the brom…
▽ More
Polarized and unpolarized neutron diffraction studies have been carried out on single crystals of the coupled spin tetrahedra systems Cu2Te2O5X2 (X=Cl, Br). A model of the magnetic structure associated with the propagation vectors k'Cl ~ -0.150,0.422,1/2 and k'Br ~ -0.172,0.356,1/2 and stable below TN=18 K for X=Cl and TN=11 K for X=Br is proposed. A feature of the model, common to both the bromide and chloride, is a canted coplanar motif for the 4 Cu2+ spins on each tetrahedron which rotates on a helix from cell to cell following the propagation vector. The Cu2+magnetic moment determined for X=Br, 0.395(5)muB, is significantly less than for X=Cl, 0.88(1)muB at 2K. The magnetic structure of the chloride associated with the wave-vector k' differs from that determined previously for the wave vector k~0.150,0.422,1/2 [O. Zaharko et.al. Phys. Rev. Lett. 93, 217206 (2004)].
△ Less
Submitted 23 December, 2005;
originally announced December 2005.
-
Neutron inelastic scattering investigation of the magnetic excitations in Cu_2Te_2O_5X_2 (X=Br, Cl)
Authors:
S. J. Crowe,
S. Majumdar,
M. R. Lees,
D. McK. Paul,
R. I. Bewley,
S. J. Levett,
C. Ritter
Abstract:
Neutron inelastic scattering investigations have been performed on the spin tetrahedral system Cu_2Te_2O_5X_2 (X = Cl, Br). We report the observation of magnetic excitations with a dispersive component in both compounds, associated with the 3D incommensurate magnetic order that develops below $T^{Cl}_{N}$=18.2 K and $T^{Br}_{N}$=11.4 K. The excitation in Cu_2Te_2O_5Cl_2 softens as the temperatur…
▽ More
Neutron inelastic scattering investigations have been performed on the spin tetrahedral system Cu_2Te_2O_5X_2 (X = Cl, Br). We report the observation of magnetic excitations with a dispersive component in both compounds, associated with the 3D incommensurate magnetic order that develops below $T^{Cl}_{N}$=18.2 K and $T^{Br}_{N}$=11.4 K. The excitation in Cu_2Te_2O_5Cl_2 softens as the temperature approaches $T^{Cl}_{N}$, leaving diffuse quasi-elastic scattering above the transition temperature. In the bromide, the excitations are present well above $T^{Br}_{N}$, which might be attributed to the presence of a degree of low dimensional correlations above $T^{Br}_{N}$ in this compound.
△ Less
Submitted 18 February, 2005;
originally announced February 2005.
-
Investigation of the field-treated magnetic state in Gd5Ge4
Authors:
S. Majumdar,
S. J. Crowe,
D. McK. Paul,
M. R. Lees,
V. Hardy
Abstract:
At low temperatures, the intermetallic compound Gd$_5$Ge$_4$ shows a sharp field-induced transition into a ferromagnetic state around 25 kOe of applied field. The material remains in the field treated ferromagnetic state even when the magnetic field is removed. We have investigated the character of this field-treated state by magnetization and heat capacity measurements. The nature of the magnet…
▽ More
At low temperatures, the intermetallic compound Gd$_5$Ge$_4$ shows a sharp field-induced transition into a ferromagnetic state around 25 kOe of applied field. The material remains in the field treated ferromagnetic state even when the magnetic field is removed. We have investigated the character of this field-treated state by magnetization and heat capacity measurements. The nature of the magnetization and the heat capacity are found to be different above and below a charactersitic temperature Tirr = 25 K.
△ Less
Submitted 14 April, 2004;
originally announced April 2004.